Master batch for polyester filament production and its preparation method and application

A technology of polyester filament and production method, which is applied in the manufacture of rayon, conjugated synthetic polymer rayon, textiles and papermaking, etc., and can solve the problems of high cost, unreachable performance, and affecting the development of polyester spinning field, etc. , to achieve the effects of low cost, improved mechanical strength and excellent comprehensive performance

Active Publication Date: 2020-12-08
苏州市苏宏塑料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in the above-mentioned patents and prior art, the cost is too high if PET primary masterbatch is completely used for spinning; or if recycled polyester chips are completely used, the performance cannot meet the required requirements, which seriously affects the development of the polyester spinning field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Master batch for polyester filament production and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041]Preparation of flat masterbatch:

[0042] (1) First, put 60 parts of waste plastic bottle slices, 10 parts of primary masterbatch, and 1 part of spherical aggregates of simethicone oil and fumed silica into a high-speed stirring reactor with a stirring speed of 100r / min. The heating temperature is 50°C, and the time is 30 minutes;

[0043] (2) Then the material processed in step (1) is put into a twin-screw extruder with a flat die head, and 1 part of glycidyl methacrylate, talcum powder and polyethylene glycol diglycidyl ether are added simultaneously. 0.2 parts of the mixture, the die head temperature is 270°C;

[0044] (3) Slice the extruded material with a cutter, the length of the slice is 3 cm, and the width is 1 cm.

[0045] Preparation of polyester filament:

[0046] (1) Put a large amount of commercially available color masterbatches into a twin-screw extruder with a flat die, set the temperature of the die to 270°C, and cut the extruded material into sheet-l...

Embodiment 2

[0050] Preparation of flat masterbatch:

[0051] (1) First, 63 parts of waste plastic bottle slices, 13 parts of primary masterbatch, and 2 parts of spherical aggregates of simethicone oil and fumed silica were put into a high-speed stirring reactor with a stirring speed of 100r / min. The heating temperature is 50°C, and the time is 30 minutes;

[0052] (2) Then the material processed in step (1) is put into a twin-screw extruder with a flat die head, and 2 parts of glycidyl methacrylate, talcum powder and polyethylene glycol diglycidyl ether are added simultaneously. 0.5 parts of the mixture, the die head temperature is 270°C;

[0053] (3) Slice the extruded material with a cutter, the length of the slice is 3 cm, and the width is 1 cm.

[0054] Preparation of polyester filament:

[0055] (1) Put 200 parts of color masterbatch into a twin-screw extruder with a flat die, set the temperature of the die to 270°C, and cut the extruded material into sheet-like color masterbatch;...

Embodiment 3

[0059] Preparation of flat masterbatch:

[0060] (1) First, 65 parts of waste plastic bottle slices, 15 parts of primary masterbatch, and 2 parts of spherical aggregates of simethicone oil and fumed silica were put into a high-speed stirring reactor with a stirring speed of 100r / min. The heating temperature is 50°C, and the time is 30 minutes;

[0061] (2) Then the material processed in step (1) is put into a twin-screw extruder with a flat die head, and 3 parts of glycidyl methacrylate, talcum powder and polyethylene glycol diglycidyl ether are added simultaneously. 0.5 parts of the mixture, the die head temperature is 270°C;

[0062] (3) Slice the extruded material with a cutter, the length of the slice is 3 cm, and the width is 1 cm.

[0063] Preparation of polyester filament:

[0064] (1) Put 200 parts of color masterbatch into a twin-screw extruder with a flat die, set the temperature of the die to 270°C, and cut the extruded material into sheet-like color masterbatch;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses master batches for production of polyester filaments, and a preparation method and application thereof. The problems that the traditional regenerated master batches cannot havethe characteristics of properties close to those of the original master batches and low cost are solved. According to the key point of the technical scheme, the master batches comprise the followingcomponents in parts by weight: 60 to 70 parts of waste plastic bottle sections, 10 to 40 parts of original master batches, 1 to 3 parts of defoaming master batches, 1 to 5 parts of compatibilizer and0.1 to 1 part of accelerant. The master batches prepared by the above formula have low cost, have excellent properties close to those of the original master batches, can be compatible with the waste plastic bottle sections well in the production of the polyester filaments and enables the polyester filaments to be uniform in character and color.

Description

technical field [0001] The invention relates to a masterbatch, in particular to a masterbatch used in the production of polyester filaments, a preparation method and application thereof. Background technique [0002] Polyester filament, also known as polyester filament, refers to a synthetic fiber produced from polyethylene terephthalate. It is made of polyester chips and masterbatch after high-temperature melting and spinning. It has the advantages of high color fastness, environmental protection, and no need for dyeing. It is known as "a revolution in the textile industry". [0003] In the production of colored polyester filaments, after obtaining the color masterbatch formula for colored spinning according to computer color matching, weigh the required three primary color masterbatches according to the formula and mix them well, then dry the composite color masterbatches and accurately measure and continuously inject them The screw extruder mixes the composite color mast...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L83/04C08L71/02C08K3/36C08K3/34D01F8/14D01F1/10
CPCC08L67/02C08L2203/12C08L2205/025C08L2205/035C08L2205/08C08L2207/20C08L2310/00D01F1/10D01F8/14C08L83/04C08L71/02C08K3/36C08K3/34
Inventor 钱菊男
Owner 苏州市苏宏塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com