Wash-and-wear finisher and preparation method thereof
A technology of non-iron finishing and cactus, which is applied in fiber treatment, shrink-resistant fibers, textiles and papermaking, etc. It can solve the problems of harmful formaldehyde, achieve low volatility, excellent shrink-proof and wrinkle-proof performance, and the manufacturing process is simple and easy to operate Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0040] The invention discloses a no-ironing finishing agent, which comprises the following components in parts by weight: 3 parts of magnesium chloride, 3 parts of citric acid, 5 parts of sodium bicarbonate, 3 parts of borax, 3 parts of triethanolamine, and hydroxymethyl cellulose 5 parts, 5 parts of bisamino silicone emulsion, 3 parts of fatty alcohol polyoxyethylene ether, 10 parts of ethanol, 3 parts of cactus powder, 10 parts of deionized water.
[0041] The present invention also provides a preparation method of a non-ironing finishing agent, the specific steps are as follows:
[0042] (1) Add 3 parts of citric acid, 5 parts of hydroxymethyl cellulose, 5 parts of bisamino silicone emulsion, and 3 parts of fatty alcohol polyoxyethylene ether into the reaction kettle, raise the temperature to 60°C, 500 rpm, Stir for 20 minutes;
[0043] (2) First, 3 parts of borax, 3 parts of triethanolamine, and 10 parts of ethanol are dispersed by ultrasonic, the ultrasonic dispersion po...
Embodiment 2
[0050] The invention discloses a non-ironing finishing agent, which comprises the following components in parts by weight: 4 parts of magnesium chloride, 4 parts of citric acid, 8 parts of sodium bicarbonate, 4 parts of borax, 4 parts of triethanolamine, hydroxymethyl cellulose 8 parts, 8 parts of diamino silicone emulsion, 4 parts of fatty alcohol polyoxyethylene ether, 13 parts of ethanol, 5 parts of cactus powder, and 15 parts of deionized water.
[0051] The present invention also provides a preparation method of a non-ironing finishing agent, the specific steps are as follows:
[0052] (1) Add 4 parts of citric acid, 8 parts of hydroxymethyl cellulose, 8 parts of bisamino silicone emulsion, and 4 parts of fatty alcohol polyoxyethylene ether into the reaction kettle, raise the temperature to 65 ° C, 800 rpm, Stir for 25 minutes;
[0053] (2) First 4 parts of borax, 4 parts of triethanolamine, and 13 parts of ethanol are dispersed with ultrasonic waves, the ultrasonic disp...
Embodiment 3
[0060] The invention discloses a no-ironing finishing agent, which comprises the following components in parts by weight: 5 parts of magnesium chloride, 5 parts of citric acid, 10 parts of sodium bicarbonate, 5 parts of borax, 5 parts of triethanolamine, and hydroxymethyl cellulose 10 parts, 10 parts of diamino silicone emulsion, 5 parts of fatty alcohol polyoxyethylene ether, 15 parts of ethanol, 7 parts of cactus powder, 20 parts of deionized water.
[0061] The present invention also provides a preparation method of a non-ironing finishing agent, the specific steps are as follows:
[0062] (1) Add 5 parts of citric acid, 10 parts of hydroxymethyl cellulose, 10 parts of bisamino silicone emulsion, and 5 parts of fatty alcohol polyoxyethylene ether into the reaction kettle, raise the temperature to 70 ° C, 1000 rpm, Stir for 30 minutes;
[0063] (2) First, 5 parts of borax, 5 parts of triethanolamine, and 15 parts of ethanol are dispersed by ultrasonic, the ultrasonic disper...