Fireproof composite glass and preparation method thereof

A technology of fire-resistant glass and glass, which is applied in the direction of parallel glass structure, window/door improvement, building components, etc. It can solve the problems affecting the service life and effect of fire-resistant glass and the apparent quality of composite fire-resistant glass, so as to avoid air bubbles and The effect of impurities

Inactive Publication Date: 2018-03-09
广西银英生物质能源科技开发股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current fire-resistant glass has many deficiencies. When it is baked by fire, it is easy to produce a large number of microbubbles, which directly affects the apparent quality of the composite fire-resistant glass, and seriously affects the service life and effect of the fire-resistant glass.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A composite fireproof glass in this embodiment comprises two glass bodies arranged parallel to each other and a fireproof liquid filled in the sealed space between the two glass bodies; the fireproof liquid includes the following raw materials in parts by weight: 20 parts of multi-component Alcohol, 50 parts of acrylamide, 3 parts of methylenebisacrylamide, 3 parts of triethoxysilane, 4 parts of carbon forming agent, 5 parts of modified silicone polymer, 1 part of potassium alum, 4 parts of magnesium chloride, 5 parts Methyl methacrylate, 5 parts butyl acrylate, 3 parts sodium hydroxide, 8 parts potassium persulfate, 7 parts deionized water, 6 parts defoamer, 4 parts leveling agent.

[0017] Specifically, the concentration of the sodium hydroxide is 0.5%.

[0018] The preparation method of the composite fireproof glass of the present embodiment comprises the following steps:

[0019] (1) Take the raw materials in parts by weight as mentioned above, mix the modified sil...

Embodiment 2

[0025] A composite fireproof glass in this embodiment comprises two glass bodies arranged parallel to each other and a fireproof liquid filled in the sealed space between the two glass bodies; the fireproof liquid includes the following raw materials in parts by weight: 30 parts of multi-component Alcohol, 60 parts of acrylamide, 4 parts of methylenebisacrylamide, 5 parts of triethoxysilane, 5 parts of carbon forming agent, 9 parts of modified silicone polymer, 1.5 parts of potassium alum, 6 parts of magnesium chloride, 6 parts Methyl methacrylate, 7 parts butyl acrylate, 8 parts sodium hydroxide, 10 parts potassium persulfate, 10 parts deionized water, 10 parts defoamer, 8 parts leveling agent.

[0026] Further, the concentration of the sodium hydroxide is 0.8%.

[0027] The preparation method of the composite fireproof glass of the present embodiment comprises the following steps:

[0028] (1) Take the raw materials in parts by weight as mentioned above, mix the modified si...

Embodiment 3

[0034] A composite fireproof glass in this embodiment comprises two glass bodies arranged parallel to each other and a fireproof liquid filled in the sealed space between the two glass bodies; the fireproof liquid includes the following raw materials in parts by weight: 40 parts of multi-component Alcohol, 70 parts of acrylamide, 5 parts of methylenebisacrylamide, 6 parts of triethoxysilane, 7 parts of carbon forming agent, 12 parts of modified silicone polymer, 2 parts of potassium alum, 7 parts of magnesium chloride, 8 parts Methyl methacrylate, 10 parts of butyl acrylate, 12 parts of sodium hydroxide, 12 parts of potassium persulfate, 12 parts of deionized water, 12 parts of defoamer, 12 parts of leveling agent.

[0035] Specifically, the concentration of the sodium hydroxide is 1%.

[0036] The preparation method of the composite fireproof glass of the present embodiment comprises the following steps:

[0037] (1) Take the raw materials in parts by weight as mentioned abo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to fireproof composite glass and a preparation method thereof. The fireproof composite glass comprises two glass bodies arranged oppositely in parallel and a fireproof liquid contained in a sealing space between the two glass bodies, wherein the fireproof liquid is prepared from raw materials in parts by weight as follows: 20-40 parts of polyhydric alcohols, 50-70 parts of acrylamide, 3-5 parts of methylene bisacrylamide, 3-6 parts of triethoxysilane, 4-7 parts of a carbon-forming agent, 5-12 parts of a modified organosilicon polymer, 1-2 parts of potassium alum, 4-7 parts of magnesium chloride, 5-8 parts of methyl methacrylate, 5-10 parts of butyl acrylate, 3-12 parts of sodium hydroxide, 8-12 parts of potassium persulfate, 7-12 parts of deionized water, 6-12 parts of a defoaming agent and 4-12 parts of a leveling agent. The fireproof composite glass can effectively prevent fire and insulate heat and can prevent the fireproof liquid from producing bubbles and impurities in the solidification process.

Description

technical field [0001] The invention relates to the technical field of glass production and manufacturing, in particular to a composite fireproof glass and a preparation method thereof. Background technique [0002] Safety glass is an important new building material. Fire-resistant glass is a kind of door and window glass with fire-proof function. It can still keep for a long time without bursting under the impact of high-temperature flames, so as to effectively prevent the spread of flames and smoke. The current fire-resistant glass has many deficiencies. When it is baked by fire, it is easy to produce a large number of microbubbles, which directly affects the apparent quality of the composite fire-resistant glass, and seriously affects the service life and effect of the fire-resistant glass. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a composite fireproof glass and a preparation method thereof for the defi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E06B3/677E06B3/67C08F283/12C08F220/56C08F222/38C08F220/14C08F220/18C09K21/14
CPCC08F283/12C09K21/14E06B3/6715E06B3/677C08F220/56Y02A30/249Y02B80/22
Inventor 马银传
Owner 广西银英生物质能源科技开发股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products