Water purifying faucet easy to clean

A faucet and water purification technology, applied in the field of faucets, can solve problems such as inconvenient use and maintenance, and achieve the effects of preventing faucet blockage, softening water quality, and improving adsorption effect.

Inactive Publication Date: 2018-03-23
新沂博瑞工业设计有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Therefore, this method of installing the water filter purifier before or after the faucet will cause problems such as inconvenient use and maintenance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water purifying faucet easy to clean
  • Water purifying faucet easy to clean
  • Water purifying faucet easy to clean

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] A method for preparing a nanocomposite material for softening water, the method comprising the following steps:

[0023] Weigh 18 parts of CaCO 3 / ZSM-5 nanocomposite, 14 parts of active hydroquinone amine resin, 30 parts of bentonite, 10 parts of calcium lignosulfonate, 3 parts of aluminum oxide, and 7 parts of butanediol salicylate were added to the pre- Stir in the mixer, at room temperature, stir at a speed of 1000r / min for 60min, mix thoroughly, add 7 parts of coupling agent KH-560 and 17 parts of triethylene glycol methyl ether in sequence, raise the temperature to 60°C for 2 hours; Separation by filtration through a Schneider funnel, washed twice with 30°C deionized water, dried in an oven at 70°C, and ground to obtain a 1200-mesh nanocomposite.

[0024] The CaCO 3 / ZSM-5 nanocomposite preparation method is as follows:

[0025] Step 1, 0.3kg dry CaCO 3 and 0.1kg of ZSM-5 zeolite powder, activated at 500°C, dispersed in 10L of ethanol, after ball milling, the ...

Embodiment 2

[0035] Weigh 28 parts of CaCO3 / ZSM-5 nanocomposite, 10 parts of active hydroquinone amine resin, 30 parts of bentonite, 10 parts of calcium lignosulfonate, 3 parts of aluminum oxide, and 7 parts of butanediol salicylate were added to the pre- Stir in the mixer, at room temperature, stir at a speed of 1000r / min for 60min, mix thoroughly, add 7 parts of coupling agent KH-560 and 17 parts of triethylene glycol methyl ether in sequence, raise the temperature to 60°C for 2 hours; Separation by filtration through a Schneider funnel, washed twice with 30°C deionized water, dried in an oven at 70°C, and ground to obtain a 1200-mesh nanocomposite.

[0036] All the other preparations are the same as in Example 1.

Embodiment 3

[0038] Weigh 8 parts of CaCO 3 / ZSM-5 nanocomposite, 18 parts of active hydroquinone amine resin, 30 parts of bentonite, 10 parts of calcium lignosulfonate, 3 parts of aluminum oxide, 7 parts of butanediol salicylate were added to the pre- Stir in the mixer, at room temperature, stir at a speed of 1000r / min for 60min, mix thoroughly, add 7 parts of coupling agent KH-560 and 17 parts of triethylene glycol methyl ether in sequence, raise the temperature to 60°C for 2 hours; Separation by filtration through a Schneider funnel, washed twice with 30°C deionized water, dried in an oven at 70°C, and ground to obtain a 1200-mesh nanocomposite.

[0039] All the other preparations are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an easy-to-clean clean water faucet, which comprises a faucet outlet pipe, a water outlet is opened at the bottom of the faucet outlet pipe, a water bundle pipe is fixedly connected to the water outlet of the faucet outlet pipe, and an outer pipe is sleeved on the outside of the water bundle pipe , the bottom end of the outer pipe extends below the water bundle pipe, and a filter plate is arranged inside the outer pipe, and an operating rod is fixedly connected to the center of the top of the filter plate, and the top end of the operating rod penetrates the pipe wall of the faucet outlet pipe and extends to the top of the faucet outlet pipe , and the top of the operating rod is fixedly connected with a pressing plate, the operating rod is covered with a spring, the inside of the beam pipe is provided with a rotating tube, and the rotating tube is sleeved on the operating rod, and the rotating tube is movably connected with the operating rod through a bearing. A plurality of wing plates are fixedly connected to the outer wall of the tube, and a brush is fixedly connected to the bottom of the outer wall of the rotating tube. The water purification faucet can filter the outlet water, and can simply and conveniently remove the impurities left after filtration, so as to prevent the faucet from being blocked.

Description

technical field [0001] The invention relates to the technical field of faucets, in particular to an easy-to-clean water faucet. Background technique [0002] At present, when people use domestic drinking water, they all directly open the tap to get water, and the hardness of water is very closely related to the health of the human body. The hardness of water refers to the content of salts dissolved in water, that is, the content of calcium salts and magnesium salts. It is an important indicator of water quality. The sum of the mass of calcium and magnesium ions is equivalent to 10mgCaO or 7.19mgMgO, which is called 1 "degree (°)". It is stipulated that below 8 degrees (°) is soft water, 8~16 degrees (°) is medium water, above 16 degrees (°) is hard water, and above 30 degrees (°) is extremely hard water. Although calcium and magnesium are essential elements for the human body, drinking water with too high hardness can cause gastrointestinal diseases such as diarrhea, and h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More