Cement mortar with high crack resistance and used for plastering and preparation method of cement mortar
A high crack resistance, cement technology, applied in the field of building mortar, can solve the problems of heavy vertical transportation burden, drying shrinkage temperature difference cracking, aggravating building load capacity, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1
[0023] Refer to Table 1, a high-crack-resistant cement batch mortar and its preparation method, which are mixed with the following components in weight ratio: ordinary Portland cement 25, heavy aggregate 65, fine aggregate 8.8, composite auxiliary Agent 1.2.
[0024] Ordinary Portland cement is black or white cement of model R325; the heavy aggregate is ordinary river sand; the fine aggregate is calcium carbonate; the composite additive is composed of redispersible latex powder and cellulose ether , Calcium formate, wood fiber, polypropylene anti-cracking fiber mixed.
[0025] The fineness number of calcium carbonate is 325 mesh; the fineness mesh number of the ordinary river sand is 40-140 mesh, the redispersible latex powder is 0.5 parts by weight, the cellulose ether is 0.25 parts by weight, Calcium formate is 0.2 parts by weight, the wood fiber is 0.15 parts by weight, and the polypropylene crack-resistant fiber is 0.1 parts by weight.
[0026] The preparation...
Example Embodiment
[0033] Example 2
[0034] Refer to Table 1, a high-crack-resistant cement batch mortar and its preparation method, which are mixed with the following components in weight ratio: ordinary Portland cement 28, heavy aggregate 60, fine aggregate 10.8, composite auxiliary Agent 1.2.
[0035] Each component was taken according to the weight shown in Example 2 in Table 1, and the production process described in Example 1 was repeated (only the weight of each component was changed) to obtain the high crack-resistant cement batch mortar of Example 2. Different from Example 1, the compressive strength and bonding strength are improved, and the functionality is enhanced.
Example Embodiment
[0036] Example 3
[0037] Refer to Table 1, a high-crack-resistant cement batch mortar and its preparation method, which are mixed with the following components in weight ratio: ordinary Portland cement 25, heavy aggregate 65, fine aggregate 8.8, composite auxiliary Agent 1.2.
[0038] Each component is taken according to the weight shown in Example 3 in Table 1, and the production process described in Example 1 is repeated (only the weight of each component is changed) to obtain the high crack-resistant cement batch mortar of Example 3, which is different from the examples. 1 and 2, enhanced bonding strength, improved water retention rate and shrinkage rate.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap