Method for lowering moisture of high-tower nitro product
A nitro, moisture technology, applied in ammonium nitrate fertilizer, application, nitrogen fertilizer and other directions, can solve the problems of pulverization, increased production cost, long hair, etc., and achieves the effect of removing drying steps, simplifying production process, and reducing production cost.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] (1) high tower nitro 15-15-15 formula, total material amount 1000g;
[0016] (2) Take ammonium nitrate (accounting for 40.4% of the total material amount) in a beaker according to the formula ratio and the total amount of material, and melt at 160-175° C.;
[0017] (3) Take undried monoammonium phosphate (moisture 2.1%, accounting for 31% of total material amount) and undried ammonium sulfate (moisture 0.6%, accounting for total material amount 2.2%) according to the formula ratio and total material amount , adding 0.25% by weight of phosphorus pentoxide and mixing;
[0018] (4) Take the second major ingredient and mix it with (3) according to the formula ratio and the total amount of material;
[0019] (5) adding the material obtained in (4) into the molten material (2) at a constant speed under stirring;
[0020] (6) Keep the temperature of the slurry at 145-155°C and stir for 2-4 minutes after adding the material, keep the distance from the ground <10cm, pour the s...
Embodiment 2
[0023] (1) The fixed formula is the high tower nitro 17-10-18 formula, and the total material amount is 1000g;
[0024] (2) Take ammonium nitrate (accounting for 45.2% of the total material amount) in a beaker according to the formula ratio and the total amount of material, and melt at 160-175° C.;
[0025] (3) Take undried monoammonium phosphate (moisture 2.1%, accounting for 23% of the total material amount) according to the formula ratio and the total material amount, add 0.25% by weight of phosphorus pentoxide and mix;
[0026] (4) Take the second major ingredient and mix it with (3) according to the formula ratio and the total amount of material;
[0027] (5) adding the material obtained in (4) into the molten material (2) at a constant speed under stirring;
[0028] (6) Keep the temperature of the slurry at 145-155°C and stir for 2-4 minutes after adding the material, keep the distance from the ground <10cm, pour the slurry onto the dry floor to cool, bag and seal;
[...
Embodiment 3
[0031] (1) The fixed formula is the high tower nitro 22-8-10 formula, and the total amount of material is 1000g;
[0032] (2) Take ammonium nitrate (accounting for 58.25% of the total material amount) in a beaker according to the formula ratio and the total amount of material, and melt at 160-175° C.;
[0033] (3) Take undried monoammonium phosphate (moisture 2.1%, accounting for 15.8% of total material amount) and undried ammonium sulfate (moisture 0.6%, accounting for total material amount 8.0%) according to the formula ratio and total material amount , adding 0.25% by weight of phosphorus pentoxide and mixing;
[0034] (4) Take the second major ingredient and mix it with (3) according to the formula ratio and the total amount of material;
[0035] (5) adding the material obtained in (4) into the molten material (2) at a constant speed under stirring;
[0036] (6) Keep the temperature of the slurry at 145-155°C and stir for 2-4 minutes after adding the material, keep the d...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com