Antibacterial glass ball and production process thereof

A technology of antibacterial glass and production process, which is applied in glass forming, glass manufacturing equipment, manufacturing tools, etc., to achieve good corrosion inhibition effect, uniform particle diameter and good dispersion

Inactive Publication Date: 2018-04-13
张立栋
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vessel glass frits in the prior art cannot take into account the requirements of all aspects, so the production of glass frits with crystal clear, high gloss, high refractive index, toughness, bright and flawless, and unique properties such as chemical stability and thermal stability is the industry's first choice. Problems that people need to solve urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of antibacterial glass ball, is made of the raw material of following parts by weight:

[0026] 280 parts of fine sand, 200 parts of colorless cullet, 5 parts of nano-alumina, 10 parts of nano-diamond, 5 parts of boric acid, 60 parts of sodium carbonate, 10 parts of potassium carbonate, 40 parts of calcite, 30 parts of fluorite, and 15 parts of barite 8 parts, 8 parts of sodium fluorosilicate, 6 parts of boron oxide, 4 parts of pyrophyllite, 2 parts of nano-zinc oxide, 1 part of pigment, 6 parts of composite clarifier, and 2 parts of corrosion inhibitor.

[0027] Among them, the composite clarifying agent is made of variable price oxides, sulfides, halides and their salts; the corrosion inhibitor is made of zinc nitrate and sodium orthophosphate.

[0028] The production technology of above-mentioned antibacterial glass ball, comprises the following steps:

[0029] (1) Ingredients: Weigh each raw material according to the formula quantity and set aside;

[0030]...

Embodiment 2

[0036] A kind of antibacterial glass ball, is made of the raw material of following parts by weight:

[0037] 300 parts of fine sand, 150 parts of colorless cullet, 10 parts of nano-alumina, 20 parts of nano-diamond, 3 parts of boric acid, 80 parts of sodium carbonate, 6 parts of potassium carbonate, 50 parts of calcite, 20 parts of fluorite, and 25 parts of barite 5 parts, 5 parts of sodium fluorosilicate, 10 parts of boron oxide, 6 parts of pyrophyllite, 3 parts of nano-zinc oxide, 2 parts of pigment, 5 parts of composite clarifier, and 4 parts of corrosion inhibitor.

[0038] Among them, the composite clarifying agent is made of variable price oxides, sulfides, halides and their salts; the corrosion inhibitor is made of zinc nitrate and sodium orthophosphate.

[0039] The production technology of above-mentioned antibacterial glass ball, comprises the following steps:

[0040] (1) Ingredients: Weigh each raw material according to the formula quantity and set aside;

[004...

Embodiment 3

[0047] A kind of antibacterial glass ball, is made of the raw material of following parts by weight:

[0048] 290 parts of fine sand, 170 parts of colorless cullet, 7 parts of nano-alumina, 14 parts of nano-diamond, 4 parts of boric acid, 70 parts of sodium carbonate, 8 parts of potassium carbonate, 45 parts of calcite, 25 parts of fluorite, and 20 parts of barite 7 parts of sodium fluorosilicate, 8 parts of boron oxide, 5 parts of pyrophyllite, 2.5 parts of nano-zinc oxide, 1.5 parts of pigment, 5.5 parts of composite clarifier, and 3 parts of corrosion inhibitor.

[0049] Among them, the composite clarifying agent is made of variable price oxides, sulfides, halides and their salts; the corrosion inhibitor is made of zinc nitrate and sodium orthophosphate.

[0050] The production technology of above-mentioned antibacterial glass ball, comprises the following steps:

[0051] (1) Ingredients: Weigh each raw material according to the formula quantity and set aside;

[0052] (2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an antibacterial glass ball and its production process, which relates to the field of glass products. The antibacterial glass ball is made of the following raw materials: fine sand, colorless cullet, nano-alumina, nano-diamond, boric acid, sodium carbonate, potassium carbonate , calcite, fluorite, barite, sodium fluorosilicate, boron oxide, pyrophyllite, nano-zinc oxide, pigment, composite clarifying agent, corrosion inhibitor, the production process of the antibacterial glass ball includes ingredients, uniform mixing, melting, molding 1. Heating tempering and annealing six steps, the antibacterial glass balls prepared by the present invention have the characteristics of crystal clear, high gloss, bright and flawless, and also have antibacterial properties.

Description

technical field [0001] The invention relates to the field of glass products, in particular to an antibacterial glass ball and a production process thereof. Background technique [0002] Glass is a fiber glass component commonly used in the world, and it belongs to borosilicate system glass. In terms of glass melting performance, it belongs to refractory glass. For glass fiber molding, it requires the quality level of quasi-optical glass. Therefore, Ball production is much more difficult than medium-alkali balls. The chemical composition of glass spheres basically determines the physical and chemical properties and process properties of glass fibers and their products, and at the same time, largely determines the composition of glass spheres and glass fibers. [0003] With the continuous improvement of people's living standards and aesthetics, the requirements for high-grade glassware are getting higher and higher, not only requiring beautiful appearance, but also requiring ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C6/06C03C6/02C03C1/00C03B19/10
CPCC03C1/00C03B19/10C03C1/002
Inventor 张立栋
Owner 张立栋