An ecological decorative diatom mud-artificial sandstone composite board and its preparation method

A technology of artificial sandstone and diatom mud, applied in ceramic products, building structures, other household appliances, etc., can solve the problems of easy detachment of diatom mud and photocatalyst components, shortened service life, reduced adsorption effect, etc., to achieve excellent breathing Humidity control function, easy to use, increase the effect of thermal insulation performance

Active Publication Date: 2020-08-25
温岭市腾锋鞋业有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the existing technologies are to use effective technical means to bond or fix the diatom ooze and photocatalyst components, causing the diatom ooze and photocatalyst components to easily fall off and lose, which greatly reduces the service life of the materials; Wrapped diatom mud and photocatalyst materials, reducing the adsorption effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An ecological decorative diatom mud-artificial sandstone composite board and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing an ecologically decorated diatom mud-artificial sandstone composite board, comprising the following steps:

[0026] (1) 5 parts by weight of MoS with a particle size of less than 100 nanometers 2 Add 20 parts by weight of diatomaceous earth into water, stir and disperse evenly, dry, pass through a 0.1mm square hole sieve, pass through a laser scanning bed, use a carbon dioxide laser as the laser source, the power is 300W, and the welding scanning speed is 20mm / s; Grade photocatalyst is fixed in the micropores of diatomite to obtain modified diatomite powder;

[0027] (2) Mix the modified diatomite powder with 50 parts by weight of porous volcanic rock and 20 parts by weight of calcium hydroxide, and add water according to the solid-liquid volume ratio of 1:0.5 to make a mixed slurry;

[0028] (3) Mix the mixed slurry obtained in step (2) with 5 parts by weight of sodium bicarbonate capsules evenly, quickly transfer them to a mold, and conduct a h...

Embodiment 2

[0030] A method for preparing an ecologically decorated diatom mud-artificial sandstone composite board, comprising the following steps:

[0031] (1) Add 6 parts by weight of ZnO with a particle size of less than 100 nanometers and 25 parts by weight of diatomaceous earth into water, stir and disperse evenly, dry, pass through a 0.1mm square hole sieve, pass through a laser scanning bed, and use a carbon dioxide laser as a laser source. The power is 400W, and the welding scanning speed is 25mm / s; the nano-scale photocatalyst is fixed in the micropores of diatomite to obtain modified diatomite powder;

[0032] (2) Mix the modified diatomite powder with 60 parts by weight of porous volcanic rock and 20 parts by weight of calcium hydroxide, and add water according to the solid-liquid volume ratio of 1:0.5 to make a mixed slurry;

[0033](3) Mix the mixed slurry obtained in step (2) with 10 parts by weight of sodium bicarbonate capsules evenly, quickly transfer them to a mold, and...

Embodiment 3

[0035] A method for preparing an ecologically decorated diatom mud-artificial sandstone composite board, comprising the following steps:

[0036] (1) 8 parts by weight of TiO with a particle size less than 100 nanometers 2 Add 50 parts by weight of diatomaceous earth into water, stir and disperse evenly, dry, pass through a 0.1mm square hole sieve, pass through a laser scanning bed, use a carbon dioxide laser as the laser source, the power is 300W, and the welding scanning speed is 30mm / s; Grade photocatalyst is fixed in the micropores of diatomite to obtain modified diatomite powder;

[0037] (2) Mix the modified diatomite powder with 100 parts by weight of porous volcanic rock and 30 parts by weight of calcium hydroxide, and add water according to the ratio of solid-liquid volume ratio of 1:1 to make a mixed slurry;

[0038] (3) Mix the mixed slurry obtained in step (2) with 10 parts by weight of sodium bicarbonate capsules evenly, quickly transfer them to a mold, and condu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore size distributionaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of ecological building materials, and provides a preparation method of a diatom ooze-artificial sandstone composite plate for ecological decoration. The preparationmethod has the advantages that diatom ooze and a photocatalyst are fixed to form a composite plate by utilizing the laser scanning, welding and foaming and the forming and curing of calcium carbonate,so that the falling of the diatom ooze and the photocatalyst is effectively prevented, and the porous adsorption characteristic of the diatom ooze and the contact area between the photocatalyst and air are better remained; when the diatom ooze-artificial sandstone composite plate is used for the internal decoration, the excellent respiration and humidity adjusting functions are realized, and theindoor heat insulation and isolation properties are realized; the photocatalyst can stably perform the photocatalytic reaction, the function of oxidizing and removing organic volatile matters in the air is realized, and the good function of killing bacteria and viruses exposed in the air is also realized.

Description

technical field [0001] The invention belongs to the field of ecological building materials, and in particular relates to an ecological decorative diatom mud-artificial sandstone composite board and a preparation method thereof. Background technique [0002] Eco-friendly, healthy and comfortable interior decoration materials have gradually become the main development trend of the building materials industry at home and abroad. The porous, fluffy, and stable chemical properties of diatomite make it have the properties of adsorption, heat insulation, and sound insulation. With other gelling components, color and particle adjustment components, a new type of wall material that is different from traditional coatings can be obtained. At present, there is a process of directly coating photocatalyst on the surface of artificial sand, which is easy to fall off, weakens the catalytic effect of photocatalyst, and has poor effect. [0003] Chinese patent application CN201310489247.X, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00C04B30/00E04F13/075
CPCC04B30/00C04B2111/00017C04B2111/00025C04B2111/2061C04B2111/40E04F13/0875C04B14/14C04B14/08C04B22/14C04B22/064C04B14/28C04B38/0022C04B22/06
Inventor 陈庆曾军堂
Owner 温岭市腾锋鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap