Surface treatment method for metal stamping die

A surface treatment and metal stamping technology, applied in heat treatment furnaces, heat treatment equipment, metal material coating processes, etc., can solve the problems of short service life of molds, laborious maintenance, neglecting the importance of surface treatment, etc., to improve service performance and life. , the effect of improving thermal fatigue life and thermal wear resistance

Inactive Publication Date: 2018-04-20
蚌埠市宏大制药机械有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In modern industry, metal stamping dies are an important condition for industrial development. The production of products often depends on mold processing. As an important tool for casting production, the working performance of molds affects the use and quality of ca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1

[0016] A method for surface treatment of a metal stamping die includes the following steps:

[0017] (1) After heating the stamping die to 500°C, immediately immerse it in the mixed infiltration liquid at a temperature of 50°C. The content of iron boride in the mixed infiltration liquid is 0.15 g / kg and the content of silicon nitride is 0.20 g / kg. The sodium chloride concentration is 0.5 g / kg, the immersion time is 30 minutes, and the vibrator is used to continuously vibrate and mix the permeate during the immersion process;

[0018] (2) Take out the mold after the infiltration treatment, dry it at 70°C, put it in a heating furnace and heat it to 450°C, keep it for 3 hours, the heat-retained mold undergoes two low-temperature tempering treatments, and the first treatment time is After 5 seconds, quickly reduce the temperature of the billet to 300°C, and then transfer it to a low-temperature box-type heating furnace. Set the temperature in the box to 260°C. After s...

Example Embodiment

[0023] Example 2

[0024] A method for surface treatment of a metal stamping die includes the following steps:

[0025] (1) After the stamping die is heated to 550°C, it is immediately immersed in the mixed infiltration liquid at a temperature of 55°C. The iron boride content in the mixed infiltration liquid is 0.18 g / kg and the silicon nitride content is 0.25 g / kg. The sodium chloride concentration is 0.6 g / kg, the immersion time is 35 minutes, and the vibrator is used to continuously vibrate and mix the permeate during the immersion process;

[0026] (2) Take out the mold after the infiltration treatment, dry it at 80°C, put it in a heating furnace and heat it to 500°C for 3.5 hours. The insulated mold undergoes two low-temperature tempering treatments. The first treatment time is In 8 seconds, the billet temperature is rapidly reduced to 320℃, and then transferred to the low-temperature box heating furnace, set the temperature in the box to 270℃, and after stagnation for 2 minute...

Example Embodiment

[0031] Example 3

[0032] A method for surface treatment of a metal stamping die includes the following steps:

[0033] (1) After heating the stamping die to 600°C, immediately immerse it in the mixed infiltration liquid at a temperature of 60°C. The content of iron boride in the mixed infiltration liquid is 0.20 g / kg and the content of silicon nitride is 0.30 g / kg. The sodium chloride concentration is 0.8 g / kg, the immersion time is 40 minutes, and the vibrator is used to continuously vibrate and mix the permeate during the immersion process;

[0034] (2) Take out the mold after infiltration treatment, dry it at 90°C, put it in a heating furnace to heat to 550°C, keep it warm for 4 hours, the heat-retained mold undergoes two low-temperature tempering treatments, and the first treatment time is In 10 seconds, quickly reduce the billet temperature to 350°C, and then transfer it to a low-temperature box-type heating furnace, set the temperature in the box to 280°C, remove it after 3 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of surface treatment of stamping dies, and discloses a surface treatment method for a metal stamping die. According to the surface treatment method, permeation treatment is carried out, penetrating fluid contains iron boride and silicon nitride, and therefore the thermal fatigue life of the die can be remarkably prolonged, and the thermal wear resistance of the die can be remarkably improved; and then heat treatment and surface strengthening treatment are carried out, different surface treatment modes are used for the die, and therefore the technical advantages of various surface treatment modes can be brought into play, and in addition, the obvious effects of the combined use can be achieved. The method has the advantages that the surface morphology, the chemical components, the structure and the stress state of the die are changed through a composite treatment technology, and therefore the operational performance of the die can be improved, and the service life of the die can be prolonged.

Description

technical field [0001] The invention belongs to the technical field of surface treatment of stamping dies, and in particular relates to a surface treatment method of metal stamping dies. Background technique [0002] Stamping die is a special process equipment for processing materials (metal or non-metal) into parts (or semi-finished products) in cold stamping processing, called cold stamping die (commonly known as cold stamping die). Stamping is a pressure processing method that uses a mold installed on a press to apply pressure to the material at room temperature to cause separation or plastic deformation to obtain the required parts. In the stamping die, various metal materials and non-metal materials are used, mainly carbon steel, alloy steel, cast iron, cast steel, hard alloy, low melting point alloy, zinc-based alloy, aluminum bronze, synthetic resin, polyurethane Rubber, plastic, laminated birch boards, etc. The material for making molds requires properties such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C12/02C21D9/00C23F1/28
CPCC23C12/02C21D9/0068C23F1/28
Inventor 张莉
Owner 蚌埠市宏大制药机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap