Purifying agent for sulfur, arsenic and phosphorus and preparation method for purifying agent

A purification agent, copper oxide technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of high bulk density and low adsorption capacity of purification agents

Active Publication Date: 2018-04-24
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention is the problem of high bulk density and low adsorption capacity of the purification agent in the prior art, and a new sulfur, arsenic, phosphorus purification agent and its preparation method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Purifying agent for sulfur, arsenic and phosphorus and preparation method for purifying agent
  • Purifying agent for sulfur, arsenic and phosphorus and preparation method for purifying agent
  • Purifying agent for sulfur, arsenic and phosphorus and preparation method for purifying agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 30 kg of copper nitrate trihydrate, 40 kg of zinc nitrate hexahydrate, 2 kg of iron nitrate, 2.5 kg of nickel nitrate hexahydrate and 500 kg of water were mixed and stirred evenly to obtain a metal salt solution, and 30 kg of sodium carbonate and 550 kg of water were mixed uniformly to obtain Sodium carbonate solution, mix sodium carbonate solution and metal salt solution evenly, react at 70°C for 1 hour, add 5 kg of pseudo-boehmite, react for 0.5 hour, wash the precipitate until the conductivity of the filtrate is less than 100 μs / cm, precipitate The material was dried, and then 1 kg of graphite and 30% by weight of water were added, mixed and rolled, granulated, roasted at 270° C. for 2 hours, and pressed into tablets. The composition of the obtained sample is shown in Table 1.

Embodiment 2

[0039] 20 kg of copper nitrate trihydrate, 50 kg of zinc nitrate hexahydrate, 2 kg of iron nitrate, 2.5 kg of nickel nitrate hexahydrate and 500 kg of water were mixed and stirred evenly to obtain a metal salt solution, and 30 kg of sodium carbonate and 550 kg of water were mixed uniformly to obtain Sodium carbonate solution, mix sodium carbonate solution and metal salt solution evenly, react at 60°C for 2 hours, add 5 kg of pseudo-boehmite, react for 0.5 hour, wash the precipitate until the conductivity of the filtrate is less than 100 μs / cm, and precipitate The material was dried, then 1 kg of graphite and 35% by weight of water were added, mixed and rolled, granulated, roasted at 270° C. for 2 hours, and pressed into tablets. The composition of the obtained sample was shown in Table 1.

Embodiment 3

[0041] 10 kg of copper nitrate trihydrate, 60 kg of zinc nitrate hexahydrate, 2 kg of iron nitrate, 2.5 kg of nickel nitrate hexahydrate and 500 kg of water were mixed and stirred evenly to obtain a metal salt solution, and 30 kg of sodium carbonate and 550 kg of water were mixed uniformly to obtain Sodium carbonate solution, mix sodium carbonate solution and metal salt solution evenly, react at 60°C for 2 hours, add 6 kg of pseudo-boehmite, react for 0.5 hour, wash the precipitate until the conductivity of the filtrate is less than 100 μs / cm, and precipitate The material was dried, then 1 kg of graphite and 35% by weight of water were added, mixed and rolled, granulated, roasted at 270° C. for 2 hours, and pressed into tablets. The composition of the obtained sample was shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bulk densityaaaaaaaaaa
Conductivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a purifying agent for sulfur, arsenic and phosphorus and a preparation method for the purifying agent. The invention is mainly to solve the problems of high bulk density and low adsorption capacity of a purifying agent in the prior art. The purifying agent for sulfur, arsenic and phosphorus provided by the invention comprises the following components in parts by weight: a)1 to 10 parts of aurichalcite; b) 10 to 50 parts of copper oxide; c) 10 to 60 parts of zinc oxide; d) 0.1 to 10 parts of nickel oxide; and e) 0.1 to 5 parts of ferric oxide. With a technical scheme of the invention, the purifying agent for sulfur, arsenic and phosphorus provided by the invention well solves the above-mentioned problems, and can be used for purification of natural gas, synthesis gas, light gaseous and liquid hydrocarbons, etc.

Description

technical field [0001] The invention relates to a sulfur, arsenic and phosphorus purifying agent and a preparation method thereof. Background technique [0002] Sulfur, arsenic, phosphorus and other impurities widely exist in raw materials such as natural gas, synthesis gas, coal gas, light gas and liquid hydrocarbons. The existence of these impurities will lead to poisoning and deactivation of many catalysts, greatly shorten the life of catalysts, and even lead to catalytic reaction It cannot be carried out normally; in addition, the impurities that have not been removed will enter the downstream synthetic products as the production progresses, which will bring a series of environmental and health problems. Therefore, efficient and high-precision removal of impurities such as sulfur, arsenic, and phosphorus is of great significance for protecting the main catalyst of downstream devices and improving the quality of downstream products at the same time. [0003] In general, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/06B01J20/30
CPCB01J20/02B01J20/06
Inventor 贾银娟王灿高焕新刘志成
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com