a rh @cusio 3 Preparation method of core-sheath structure catalyst

A technology of catalysts and hydrogenation catalysts, applied in the field of Rh@CuSiO3 nanostructured noble metal catalysts and their preparation, can solve the problems of poor thermal stability and grain migration of the active component Rh, achieve large gas flux, and solve grain migration Effect

Inactive Publication Date: 2020-10-27
SICHUAN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For Rh-based catalysts in CO 2 Problems such as grain migration, sintering, and poor thermal stability of the active component Rh are prone to occur during the reaction process of hydrogenation to low-carbon alcohols. The present invention designs and uses conventional materials such as oxides and silicates to develop low-cost, simple-to-operate The core-sheath structure Rh-based nanoreactor catalyst, coupled with the confinement effect of the core-sheath structure material and the synergistic effect between components, improves the dispersion of the active component and its interaction with the carrier, thereby improving the reactivity and stability. sexual purpose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a rh @cusio <sub>3</sub> Preparation method of core-sheath structure catalyst
  • a rh @cusio <sub>3</sub> Preparation method of core-sheath structure catalyst
  • a rh @cusio <sub>3</sub> Preparation method of core-sheath structure catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1.5 g of Cu(NO 3 ) 2 •6H 2 O was dissolved in water, then 25% ammonia water was added to make the solution precipitate and then dissolved again, and then ethanol was added to stir. After 10 minutes, the previously prepared 0.5mol / L NaSiO 3 •9H 2 Add 10mL of O solution into the solution to form a blue precipitate, stir for 180min, then transfer to a 150mL hydrothermal kettle, move to an oven for 12-36 hours under 473K hydrothermal treatment, then take it out for cooling, filter, wash, dry, and roast. Vested CuPNTs. Then 0.032g solid RhCl 3 Add to 25ml absolute ethanol and sonicate to aid in dissolution. RhCl 3 After the solids are completely dissolved, pour 0.5g of CuPNTs weighed in advance, and continue to sonicate. After the CuPNTs are completely dissolved, sonicate for another 20 minutes and take them out of the ultrasonic cleaner. Add 25ml of deionized water, stir and let it stand. After layering, divide the lower layer solution into several watch glasses, dry...

Embodiment 2

[0027] In this example, on the basis of Example 1, the loading amount of the loaded active component is changed.

[0028] 1.5 g of Cu(NO 3 ) 2 •6H 2 O was dissolved in water, then 25% ammonia water was added to make the solution precipitate and then dissolved again, and then ethanol was added to stir. After 10 minutes, the previously prepared 0.5mol / L NaSiO 3 •9H 2 Add 10mL of O solution into the solution to form a blue precipitate, stir for 180min, then transfer to a 150mL hydrothermal kettle, move to an oven for 12-36 hours under 473K hydrothermal treatment, then take it out for cooling, filter, wash, dry, and roast. Vested CuPNTs. Then 0.077g solid RhCl 3 Add to 25ml absolute ethanol and sonicate to aid in dissolution. RhCl 3 After the solids are completely dissolved, pour 0.5g of CuPNTs weighed in advance, and continue to sonicate. After the CuPNTs are completely dissolved, sonicate for another 20 minutes and take them out of the ultrasonic cleaner. Add 25ml of dei...

Embodiment 3

[0030] In this example, on the basis of Example 1, the loading amount of the loaded active component is changed.

[0031] 1.5 g of Cu(NO 3 ) 2 •6H 2 O was dissolved in water, then 25% ammonia water was added to make the solution precipitate and then dissolved again, and then ethanol was added to stir. After 10 minutes, the previously prepared 0.5mol / L NaSiO 3 •9H 2 Add 10mL of O solution into the solution to form a blue precipitate, stir for 180min, then transfer to a 150mL hydrothermal kettle, move to an oven for 12-36 hours under 473K hydrothermal treatment, then take it out for cooling, filter, wash, dry, and roast. Vested CuPNTs. Then 0.113g solid RhCl 3 Add to 25ml absolute ethanol and sonicate to aid in dissolution. RhCl 3After the solids are completely dissolved, pour 0.5g of CuPNTs weighed in advance, and continue to sonicate. After the CuPNTs are completely dissolved, sonicate for another 20 minutes and take it out of the ultrasonic cleaner. Add 25ml of deioni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Rh@CuSiO 3 Nanostructured hydrogenation catalyst and preparation method thereof. This Rh@CuSiO 3 The preparation process of the hydrogenation catalyst is: first, use a hydrothermal method to synthesize silicate nanotubes in an ethanol-water system, and control the synthesis of copper silicate nanotubes by adjusting experimental conditions; then, use an impregnation method to synthesize copper silicate nanotubes. The nanotube is loaded with metal rhodium. Rh@CuSiO prepared by this method 3 By coupling the structural confinement effect of the core-sheath material and the synergistic effect between components, the hydrogenation catalyst can improve the dispersion of active components and their interaction with the carrier, thereby improving the catalytic hydrogenation reaction performance and has a wide range of applications. prospect.

Description

technical field [0001] The present invention relates to a kind of Rh@CuSiO 3 Nanostructured noble metal catalyst and preparation method thereof, the catalyst uses confinement to make Rh species exist in the form of nanoparticles, has a high amount of Rh active components and thermal stability, and can be used for CO 2 Catalytic hydrogenation reaction. Background technique [0002] CO 2 Catalytic hydrogenation reaction can convert and produce a variety of low-carbon compounds, which is of great significance to environmental protection and industrial production. So far, CO 2 Catalysts for catalytic hydrogenation are usually heterogeneous systems, which can be mainly classified into supported catalysts with copper, noble metals and bimetallic active components. Among them, typical noble metals such as Rh have strong H 2 Dissociation and hydrogenation reaction ability, and the metal Rh is in the periodic table of elements between the elements (Fe, Co) that easily decompose ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/89B01J37/03B01J37/08B01J37/10
CPCB01J23/8926B01J37/031B01J37/08B01J37/10B01J35/396
Inventor 岳海荣廖瑞唐思扬刘长军梁斌
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com