Aging-resistant easy-welding thermoplastic polyolefin waterproof roll material and preparation method thereof

A thermoplastic polyolefin and waterproof membrane technology, which is applied in the field of anti-aging and easy-to-weld thermoplastic polyolefin waterproof membrane and its preparation, to achieve the effects of good waterproof performance, good construction performance and easy welding

Active Publication Date: 2018-05-01
广州大禹防漏技术开发有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above method only solves a certain problem of thermoplastic polyolefin waterproofing membrane in a targeted manner. As for how to improve the aging resistance and welding performance of thermoplastic polyolefin waterproofing membrane from the aspects of formula system and equipment technology, it is still a question. need further study

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aging-resistant easy-welding thermoplastic polyolefin waterproof roll material and preparation method thereof
  • Aging-resistant easy-welding thermoplastic polyolefin waterproof roll material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Take 50 parts of polyolefin thermoplastic elastomer, 30 parts of polypropylene, and 20 parts of filler masterbatch, and use it as a benchmark for the mass fraction of other materials, mix it in a high-speed mixer (500r / min) for 15 minutes, and set the twin-screw extruder The temperature is 200°C, and the above-mentioned uniformly mixed materials are put into the first feeding port, 0.15 parts of light stabilizer, 1.5 parts of rutile titanium dioxide, and 0.1 part of antioxidant are put into the second feeding port, 0.15 parts of light stabilizer, rutile 1.5 parts of titanium dioxide and 0.1 part of antioxidant were put into the third feeding port, and elliptical particles were obtained through extrusion, granulation and dicing. In the second step, the elliptical particles are put into a sheet material extruder, and the thermoplastic polyolefin waterproof membrane of Example 1 is obtained through extrusion, calendering, tempering, traction, and winding.

Embodiment 2

[0044]Take 60 parts of polyolefin thermoplastic elastomer, 30 parts of polypropylene, and 10 parts of filler masterbatch, and use it as a benchmark for the mass fraction of other materials, mix it in a high-speed mixer (500r / min) for 15 minutes, and set the twin-screw extruder The temperature is 200°C, and the above-mentioned uniformly mixed materials are put into the first feeding port, 0.15 parts of light stabilizer, 1.5 parts of rutile titanium dioxide, and 0.1 part of antioxidant are put into the second feeding port, 0.15 parts of light stabilizer, rutile 1.5 parts of titanium dioxide and 0.1 part of antioxidant were put into the third feeding port, and elliptical particles were obtained through extrusion, granulation and dicing. In the second step, the elliptical particles are put into a sheet material extruder, and the thermoplastic polyolefin waterproof membrane of Example 2 is obtained through extrusion, calendering, tempering, traction, and winding.

Embodiment 3

[0046] Take 60 parts of polyolefin thermoplastic elastomer, 30 parts of polypropylene, and 10 parts of filler masterbatch, and use it as a benchmark for the mass fraction of other materials, mix it in a high-speed mixer (500r / min) for 15 minutes, and set the twin-screw extruder The temperature is 200°C, and the above-mentioned uniformly mixed materials are put into the first feeding port, 0.25 parts of light stabilizer, 2 parts of rutile titanium dioxide, and 0.05 parts of antioxidant are put into the second feeding port, 0.05 parts of light stabilizer, rutile 1 part of titanium dioxide and 0.15 part of antioxidant were put into the third feeding port, and elliptical particles were obtained through extrusion, granulation and dicing. In the second step, the elliptical particles are put into a sheet material extruder, and the thermoplastic polyolefin waterproof membrane of Example 3 is obtained through extrusion, calendering, tempering, traction, and winding.

[0047] attached ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aging-resistant easy-welding thermoplastic polyolefin waterproof roll material and a preparation method thereof. The aging-resistant easy-welding thermoplastic polyolefin waterproof roll material consists of the following raw materials in parts by mass: 40-60 parts of polyolefin elastomer, 20-40 parts of polypropylene, 10-30 parts of filling masterbatch, 0.2-0.5 part ofantioxidant, 0.2-0.6 part of light stabilizer, and 1-4 parts of titanium dioxide. The aging-resistant easy-welding thermoplastic polyolefin waterproof roll material is prepared through a two-step method, and the preparation method comprises a first step of raw material extrusion granulation and a second step of particle press polish molding. The prepared thermoplastic polyolefin waterproofing rollmaterial has excellent aging resistance and long-term weather resistance, has good high and low temperature performance, is easy welding, has good waterproof performance, is not easy to crack, is green and environmentally friendly, has good construction performance, and can be applied to areas with larger environment temperature changes.

Description

technical field [0001] The invention relates to an aging-resistant and easy-to-weld thermoplastic polyolefin waterproof coiled material and a preparation method thereof. Background technique [0002] With the popularization and development of various modern buildings and related technologies, the demand for waterproof materials in the field of construction engineering is increasing, and the quality requirements for them are also getting higher and higher. With the introduction of single-ply roofing systems in Europe and the United States and rapid development at home and abroad, its supporting waterproof membranes are also developing continuously, and have gradually become the mainstream of waterproof membrane development. As a new type of waterproof membrane, thermoplastic polyolefin waterproof membrane is mainly composed of hydrocarbons and does not contain other chemical elements. It has the weather resistance of EPDM waterproof membrane and the performance of PVC waterpr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/12C08L23/06C08K13/02C08K3/22C08K3/26C08K5/526
CPCC08K2003/2241C08K2003/265C08L23/16C08L2201/08C08L2205/03C08L23/12C08L23/06C08K13/02C08K3/22C08K3/26C08K5/526
Inventor 周智轶
Owner 广州大禹防漏技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com