Packaging plastic thin film containing modified kaolinite powder

A technology of kaolinite powder and plastic film, applied in the field of plastic film materials, can solve the problems of poor pressure resistance and impact resistance of plastic film, troublesome daily use, etc. Effect

Inactive Publication Date: 2018-05-08
桐城市桃花制刷有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing plastic films have poor pressure resistance and impact resistance, and cause troubles in daily use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A packaging plastic film containing modified kaolinite powder, which comprises the following raw materials in parts by weight: 50 parts of ethylene-vinyl acetate copolymer, 10 parts of triethylene glycol diisocaprylate, 2 parts of polyethylene wax powder Parts, 2 parts of vinyl triethoxysilane, 1 part of butyltin mercaptide, 6 parts of fumarate, 5 parts of disulfide carbamate, 1 part of nano titanium dioxide, 1 part of antioxidant, 5 parts of plasticizer, 1 part of nano clay, 8 parts of stearic acid, 4 parts of cellulose acetate butyrate, 5 parts of carbon black, 3 parts of attapulgite, and 3 parts of modified kaolinite powder.

[0017] The preparation method of the described packaging plastic film that contains modified kaolinite powder, it comprises the following steps:

[0018] (1) Take each raw material component according to the ratio in parts by weight;

[0019] (2) adding each raw material component prepared in the step (1) into a kneader and fully stirring even...

Embodiment 2

[0022] A packaging plastic film containing modified kaolinite powder, which comprises the following raw materials in parts by weight: 62 parts of ethylene-vinyl acetate copolymer, 20 parts of triethylene glycol diisocaprylate, 6 parts of polyethylene wax powder 6 parts of vinyl triethoxysilane, 2 parts of butyltin mercaptide, 12 parts of fumarate, 13 parts of disulfide urethane, 4 parts of nano titanium dioxide, 3 parts of antioxidant, 7 parts of plasticizer, 5 parts of nano clay, 12 parts of stearic acid, 9 parts of cellulose acetate butyrate, 10 parts of carbon black, 7 parts of attapulgite, and 6 parts of modified kaolinite powder.

[0023] The preparation method of the described packaging plastic film that contains modified kaolinite powder, it comprises the following steps:

[0024] (1) Take each raw material component according to the ratio in parts by weight;

[0025] (2) adding each raw material component prepared in the step (1) into a kneader and fully stirring even...

Embodiment 3

[0028] A packaging plastic film containing modified kaolinite powder, which comprises the following raw materials in parts by weight: 60 parts of ethylene-vinyl acetate copolymer, 14 parts of triethylene glycol diisocaprylate, 4 parts of polyethylene wax powder 3 parts of vinyl triethoxysilane, 2 parts of butyltin mercaptide, 9 parts of fumarate, 8 parts of disulfide urethane, 3 parts of nano titanium dioxide, 2 parts of antioxidant, 6 parts of plasticizer, 5 parts of nano clay, 10 parts of stearic acid, 7 parts of cellulose acetate butyrate, 9 parts of carbon black, 5 parts of attapulgite, and 5 parts of modified kaolinite powder.

[0029] The preparation method of the described packaging plastic film that contains modified kaolinite powder, it comprises the following steps:

[0030] (1) Take each raw material component according to the ratio in parts by weight;

[0031] (2) adding each raw material component prepared in the step (1) into a kneader and fully stirring evenly,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses packaging plastic thin film containing modified kaolinite powder. The packaging plastic thin film containing the modified kaolinite powder is prepared from, by weight, 50-62 parts of ethylene-vinyl acetate copolymer, 10-20 parts of triethylene glycol di-2-ethylhexoate, 2-6 parts of polyethylene wax powder, 2-6 parts of vinyltriethoxysilane, 1-2 parts of butylmercaptooxo stannane, 6-12 parts of fimethyl fumarate, 5-13 parts of disulfide carbamate, 1-4 parts of nano titanium dioxide, 1-3 parts of antioxidant, 5-7 parts of plasticizer, 1-5 parts of nano clay, 8-12 parts ofstearic acid, 4-9 parts of cellulose acetate butyrate, 5-10 parts of carbon black, 3-7 parts of attapulgite and 3-6 parts of modified kaolinite powder. Compared with the prior art, the packaging plastic thin film containing the modified kaolinite powder has good pressure resistance and impact resistance, and the service life is prolonged conveniently.

Description

technical field [0001] The invention belongs to the field of plastic film materials, in particular to a packaging plastic film containing modified kaolinite powder. Background technique [0002] Plastic packaging and plastic packaging products are taking an increasing share in the market, especially composite plastic flexible packaging, which has been widely used in food, medicine, chemical and other fields. For example, beverage packaging and quick-frozen food packaging are widely used in food , cooking food packaging, fast food packaging, etc., these products have brought great convenience to people's lives. However, the existing plastic films have poor pressure resistance and impact resistance, and bring troubles to daily use. Contents of the invention [0003] The object of the present invention is to provide a packaging plastic film containing modified kaolinite powder, which has good pressure resistance and impact resistance, and is beneficial to prolong service lif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L1/14C08K13/06C08K9/00C08K3/34C08K5/103C08K5/5425C08K3/22C08K5/09C08K3/04C08J5/18
CPCC08J5/18C08J2323/08C08J2401/14C08J2423/06C08K3/04C08K3/346C08K5/09C08K5/103C08K5/5425C08K9/00C08K13/06C08K2003/2241C08K2201/011
Inventor 叶倩倩
Owner 桐城市桃花制刷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products