Super-amphiphobic corrosion resistant coating for rain gauge and preparation method thereof

A corrosion-resistant coating, super-amphiphobic technology, applied in coatings, anti-corrosion coatings, fire-resistant coatings, etc., can solve the problems of water funnels being easily corroded, easily stained with impurities, and affecting the service life of rain gauges, etc., to achieve excellent Hydrophobic and oleophobic properties and anti-fouling properties, good high temperature resistance, improved service life and the effect of measurement precision

Active Publication Date: 2018-05-11
BEIJING FORESTRY UNIVERSITY
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The rain gauge is an important instrument for field rainfall observation, but when the existing rain gauge is placed in the field for a long time, the inner wall of the rain gauge and the water receiving funnel of the rain gauge are easily corroded, and it is easy to be contaminated with impurities, which not only affects The service life of the rain gauge is shortened, and the measurement accuracy of the rain gauge is affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-amphiphobic corrosion resistant coating for rain gauge and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] Specifically, the preparation method of the superamphiphobic corrosion-resistant coating for rain gauges includes: by weight, 40-60 parts of silicone epoxy resin, 10-20 parts of polytetrafluoroethylene, polyether ether 10-20 parts of ketone, 20-25 parts of polydopamine, 20-25 parts of nano-polyaniline modified oxyferric chloride, 5-10 parts of aluminum tripolyphosphate, 5-10 parts of talcum powder, 5-10 parts of nano-silver particles 1 to 3 parts of silane coupling agent, 1 to 2 parts of wetting agent, 0.5 to 2 parts of defoamer, 0.5 to 2 parts of dispersant, and 30 to 50 parts of n-butanol to obtain the first component and then uniformly mix the first component with 5-10 parts of curing agent, so as to obtain the super amphiphobic corrosion-resistant coating for rain gauge. In practical applications, the nano-polyaniline modified oxyferric chloride is preferably prepared by the following preparation method, which may specifically include the following steps:

[0046] ...

Embodiment 1

[0056] A superamphiphobic corrosion-resistant coating for rain gauges, the preparation method comprising: by weight, 60 parts of silicone epoxy resin, 20 parts of polytetrafluoroethylene, 20 parts of polyether ether ketone, polydopamine 25 parts, 25 parts of nano-polyaniline modified oxyferric chloride, 10 parts of aluminum tripolyphosphate, 10 parts of talcum powder, 10 parts of nano-silver particles, 3 parts of silane coupling agent, 2 parts of wetting agent, defoamer 2 parts, 2 parts of dispersant, and 50 parts of n-butanol are mixed together to obtain the first component; and then the first component is uniformly mixed with 10 parts of curing agent, thereby making a super amphiphobic corrosion-resistant coating .

Embodiment 2

[0058] A superamphiphobic corrosion-resistant coating for rain gauges, the preparation method comprising: by weight, 40 parts of silicone epoxy resin, 10 parts of polytetrafluoroethylene, 10 parts of polyether ether ketone, polydopamine 20 parts, 20 parts of nano-polyaniline modified oxyferric chloride, 5 parts of aluminum tripolyphosphate, 5 parts of talcum powder, 5 parts of nano-silver particles, 10 parts of silane coupling agent, 1 part of wetting agent, defoamer 0.5 parts, 0.5 parts of dispersant, and 30 parts of n-butanol are mixed together to obtain the first component; then the first component is uniformly mixed with 5 parts of curing agent to obtain a super amphiphobic corrosion-resistant coating .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a super-amphiphobic corrosion resistant coating for rain gauge and a preparation method thereof. The super-amphiphobic corrosion resistant coating is prepared from, by weight,40-60 parts of organosilicon epoxy resin, 5-10 parts of curing agent, 10-20 parts of polytetrafluoroethylene, 10-20 parts of polyether-ether-ketone, 20-25 parts of polydopamine, 20-25 parts of oxygenbased ferric chloride modified by nano polyaniline, 5-10 parts of aluminium triphosphate, 5-10 parts of talc powder, 5-10 parts of nano silver particles, 1-3 parts of silane coupling agent, 1-2 partsof wetting agent, 0.5-2 parts of defoamer, 0.5-2 parts of dispersant and 30-50 parts of n-butyl alcohol. The super-amphiphobic corrosion resistant coating not only has good properties of high temperature resistance, high pressure resistance, strong acid resistance, strong alkali resistance, corrosion resistance and the like, but also has an excellent hydrophobic and oileophobic property and an anti fouling property, can significantly prolong the service-life of the rain gauge, and significantly improve the measurement precision of the rain gauge.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings for rain gauges, in particular to a super-amphiphobic anti-corrosion coating for rain gauges and a preparation method thereof. Background technique [0002] The rain gauge is an important instrument for field rainfall observation, but when the existing rain gauge is placed in the field for a long time, the inner wall of the rain gauge and the water receiving funnel of the rain gauge are easily corroded, and it is easy to be contaminated with impurities, which not only affects The service life of the rain gauge is shortened, and the measurement accuracy of the rain gauge is affected. Contents of the invention [0003] Aiming at the above deficiencies in the prior art, the present invention provides a superamphiphobic corrosion-resistant coating for rain gauges and a preparation method thereof, which not only has good resistance to high temperature, high pressure, strong acid and a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D127/18C09D161/16C09D179/04C09D5/08C09D5/16C09D7/61C09D7/62C09D7/63
CPCC08K2003/0806C08K2003/327C08L2205/035C09D5/08C09D5/1618C09D5/1662C09D5/1687C09D5/18C09D163/00C08L27/18C08L61/16C08L79/04C08K13/06C08K9/08C08K3/16C08K3/32C08K3/34C08K3/08
Inventor 马岚梅雪梅朱清科李柏张栋王梓默陈佩岩刘京晶黎俊佑
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com