An environmental protection and floor technology, applied in polyester coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of general coating performance, many construction problems and high cost, achieve excellent health performance, improve performance, improve The effect of adhesion

Inactive Publication Date: 2018-06-08
ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the existing high-grade floor paint uses synthetic fatty acid and acrylic acid system, which has good performance, but the cost is high, and the market is difficult to accept; other systems have advantages in price, but the coating film performance is average, and there are many construction problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of strong adhesion wear-resisting environmental protection floor coating of the present embodiment comprises the raw material of following weight part:

[0037] 20 parts of high temperature resistant filler, 15 parts of silicone resin, 5 parts of wear-resistant additive, 45 parts of reinforced resin, 2 parts of anti-sedimentation agent, 1 part of auxiliary agent, 3 parts of synergist, 30 parts of organic solvent.

[0038] The high-temperature-resistant filler in this embodiment is a mixture of quartz powder, mica powder, and talcum powder in a weight ratio of 2:1:2, and the specification of the high-temperature-resistant filler is over 400 mesh;

[0039] The wear-resistant additive is a mixture of nano zirconia and nano ceramic powder in a weight ratio of 2:1.

[0040] The reinforcing resin in this example is a mixture of fatty acid-modified low-viscosity short-oil alkyd resin and benzene-free high-hydroxyl short-oil alkyd resin in a weight ratio of 3:2. The benz...

Embodiment 2

[0051] A kind of strong adhesion wear-resisting environmental protection floor coating of the present embodiment comprises the raw material of following weight part:

[0052] 25 parts of high temperature resistant filler, 25 parts of silicone resin, 8 parts of wear-resistant additive, 55 parts of reinforced resin, 4 parts of anti-sedimentation agent, 3 parts of auxiliary agent, 5 parts of synergist, 40 parts of organic solvent.

[0053] The high-temperature-resistant filler in this embodiment is a mixture of quartz powder, mica powder, and talcum powder in a weight ratio of 2:1:2, and the specification of the high-temperature-resistant filler is over 400 mesh;

[0054] The wear-resistant additive is a mixture of nano zirconia and nano ceramic powder in a weight ratio of 2:1.

[0055] The reinforcing resin in this example is a mixture of fatty acid-modified low-viscosity short-oil alkyd resin and benzene-free high-hydroxyl short-oil alkyd resin in a weight ratio of 3:2. The ben...

Embodiment 3

[0066] A kind of strong adhesion wear-resisting environmental protection floor coating of the present embodiment comprises the raw material of following weight part:

[0067] 24 parts of high temperature resistant filler, 20 parts of silicone resin, 7 parts of wear-resistant additive, 50 parts of reinforced resin, 3 parts of anti-sedimentation agent, 2 parts of auxiliary agent, 4 parts of synergist, 35 parts of organic solvent.

[0068] The high-temperature-resistant filler in this embodiment is a mixture of quartz powder, mica powder, and talcum powder in a weight ratio of 2:1:2, and the specification of the high-temperature-resistant filler is over 400 mesh;

[0069] The wear-resistant additive is a mixture of nano zirconia and nano ceramic powder in a weight ratio of 2:1.

[0070] The reinforcing resin in this example is a mixture of fatty acid-modified low-viscosity short-oil alkyd resin and benzene-free high-hydroxyl short-oil alkyd resin in a weight ratio of 3:2. The ben...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-viscosity wear-resistant environment-friendly floor paint, and a preparation method thereof. The high-viscosity wear-resistant environment-friendly floor paint is preparedfrom the following raw materials in parts by weight: 20 to 25 parts of high temperature resistant filler, 15 to 25 parts of organic silicon resin, 5 to 8 parts of wear-resistant additive, 45 to 55 parts of reinforced resin, 2 to 4 parts of anti-settling agent, 1 to 3 parts of assistant agent, 3 to 5 parts of synergistic agent, and 30 to 40 parts of organic solvent. A membrane layer obtained through the floor paint provided by the invention is smooth and good in adhesion, has effects of wear resistant, water resistant and high temperature resistant, is good in levelling property, excellent intactility, and superior in combination property, and additionally has a certain performances of air purification, sterilization and mildewproof; meanwhile, the high-viscosity wear-resistant environment-friendly floor paint provided by the invention is safe and reliable in raw material components, non-toxic and harmless, easy to get raw materials, lower in cost, simple and clear in process, and easy to operate and realizes industrial production, and has a higher practical value and a favorable application prospect.

Description

technical field [0001] The invention relates to the technical field of floor protection, in particular to a strong adhesive, wear-resistant and environmentally friendly floor paint and a preparation method thereof. Background technique [0002] The floor is generally easy to wear due to people's walking or dragging of heavy objects, so it needs to be painted with a layer of protective paint, so the surface is smooth, wear-resistant and water-resistant. There are currently two types of floor coatings commonly used: water-based paints and solvent-based paints. Water-based paint uses water as a solvent, and after the water evaporates, a paint film is formed. Due to the excessive stress and poor flexibility of the coating film after curing, the paint film is easy to crack and blisters are easy to occur. The higher the temperature and the greater the air humidity, the easier the blisters will occur and the faster the development speed. affect the decorative effect. However, ex...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D5/14C09D7/61C09D7/65
Inventor 艾明贤
Owner ANHUI YINUO WOOD PLASTIC SHEET TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap