Ba-Pt-Cr aluminum alloy applied to corrosion-resistant copper-clad aluminum wire

A ba-pt-cr, copper-clad aluminum wire technology, applied in the field of alloys, can solve the problems of aluminum-barium alloy research, development and application limitations, easy to produce flux inclusions in castings, complex equipment, etc., to achieve excellent filling performance, metal The effect of low liquid absorptivity and low tendency to form shrinkage cavities

Inactive Publication Date: 2018-06-15
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has the disadvantages of high cost to varying degrees, flux inclusions in castings, and complicated equipment.
Therefore, the research, development and application of aluminum-barium alloys are limited.
Therefore, in the industrial and national defense fields that are in urgent need of large-scale use of aluminum-barium alloys, there has always been a current situation that needs to be overcome, such as low output, cumbersome processes, and high costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A Ba-Pt-Cr aluminum alloy for copper-clad aluminum wire with corrosion resistance smelted at 750 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.6wt.%, Pt: 0.2wt.%; Cr: 0.5wt.%, Sn: 0.3wt.%, Y: 0.9wt.%, Th: 0.2wt .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 750 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 750°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 12m / min. The ingot can be used as extrusion raw material for extrusion to prepare aluminum wires of various diameters. Copper-clad aluminum wires can be prepared by combi...

Embodiment 2

[0022] A Ba-Pt-Cr aluminum alloy for copper-clad aluminum wire with corrosion resistance smelted at 770 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.5wt.%, Pt: 0.3wt.%; Cr: 0.6wt.%, Sn: 0.3wt.%, Y: 0.9wt.%, Th: 0.3wt .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 770 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 770°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square ingots and round ingots. The ingot moving speed is 14m / min. The ingot can be used as extrusion raw material for extrusion to prepare aluminum wires of various diameters. Copper-clad aluminum wires can be prepared by combini...

Embodiment 3

[0025] A Ba-Pt-Cr aluminum alloy for copper-clad aluminum wire with corrosion resistance smelted at 790 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ba: 0.7wt.%, Pt: 0.3wt.%; Cr: 0.5wt.%, Sn: 0.3wt.%, Y: 1.1wt.%, Th: 0.2wt.% .%, the balance is aluminum. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 790 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 790°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 12m / min. The ingot can be used as extrusion raw material for extrusion to prepare aluminum wires of various diameters. Copper-clad aluminum wires can be prepared by com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses Ba-Pt-Cr aluminum alloy applied to a corrosion-resistant copper-clad aluminum wire and a machining process of the Ba-Pt-Cr aluminum alloy. The Ba-Pt-Cr aluminum alloy comprisesthe following components in percentage by weight: 0.5-0.8 wt% of Ba, 0.2-0.4 wt% of Pt, 0.5-0.6 wt% of Cr, 0.2-0.4 wt% of Sn, 0.8-1.2 wt% of Y, 0.1-0.3 wt% of Th and the balance of aluminum. The aluminum-barium alloy has excellent mechanical properties and corrosion resistance which the traditional aluminum alloy applied to the copper-clad aluminum wire does not have. The Ba-Pt-Cr aluminum alloyis widely applied to the electric appliance manufacturing industry, the electric wire and cable industry and the radio industry.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an aluminum-barium alloy. Background technique [0002] With the rapid development of the national economy and the continuous improvement of people's living standards, the demand for electricity has increased sharply, and transmission lines are increasingly developing in the direction of large capacity, which requires increasing the transmission capacity of wires. Aluminum alloy conductors have been used in overhead lines as early as 1921. With the improvement of power transmission and transformation technology and the development of power transmission and transformation lines, aluminum alloy wires are increasingly showing their superiority. Since the 1950s, it has been widely used in Western Europe, Northern Europe, the United States, Canada, Japan and other countries. In France, more than 90% of the transmission lines use aluminum alloy conductors, and Japan has also reached mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/00C22C1/02C22F1/04
CPCC22C21/003C22C1/026C22F1/04
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap