Process for producing novel antibacterial thermal home textile yarns

A kind of yarn and new technology, applied in the field of textiles, can solve the problems of poor moisture absorption and air permeability, poor bulkiness, easy to grow mites, etc., and achieve the effects of improving moisture absorption and air permeability, low pilling rate, and less hairiness

Inactive Publication Date: 2018-06-22
IANGSU COLLEGE OF ENG & TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Home textile fabrics usually require breathability, warmth retention, and moisture absorption. At present, cotton home textile fabrics are commonly used, which have better warmth retention properties, but they all have some disadvantages, such as hard hand feeling, poor bulkiness, slightly poor moisture absorption and air permeability, and are prone to mites, causing Respiratory tract, skin and other diseases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0020] A new type of antibacterial and warm household yarn, which is composed of coffee carbon fiber, modal fiber and PTT fiber blended. The novel antibacterial and warm household yarn consists of the following parts by weight: 35 parts of coffee carbon fiber, 15 parts of modal fiber and 15 parts of PTT fiber. The coffee carbon fiber is 1.5D, 38mm, hollow circular hole, special-shaped, and the coffee carbon fiber is sprayed with 1% nano-titanium dioxide antibacterial liquid, and the spraying rate is 20g / m 2 , Dry at 90°C. The specification of the modal fiber is 1.4D, 37mm. The specification of the PTT fiber is 0.8D, 36mm, ultra-fine, cashmere-like staple fiber.

[0021] The weaving method of the novel antibacterial and warm household yarn comprises a cleaning process, a carding process, a drawing process, a roving process, and a spinning process; the specific operation steps are as follows:

[0022] (1) Cleaning process: Blend the three raw materials fibers of coffee carbon...

specific Embodiment 2

[0027] A new type of antibacterial and warm household yarn, which is composed of coffee carbon fiber, modal fiber and PTT fiber blended. The novel antibacterial and warm household yarn consists of the following parts by weight: 65 parts of coffee carbon fiber, 25 parts of modal fiber and 25 parts of PTT fiber. The coffee carbon fiber is 10D, 42mm, hollow circular hole, special-shaped, and the coffee carbon fiber is sprayed with 3% nano-titanium dioxide antibacterial liquid, and the spray coating is 50g / m 2 , Dry at 110°C. The specification of the modal fiber is 1.6D, 39mm. The specification of the PTT fiber is 1.2D, 39mm, ultra-fine, cashmere-like staple fiber.

[0028] The weaving method of the novel antibacterial and warm household yarn comprises a cleaning process, a carding process, a drawing process, a roving process, and a spinning process; the specific operation steps are as follows:

[0029] (1) Cleaning process: Blend the three raw materials fibers of coffee carbon...

specific Embodiment 3

[0034] A new type of antibacterial and warm household yarn, which is composed of coffee carbon fiber, modal fiber and PTT fiber blended. The novel antibacterial and warm household yarn consists of the following parts by weight: 55 parts of coffee carbon fiber, 19 parts of modal fiber and 22 parts of PTT fiber. The coffee carbon fiber is 7D, 40mm, hollow circular hole, special-shaped, and the coffee carbon fiber is sprayed with 2% nano-titanium dioxide antibacterial liquid, and the spraying rate is 35g / m 2 , Dry at 100°C. The specification of the modal fiber is 1.5D, 38mm. The specification of the PTT fiber is 1.1D, 38mm, ultra-fine, cashmere-like staple fiber.

[0035] The weaving method of the novel antibacterial and warm household yarn comprises a cleaning process, a carding process, a drawing process, a roving process, and a spinning process; the specific operation steps are as follows:

[0036] (1) Cleaning process: Blend the three raw materials fibers of coffee carbon ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for spinning and weaving novel antibacterial thermal home textile yarns. The novel antibacterial thermal home textile yarns comprise, by weight, 35%-65% of coffee carbon fibers, 15%-25% of modal fibers and 15%-25% of PTT (polytrimethylene terephthalate) fibers. The coffee carbon fibers, the modal fibers and the PTT fibers are blended to form the novel antibacterialthermal home textile yarns. The method for processing the novel antibacterial thermal home textile yarns includes working procedures of blowing, cotton carding, drawing, roving, spinning and the like. The method has the advantages that the method includes simple processes, and the novel antibacterial thermal home textile yarns can be automatically produced by the aid of the method on a large scale; the novel antibacterial thermal home textile yarns are skin-friendly, comfortable, antibacterial and thermal, and are high in yarn strength, low in hairiness and excellent in moisture absorption and breathability, pilling can be prevented, requirements of consumers in family, hotels and the like can be met, home textile fabrics woven by the aid of the method are fluffy and thermal, and accordingly the method has an excellent application prospect.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a production process of a novel antibacterial and warm-keeping yarn for home textiles. Background technique [0002] Home textile fabrics usually require breathability, warmth retention, and moisture absorption. At present, cotton home textile fabrics are commonly used, which have better warmth retention properties, but they all have some disadvantages, such as hard hand feeling, poor bulkiness, slightly poor moisture absorption and air permeability, and are prone to mites, causing Respiratory, skin and other diseases. Contents of the invention [0003] Purpose of the invention: In order to solve the deficiencies of the prior art, the present invention provides a new type of antibacterial and warm home textile yarn. After weaving, the home textile fabric is fluffy and warm, skin-friendly and comfortable, with high yarn strength and less hairiness. Pilling, good moisture absorption and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/44D06M11/46D06M101/40
CPCD02G3/045D02G3/44D02G3/449D06M11/46D06M16/00D06M2101/40D10B2201/22D10B2331/04
Inventor 张炜栋黄旭
Owner IANGSU COLLEGE OF ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap