Light solid wood sectional material and manufacturing method thereof
A manufacturing method and lightweight technology, applied in wood treatment, impregnated wood, manufacturing tools, etc., can solve the problems of logistics, use and construction process, increase the logistics cost of the final product, and consume a lot of labor and working hours. The decoration effect is natural, the logistics cost is increased, and the transportation effect is beneficial
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1: A lightweight solid wood profile, including a Paulownia solid wood profile with a thickness of 2 mm, the Paulownia solid wood profile contains 20-25 wt% of polymer resin, and its porosity is 70-75 vol% and the density is 6% when the moisture content is 6%. 0.32-0.38g / cm 3 , The static bending strength is 30-35Mpa, and the elastic modulus is 4100-4300 Mpa. The porosity of the paulownia solid wood profile is obtained by impregnating the paulownia solid wood board with a lightweight mixture, the lightweight mixture includes a melamine resin with a solid content of 60% and an azo compound chemical foaming agent with a content of 3wt% , 0.1wt% of acrylic modifier and 0.1wt% of etherified melamine resin crosslinking agent.
[0025] This lightweight solid wood profile is manufactured through the following steps:
[0026] a. Prepare a Paulownia solid wood blank by sawing to obtain a Paulownia solid wood blank with a thickness of 2 mm;
[0027] b. Pretreatment, soa...
Example Embodiment
[0031] Example 2: A lightweight solid wood profile, comprising a paulownia solid wood profile with a thickness of 6 mm, the paulownia solid wood profile comprising 35-40 wt % of polymer resin, and its porosity is 65-70 vol %, and its density is 6 % moisture content 0.50-0.56g / cm 3 , The static bending strength is 35-40Mpa, and the elastic modulus is 4300-4500 Mpa. The porosity of the paulownia solid wood profile is obtained by impregnating the paulownia solid wood board with a lightweight mixture, which includes a melamine resin with a solid content of 75% and an azo compound chemical foaming agent with a content of 1 wt%. , 0.5wt% of acrylic modifier and 0.2wt% of etherified melamine resin crosslinking agent.
[0032] This lightweight solid wood profile is manufactured through the following steps:
[0033] a. Prepare a Paulownia solid wood blank by sawing to obtain a Paulownia solid wood blank with a thickness of 2 mm;
[0034] b. Pretreatment, soaking the paulownia solid ...
Example Embodiment
[0038] Example 3: A lightweight solid wood profile, comprising a paulownia solid wood profile with a thickness of 4 mm, the paulownia solid wood profile contains 30wt% polymer resin, and the density is 0.38 when the porosity is 68-72 vol% and the moisture content is 6% -0.50g / cm 3 , The static bending strength is 33-47Mpa, and the elastic modulus is 4200-4400 Mpa. The porosity of the paulownia solid wood profile is obtained by impregnating the paulownia solid wood board with a lightweight mixture, which includes a melamine resin with a solid content of 70% and an azo compound chemical foaming agent with a content of 2wt%. , 0.3wt% of acrylic modifier and 0.15wt% of etherified melamine resin crosslinking agent.
[0039] This lightweight solid wood profile is manufactured through the following steps:
[0040] a. Prepare a Paulownia solid wood blank by sawing to obtain a Paulownia solid wood blank with a thickness of 4 mm;
[0041] b. pretreatment, soaking the paulownia solid ...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Static bending strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap