A kind of water-based PET heat-shrinkable film plastic printing ink and preparation method thereof

A heat-shrinkable film and plastic printing technology, applied in the field of plastic printing inks, can solve problems affecting workers' health, non-applicability of environmental regulations and policies, VOC emissions, etc.

Active Publication Date: 2021-05-07
中山创美涂料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In terms of supporting printing inks, the printing inks for heat-shrinkable films currently on the market are basically alcohol-ester-soluble inks, which will generate a large amount of VOC emissions in themselves and during use. The total VOC content of alcohol-ester-soluble inks can reach About 80%, on the one hand, it will affect the health of workers, on the other hand, it is not applicable to new environmental regulations and policies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based PET heat-shrinkable film plastic printing ink and preparation method thereof
  • A kind of water-based PET heat-shrinkable film plastic printing ink and preparation method thereof
  • A kind of water-based PET heat-shrinkable film plastic printing ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A water-based PET heat-shrinkable film plastic printing ink, comprising the following components by weight percentage: modified polyurethane water-based polymer emulsion 18%, water-based polyester resin 25%, 95% ethanol 9.5%, purified water 15%, titanium dioxide 30%, dispersant 0.5%, silicone 0.5%, oxidized polyethylene wax 1.5%. This formula is white ink formula, and preparation method comprises the following steps:

[0028] (1) Step 1: Weigh the raw materials according to the weight percentage of the above formula, first put purified water and 95% ethanol into the mixing tank, set the mixer speed to 325r / min, stir for 3 minutes, then mix the dispersant and modified polyurethane water-based polymerization Put the emulsion into the mixing tank, and continue to stir for 18 minutes until the materials are mixed evenly to obtain a resin mixture;

[0029] (2) Step 2: put titanium dioxide, silicone and oxidized polyethylene wax into the resin mixture in the mixing tank, set...

Embodiment 2

[0033] A water-based PET heat-shrinkable film plastic printing ink, comprising the following components by weight percentage: modified polyurethane water-based polymer emulsion 20%, water-based polyester resin 28%, 95% ethanol 16.5%, purified water 22%, phthalocyanine Blue (15:3) 10%, dispersant 2%, silicone 0.3%, oxidized polyethylene wax 1.2%. This formula is blue ink formula, and preparation method comprises the following steps:

[0034] (1) Step 1: Weigh the raw materials according to the weight percentage of the above formula, first put purified water and 95% ethanol into the mixing tank, set the mixer speed to 300r / min, stir for 3 minutes, and then mix the dispersant and modified polyurethane water-based polymerization Put the emulsion into the mixing tank, and continue to stir for 20 minutes until the materials are mixed evenly to obtain a resin mixture;

[0035] (2) Step 2: Put phthalocyanine blue (15:3), silicone and oxidized polyethylene wax into the resin mixture i...

Embodiment 3

[0039] A water-based PET heat-shrinkable film plastic printing ink, including the following components by weight percentage: modified polyurethane water-based polymer emulsion 22%, water-based polyester resin 27.6%, 95% ethanol 10.6%, purified water 24%, P.R.254 Red 11.5%, dispersant 2.8%, silicone 0.3%, oxidized polyethylene wax 1.2%. This formula is red ink formula, and preparation method comprises the following steps:

[0040] (1) Step 1: Weigh the raw materials according to the weight percentage of the above formula, first put purified water and 95% ethanol into the mixing tank, set the mixer speed to 350r / min, stir for 3 minutes, and then mix the dispersant and modified polyurethane water-based polymerization Put the emulsion into the mixing tank, and continue to stir for 15 minutes until the materials are mixed evenly to obtain a resin mixture;

[0041] (2) Step 2: Put P.R.254 red, silicone and oxidized polyethylene wax into the resin mixture in the mixing tank, set the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based PET heat-shrinkable film plastic printing ink, which comprises the following components by weight percentage: modified polyurethane water-based polymer emulsion 15-25%, water-based polyester resin 23-30%, 95% ethanol 8-20% %, purified water 15‑25%, pigment 10‑30%, dispersant 0.5‑3%, silicone 0.1‑0.8%, oxidized polyethylene wax 0.1‑3%. The invention also provides a preparation method of the printing ink. The water-based plastic printing ink for PET heat-shrinkable film of the present invention is specially used for PET heat-shrinkable film, has the advantages of environmental protection, low VOC content, safe and non-toxic printing products, good stability and strong water resistance.

Description

technical field [0001] The invention relates to the technical field of plastic printing inks, in particular to a water-based PET heat-shrinkable film plastic printing ink using a heat-shrinkable body-fitting packaging material PET heat-shrinkable film as a printing material and a preparation method thereof. Background technique [0002] PET (polyethylene terephthalate) heat-shrinkable film is a new type of heat-shrinkable packaging material, which has the characteristics of easy recycling, non-toxic, odorless, good mechanical properties, and meets environmental protection requirements. The highest heat shrinkage rate of the film can be as high as 80%. According to the development trend of heat shrinkable skin packaging materials, PET environmental protection materials will gradually replace the PVC (polyvinyl chloride) heat shrinkable film with the largest amount in the market, and become the mainstream of environmentally friendly packaging. , is an ideal substitute for PVC ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/104C09D11/102C09D11/037C09D11/03
CPCC09D11/03C09D11/037C09D11/102C09D11/104
Inventor 吴伦陈志国林秋云余钰祺冼文辉
Owner 中山创美涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com