A kind of preparation method of concrete curing agent

A concrete curing agent and catalyst technology, applied in the field of curing agents, can solve the problems of easy efflorescence and poor durability, and achieve the effects of avoiding efflorescence, increasing permeability, and accelerating curing rate.

Active Publication Date: 2020-09-15
广州德雄交通科技有限公司
View PDF19 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention: Although the current curing agent can provide concrete strength and wear resistance, but the durability is poor, and it is easy to efflorescence, the present invention provides a preparation method of concrete curing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] A preparation method of a concrete curing agent. The preparation method includes the following steps:

[0020] (1) According to the mass ratio of 6:1:12~16, take tetrabutyl titanate, aminophenyltrialkoxysilane and anhydrous ethanol for 15min ultrasonic vibration, and then add 3~5 times the mass of anhydrous ethanol 0.01 mol / L citric acid solution, mix evenly, put it into the reaction kettle, add 5-10% of the weight of tetrabutyl titanate additives, stir at 60-80℃ for 2h;

[0021] (2) After the stirring, cool to room temperature and discharge, collect the discharged material, sonicate and centrifuge the discharged material, collect the precipitate, dry the precipitate at 90°C, crush, pass through a 500 mesh sieve, and collect Sieving the particles, ball milling the sieved particles and nano-silica at a mass ratio of 3-6:5 at 800r / min for 40 minutes, and collect the ball-milled material;

[0022] (3) In parts by weight, take 50-60 parts of acetone, 30-35 parts of toluene, 20-25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a concrete curing agent, and belongs to the field of curing agents. The method includes taking tetrabutyl titanate, aminophenyl trialkoxyl silane, anhydrous ethanol and citric acid solution, mixing uniformly, adding additive, stirring, cooling and collecting a product at 60-80 DEG C, performing ultrasonic processing and centrifugation on the product,collecting precipitate, drying the precipitate, smashing and sieving the precipitate, collecting sieved particles for ball milling, and collecting a ball milling product; and taking acetone, toluene,the ball milling product, hydroxyl terminated polymethyl silicone oil, acrylic acid, phenol, ammonium persulfate and catalyst for mixing, discharging, filtration and drying and the like to obtain theconcrete curing agent.

Description

Technical field [0001] The invention belongs to the field of curing agents, and specifically relates to a preparation method of a concrete curing agent. Background technique [0002] Concrete curing agent, also known as liquid curing agent or concrete sealant, is a water-based transparent and environmentally friendly solution, colorless, odorless and non-toxic. Concrete is composed of coarse granular aggregates and cement hydrates. In the process of concrete construction, the cement components undergo a very complex chemical reaction with water to form hard hydrates, which cement the aggregates filled in to form A structure with high compressive strength, and has the advantages of economy, durability, fire resistance, and high compressive performance. However, due to the inherent process of cement hardening, concrete has the inevitable shortcomings, that is, the microstructure contains a large number of intersecting capillary pores, resulting in concrete structures that are ofte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/42
CPCC04B40/0039C04B24/40C04B24/42C04B24/008C04B24/00C04B24/04C04B22/147C04B2103/10C04B14/062
Inventor 翟琳施衍刘红妹
Owner 广州德雄交通科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap