Processing method of baking-free colorful tiles

Abstract

The invention discloses a processing method of baking-free colorful tiles. The method comprises the steps that 1) after an operation table is cleaned and leveled, an asbestos tile mold, a polyester mold and a flat steel frame are placed on the operation table, and then a thin surface-layer material is laid uniformly on the polyester mold, 400 grams of glass fiber filaments are laid, a trowel is used to press the glass fiber filaments uniformly, then one third of a back-layer materials are laid and compacted, then 300 grams of the glass fiber filaments are laid, the two thirds of the back-layermaterials are laid and flattened and compacted by the trowel, and finally a polyester film is laid on the two thirds of the back-layer materials; and 2), demolding is carried out on the formed tilesafter eight hours, wiping the tile surfaces is not allowed after the mold is stripped, then the tiles are stacked in a face-to-face and back-to-back mode or are stacked into the shape like a Chinese character "jing", the stacking height is not more than 1.5 m, and then after airing is carried out on the stacked tiles for 10 days, the stacked tiles are left to stand to be hardened for 15 days. According to the processing method of the baking-free colorful tiles, the tiles belong to building blocks which are low in cost, light in weight, high in strength and free of baking and steaming, the activity of industrial waste residues is utilized and improved, so that the industrial waste residues are enabled to have gel property, then the use amount of cement is reduced, and the cost is reduced.

Description

technical field

[0001] The invention relates to the technical field of building materials, in particular to a method for processing non-fired colorful bricks and tiles. Background technique

[0002] Wall materials are indispensable and important building materials in the construction industry. The construction industry is also a pillar industry of the national economy and plays an irreplaceable role in promoting the process of modernization in my country. Its huge construction market capacity also provides a very broad prospect for the production of wall materials. Contents of the invention

[0003] In view of this, the present invention provides a processing method of non-fired colorful tiles. The present invention overcomes the shortcomings of existing similar products such as many types of materials, heavy weight, and high cost, and provides a low-cost, light-weight, high-strength The non-burning and non-steaming building block brick and its manufacturing process utili...

Examples

Embodiment 1

[0022] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0023] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0024] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0025] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 2

[0029] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0030] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0031] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0032] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 3

[0036] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0037] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0038] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0039] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

technical field

[0001] The invention relates to the technical field of building materials, in particular to a method for processing non-fired colorful bricks and tiles. Background technique

[0002] Wall materials are indispensable and important building materials in the construction industry. The construction industry is also a pillar industry of the national economy and plays an irreplaceable role in promoting the process of modernization in my country. Its huge construction market capacity also provides a very broad prospect for the production of wall materials. Contents of the invention

[0003] In view of this, the present invention provides a processing method of non-fired colorful tiles. The present invention overcomes the shortcomings of existing similar products such as many types of materials, heavy weight, and high cost, and provides a low-cost, light-weight, high-strength The non-burning and non-steaming building block brick and its manufacturing process utili...

Examples

Embodiment 1

[0022] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0023] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0024] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0025] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 2

[0029] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0030] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0031] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0032] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...

Embodiment 3

[0036] A kind of processing method of fire-free colorful brick and tile, it is the following steps:

[0037] 1) Clean up the operation table, after it is leveled, put the asbestos tile mould, polyester mould, and flat steel frame, then spread the surface material on the polyester mould, then spread 400 grams of glass fiber filaments, and use a wipe Press it evenly, then spread one-third of the back layer material, compact it, then spread 300 grams of glass fiber filaments, and finally spread two thirds of the back layer material, use a trowel to flatten and spread the polyester film. ;

[0038] 2) The molded tiles should be removed from the mold after eight hours. Do not wipe the surface of the tiles after removing the molds. Stack the tiles face-to-face or back-to-back or well stacked. The stacking height should not exceed 1.5m. Stop and harden for 15 days.

[0039] The surface material is made by mixing magnesium oxide, fly ash or talcum powder, 191 resin, pigment and magn...