Light-weight and high-strength thermoplastic composite material sandwich board and production method thereof

A composite material board and composite material technology, which is applied in the field of thermoplastic composite sandwich panels and their production, can solve the problems of wooden boards such as flammability, high thermal conductivity, and poor corrosion resistance, and achieve the degree of strengthening and good heat insulation performance , good design flexibility

Inactive Publication Date: 2014-02-12
SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
View PDF16 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the shortcomings of the above-mentioned types of sandwich panels are: metal panels have high density, poor corrosion resistance, high thermal conductivity, and cannot achieve efficient heat insulation; wooden panels are flammable, not fireproof, and easy to absorb water and deform , poor moisture resistance, easy to corrode when encountering acid and alkali;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light-weight and high-strength thermoplastic composite material sandwich board and production method thereof
  • Light-weight and high-strength thermoplastic composite material sandwich board and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Take 200 parts of polypropylene pellets as thermoplastic matrix material, 600 parts of glass fiber (alkali-free) yarn as reinforcement material, 10 parts of antioxidant 1010, 20 parts of antioxidant 168 as antioxidant, 10 parts of organosilane A -187 is a coupling agent, 1 part of UV-531 is a light stabilizer, 150 parts of decabromodiphenyl ether is a flame retardant, and 10 parts of calcium stearate is an auxiliary agent.

[0046] Mix the above materials in a high mixer for 2 to 5 minutes except for the glass fiber, and then extrude through the extruder at 180 to 200 ° C. During the extrusion process, the molten thermoplastic melt is dipped and stretched 600 parts of non-alkali glass fiber yarns are rolled and cooled to form a prepreg tape. The thickness of the prepreg tape is about 0.21 mm.

[0047] During the panel molding process, polyethylene terephthalate release plastics are sequentially laid in the lower mold, and 3 layers of prepreg tapes are laid, arranged al...

Embodiment 2

[0050] Take 500 parts of polypropylene pellets as thermoplastic matrix material, 480 parts of glass fiber (alkali-free) cloth as reinforcing material, 1 part of antioxidant 1076, 1 part of organosilane A-174 as coupling agent, 3 parts of UV-327 It is a light stabilizer, 10 parts of chlorinated paraffin 70 is a flame retardant, and 5 parts of calcium stearate is an auxiliary agent.

[0051] Mix the above materials in a high mixer for 2 to 3 minutes except for the glass fiber, and then extrude through the extruder at 180 to 200 ° C. During the extrusion process, the molten thermoplastic melt is dipped and stretched 480 parts of non-alkali glass fiber cloth, which is rolled and cooled to form a prepreg tape. The thickness of the prepreg tape is about 0.28mm. During the panel forming process, polyethylene terephthalate release plastics are sequentially laid in the lower mold, and 7 layers of prepreg tapes are laid, arranged alternately along the fiber direction and vertical fiber...

Embodiment 3

[0054] Take 430 parts of polycarbonate pellets as thermoplastic matrix material, 450 parts of carbon fiber cloth as reinforcing material, 1 part of antioxidant 1010, 5 parts of antioxidant 1076, 10 parts of antioxidant 168 as antioxidant, take 20 parts A-187 is a coupling agent, 3 parts of UV-9 is used as a light stabilizer, and 80 parts of tetrabromobisphenol A is used as a flame retardant.

[0055] Put the above materials except carbon fiber into a high mixer and mix them for 2-3 minutes, then extrude them through an extruder at 250-260°C. 450 parts of carbon fiber cloth are rolled and cooled to form a prepreg tape, and the thickness of the prepreg tape is 0.42mm. During the molding process, polyethylene terephthalate release plastics are sequentially placed in the lower mold, 11 layers of prepreg tape are laid, polyethylene terephthalate release plastics are placed, and the upper mold is placed. Send the laid materials into a hot press for hot pressing. The hot pressing te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a light-weight and high-strength thermoplastic composite material sandwich board and a production method thereof. The light-weight and high-strength thermoplastic composite material sandwich board comprises two panels and a sandwich layer, wherein the sandwich layer is fixedly arranged between the two panels. The preparation method comprises the following steps: putting the sandwich layer between the two panels; and sticking the two panels on the front and rear faces of the sandwich layer by a thermoplastic glue film through a hot pressing process and a cold pressing process to produce the thermoplastic composite material sandwich board. The panels are continuous fiber enhanced thermoplastic composite material boards and the sandwich layer is made of a honeycomb aluminum material. Compared with the prior art, the thermoplastic composite material sandwich board has the advantages of light weight, high strength, heat preservation, fireproof prevention, moisture prevention, corrosion prevention and the like.

Description

technical field [0001] The invention belongs to the technical fields of architectural decoration and transportation, and in particular relates to a lightweight and high-strength thermoplastic composite sandwich panel and a manufacturing method thereof. Background technique [0002] With the rapid development of science and technology, there are endless types of sandwich panels used in the fields of building decoration and transportation. Not only is the structure and panel style ingenious, but also the function has undergone earth-shaking changes. People require not only beautiful appearance and reliable quality, but also light weight, high strength, flame retardant, heat preservation, heat insulation, anti-corrosion and other functions. Sandwich panels currently on the market include metal panels and other types of non-metallic panels, such as wood panels, gypsum panels, and glass steel panels. [0003] Commonly used metal sandwich panels are composed of color steel plate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/08B32B27/04B32B27/18B32B7/10B32B37/06B32B37/10
Inventor 马春霞
Owner SHANGHAI GENIUS ADVANCED MATERIAL (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap