A kind of hydrocolloid and hydrocolloid dressing and preparation method thereof

A hydrocolloid and liquid paraffin technology, applied in the field of medical materials, can solve the problems of not fast absorption, less than complete absorption, and surrounding skin damage, and achieve good moisturizing effect, strong exudate absorption ability, and skin repair effect

Active Publication Date: 2019-09-20
GUANGZHOU RAINHOME PHARM&TECH CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional hydrocolloid dressings generally cannot be used for wounds with more exudate, because the absorption efficiency of traditional hydrocolloid dressings for exudate is not very fast, so that it is too late to absorb completely for wounds with more exudate, making the exudate Spillage, damage to surrounding skin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrocolloid and hydrocolloid dressing and preparation method thereof
  • A kind of hydrocolloid and hydrocolloid dressing and preparation method thereof
  • A kind of hydrocolloid and hydrocolloid dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: prepare described hydrocolloid and hydrocolloid dressing

[0031] 1. Preparation of hydrocolloids

[0032] Take 10 parts of high molecular weight copolymers of polystyrene block and polyethylene-butylene block and 10 parts of liquid paraffin in proportion by weight, and soften in a reaction kettle at a temperature of 200 ° C for 40 minutes;

[0033] Adjust the temperature, and after the temperature drops to 100°C, take 5 parts of lanolin, 20 parts of sodium carboxymethyl cellulose, and 5 parts of sodium hyaluronate according to the weight ratio, and put them into the softened polystyrene block and polyethylene -In the high molecular weight copolymer of butene block, mix 20min with the rotating speed of 80r / min, make it mix to form the homogeneous molten substance, then vacuum defoaming, obtain hydrocolloid;

[0034] 2. Preparation of hydrocolloid dressing

[0035] Transfer the hydrocolloid after vacuum defoaming to the glue tank in the hot-melt adhesive ...

Embodiment 2

[0036] Embodiment 2: prepare described hydrocolloid and hydrocolloid dressing

[0037] 1. Preparation of hydrocolloids

[0038] Take 20 parts of high molecular weight copolymers of polystyrene block and polyethylene-propylene block and 10 parts of liquid paraffin in proportion by weight, and soften in a reaction kettle at a temperature of 200° C. for 40 minutes;

[0039] Adjust the temperature, and after the temperature drops to 150°C, take 5 parts of lanolin, 30 parts of sodium carboxymethyl cellulose, and 5 parts of sodium hyaluronate according to the weight ratio, and put them into the softened polystyrene block and polyethylene -In the high-molecular-weight copolymer of propylene block, mix 20min with the rotating speed of 100r / min, make it mix to form uniform molten substance, then vacuum defoaming, obtain hydrocolloid;

[0040] 2. Preparation of hydrocolloid dressing

[0041] Transfer the hydrocolloid after vacuum defoaming to the glue tank in the hot-melt adhesive doubl...

Embodiment 3

[0042] Embodiment 3: prepare described hydrocolloid and hydrocolloid dressing

[0043] 1. Preparation of hydrocolloids

[0044] Take 30 parts of high molecular weight copolymers of polystyrene block and polyethylene-butylene block and 15 parts of liquid paraffin in proportion by weight, and soften in a reaction kettle at a temperature of 200° C. for 40 minutes;

[0045] Adjust the temperature, and after the temperature drops to 100°C, take 10 parts of lanolin, 40 parts of sodium carboxymethyl cellulose, and 10 parts of sodium hyaluronate according to the weight ratio, and put them into the softened polystyrene block and polyethylene -In the high molecular weight copolymer of butene block, mix 30min with the rotating speed of 120r / min, make it mix to form uniform molten substance, vacuum defoaming then, obtain hydrocolloid;

[0046] 2. Preparation of hydrocolloid dressing

[0047] Transfer the hydrocolloid after vacuum defoaming to the glue tank in the hot-melt adhesive doubl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of medical materials, and discloses a hydrocolloid and a hydrocolloid dressing and a preparation method thereof. The hydrocolloid includes a thermoplasticelastomer, sodium carboxymethyl cellulose, lanolin, sodium hyaluronate, and liquid paraffin. The lanolin and the sodium carboxymethyl cellulose and the like are added to the hydrocolloid to significantly increase the liquid absorbing property, so that the hydrocolloid can be applied to a highly-exudative wound dressing, and the problem that seepage of a traditional hydrocolloid dressing is easy toleak to cause damage to the surrounding skin can be avoided.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a hydrocolloid, a hydrocolloid dressing and a preparation method thereof. Background technique [0002] Medical dressings made of natural or synthetic biological materials are called medical biological dressings. In recent years, with the rapid development of modern science and technology, the research on medical dressings has also developed rapidly. A variety of new medical dressings emerge in an endless stream, and their performance is getting better and better. The so-called medical dressing is a common type of medical material used for temporary covering of wounds and wound surfaces. This medical material can also avoid bacterial infection and external factors that affect the wound. Good protection. For patients with extensive burns, wound infection is still the most important cause of burn death. Therefore, it is necessary to search for an ideal wound covering t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/20A61L15/24A61L15/26A61L15/28A61L15/40A61L15/42A61L15/60
Inventor 黄海艳赵澎车七石刘少辉
Owner GUANGZHOU RAINHOME PHARM&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com