A kind of preparation method of light color rosin resin

A rosin resin and light-colored technology, which is applied in the field of preparation of ultra-light-colored rosin resin, can solve problems such as difficult process control, high catalyst cost, and increased product cost, and achieve the goal of improving reusability, reducing color, and reducing odor Effect

Active Publication Date: 2020-09-15
南雄市松林树脂有限公司
View PDF19 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are still great shortcomings in the process of producing light-colored rosin resin, such as complex process, long reaction time, high catalyst cost, easy deactivation, etc., and most of them adopt high-pressure hydrogenation process, which virtually increases the cost of the product. And the process is more difficult to control, resulting in poor product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of light color rosin resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Ni / Al 2 o 3 Preparation of composite materials: take Ni(NO 3 ) 2 28 parts were added to absolute ethanol for ultrasonic dissolution, and then Al 2 o 3 Pour 25 parts of powder into Ni(NO 3 ) 2 In anhydrous ethanol, rotate and immerse in a rotary evaporator for 11h, remove the solvent, then vacuum dry at 76°C for 10h, and then put it in a muffle furnace and roast at 400°C for 2h to obtain Ni / Al 2 o 3 composite materials;

[0031] Montmorillonite / Ni / Al 2 o 3 Preparation of composite materials: Ni / Al 2 o 3 The composite material was dissolved in absolute ethanol and transferred to the reaction kettle, 9 parts of nitric acid was added dropwise to the reaction kettle, then 18 parts of distilled water was slowly added dropwise, stirred for 10 minutes, 35 parts of montmorillonite powder was added to the reaction kettle, and the reaction was stirred After 2 hours, let stand for 10.5 hours, then wash with water, dehydrate, vacuum dry, and then roast at 450°C for 2 hou...

Embodiment 2

[0037] Ni / Al 2 o 3 Preparation of composite materials: take Ni(NO 3 ) 2 20 parts were added to absolute ethanol for ultrasonic dissolution, and then Al 2 o 3 Pour 30 parts of powder into Ni(NO 3 ) 2 In absolute ethanol, rotate and immerse in a rotary evaporator for 10 hours, remove the solvent, then vacuum dry at 70°C for 11 hours, and then put it in a muffle furnace and roast at 500°C for 2 hours to obtain Ni / Al 2 o 3 composite materials;

[0038] Montmorillonite / Ni / Al 2 o 3 Preparation of composite materials: Ni / Al 2 o 3 The composite material was dissolved in absolute ethanol and transferred to the reaction kettle, 10 parts of nitric acid was added dropwise to the reaction kettle, and then 20 parts of distilled water was slowly added dropwise, stirred for 10 minutes, 32 parts of montmorillonite powder were added to the reaction kettle, stirred and reacted After 2 hours, let stand for 11 hours, then wash with water, dehydrate, vacuum dry, and then roast at 400°C ...

Embodiment 3

[0044] Ni / Al 2 o 3 Preparation of composite materials: take Ni(NO 3 ) 2 30 parts were added to absolute ethanol for ultrasonic dissolution, and then Al 2 o 3 Pour 28 parts of powder into Ni(NO 3 ) 2 In absolute ethanol, rotate and immerse in a rotary evaporator for 10.5h, remove the solvent, then vacuum dry at 73°C for 12h, and then put it into a muffle furnace and roast at 420°C for 2h to obtain Ni / Al 2 o 3 composite materials;

[0045] Montmorillonite / Ni / Al 2 o 3 Preparation of composite materials: Ni / Al 2 o 3 The composite material was dissolved in absolute ethanol and transferred to the reaction kettle, 8 parts of nitric acid was added dropwise to the reaction kettle, then 19 parts of distilled water was slowly added dropwise, stirred for 10 minutes, 30 parts of montmorillonite powder was added to the reaction kettle, stirred and reacted After 2 hours, let stand for 11.5 hours, then wash with water, dehydrate, vacuum dry, and then roast at 480°C for 2 hours to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of rosin processing, in particular to a preparation method of super light-colored rosin resin. The method comprises the following preparation steps: firstly preparing a catalyst A for rosin catalytic hydrogenation, then adding rosin and the catalyst A into a reaction kettle, afterwards, sealing, then vacuumizing, detecting leakage and exhausting air, then keeping ordinary pressure in the reaction kettle, then heating to fuse the rosin, afterwards, introducing hydrogen gas to react, then filtering and performing negative pressure removal of easy volatile ingredients to obtain hydrogenated rosin; then enabling the hydrogenated rosin to react with glycerinum to prepare rosin glycerin ester, and finally cooling, pelleting and packaging to obtain thesuper light-colored rosin resin.

Description

technical field [0001] The invention belongs to the technical field of rosin processing, in particular to a preparation method of ultra-light-colored rosin resin. Background technique [0002] Rosin has many excellent properties such as anti-corrosion, moisture-proof, adhesion, emulsification, etc., and is widely used in papermaking, ink, soap, food, medicine and other industries. Rosin is an abundant renewable resin in nature obtained from the processing of pine resin. Pine resin is the oily liquid that flows out after the pine tree is cut. The pine resin is colorless just after being picked from the tree. When it is placed in the air, the turpentine in the pine resin will volatilize, and the last remaining solid substance is rosin. Rosin is mainly composed of some resin acids and some neutral substances. Resin acids are a general term for a class of compounds. The structure is a three-membered ring phenanthrene skeleton structure. It contains two active groups, double bon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09F1/04B01J23/755
CPCB01J23/755C09F1/04
Inventor 周文辽
Owner 南雄市松林树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products