Preparation method of bamboo mat not prone to deformation

A bamboo mat, not easy technology, applied in the field of non-deformable bamboo mat preparation, can solve the problems of deformation of the formed material, poor hardness of the surface layer of the bamboo mat, large internal stress of the board, etc., to prevent moisture and gas, and not easy to be insects Corrosion, good thermal stability

Inactive Publication Date: 2018-08-17
施文杰
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the hardest bamboo green on the bamboo material is removed during the preparation of the bamboo mat, and the surface layer of the shaped material is opposite to the original surface layer of the original bamboo, the surface layer of the bamboo mat is relatively hard, and it is solidified into a bamboo mat after high pressure. The profile, the internal stress of the plate is large, and the profile will be deformed due to the internal stress after a long time, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of non-deformable bamboo mat preparation method that the present invention proposes, comprises the steps:

[0019] S1. Carry out carbonization treatment on the pretreated bamboo, and then send it to the hot press to flatten to obtain the carbonized bamboo. The carbonization treatment is to send the bamboo into the drying and disinfection carbon dryer, and the heating temperature of the drying and disinfection carbon dryer is 160 ° C. , the heating time is 2 hours, the bamboo is carbonized, and the degree of carbonization is 5%;

[0020] S2. Put the carbonized bamboo into the ethanol solution, add soybean lecithin, tetraisopropyl titanate and stir, add hydrochloric acid, tartaric acid complexed copper nitrate, polyvinyl alcohol, heat up and stir, filter, wash, dry, dry, and weave to obtain Non-deformable bamboo mat.

Embodiment 2

[0022] A kind of non-deformable bamboo mat preparation method that the present invention proposes, comprises the steps:

[0023] S1. Carbonize the pretreated bamboo, and then send it to the hot press to flatten to obtain the carbonized bamboo. The carbonization process is to send the bamboo into the drying and disinfection carbon dryer, and the heating temperature of the drying and disinfection carbon dryer is 170 ° C. , the heating time is 3 hours, the bamboo is carbonized, and the degree of carbonization is 25%;

[0024] S2. Put 60 parts of carbonized bamboo into 100 parts of ethanol solution with a concentration of 75wt% by weight, add 4 parts of soybean lecithin and 8 parts of tetraisopropyl titanate and stir for 20 minutes, add 8 parts with a concentration of 1.5 mol / L Hydrochloric acid, 2 parts of tartaric acid complexed copper nitrate, 10 parts of polyvinyl alcohol, heated to 145 ° C and stirred for 4 hours, filtered, washed, dried, dried at 90 ° C, and woven to obtain ...

Embodiment 3

[0026] A kind of non-deformable bamboo mat preparation method that the present invention proposes, comprises the steps:

[0027] S1. Carry out carbonization treatment on the pretreated bamboo, and then send it to the hot press to flatten to obtain the carbonized bamboo. The carbonization treatment is to send the bamboo into the drying and disinfection carbon dryer, and the heating temperature of the drying and disinfection carbon dryer is 190 ° C. , the heating time is 4 hours, the bamboo is carbonized, and the degree of carbonization is 30%;

[0028] S2. Put 50 parts by weight of carbonized bamboo into 140 parts of ethanol solution with a concentration of 60wt%, add 8 parts of soybean lecithin and 4 parts of tetraisopropyl titanate and stir for 30 minutes, add 4 parts with a concentration of 2.5mol / L Hydrochloric acid, 1 part of tartaric acid complexed copper nitrate, 16 parts of polyvinyl alcohol, heated to 135 ° C and stirred for 8 hours, filtered, washed, dried, dried at 8...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a bamboo mat not prone to deformation. The method comprises the following steps: S1, carrying out carbonization treatment of a pretreated bamboo, then feeding the bamboo into a hot press and flattening the bamboo to obtain the carbonized bamboo, wherein the carbonization treatment is characterized by feeding the bamboo into a drying and disinfectingcarbon dryer, the heating temperature of the drying and disinfecting carbon dryer is 160-190 DEG C, the heating time is 2-4 hours, and the bamboo is carbonized at a carbonization degree of 5-30%; andS2, feeding the carbonized bamboo into an ethanol solution, adding soyabean lecithin and tetraisopropyl titanate, then stirring, adding hydrochloric acid, tartaric acid complex copper nitrate and polyvinyl alcohol, increasing the temperature and stirring, filtering, washing, drying and knitting to obtain the bamboo mat not prone to deformation.

Description

technical field [0001] The invention relates to the technical field of bamboo mats, in particular to a method for preparing a non-deformable bamboo mat. Background technique [0002] The traditional bamboo mat is to process bamboo into bamboo slices, remove the green layer and dead yellow layer, split the bamboo slices into bamboo strands or grind them into large vertically and horizontally connected bamboo strands, and put the bamboo strands or bamboo strands in a carbonization tank It is made by pyrolysis and carbonization, and then cured after high pressure. However, since the hardest bamboo green on the bamboo material is removed during the preparation of the bamboo mat, and the surface layer of the shaped material is opposite to the original surface layer of the original bamboo, the surface layer of the bamboo mat is relatively hard, and it is solidified into a bamboo mat after high pressure. The profile, the internal stress of the plate is large, and the profile will ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K9/00B27K3/52B27K3/16B27J1/02B27J1/00B27M1/06
CPCB27K9/002B27J1/00B27J1/02B27K3/16B27K3/52B27K2240/20B27M1/06
Inventor 施文杰
Owner 施文杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap