Super-hydrophilicity and high-adhesion glass surface treatment agent and preparation method thereof

A technology with high adhesion and glass surface, applied in the direction of coating, etc., can solve the problems of lack of durability and complicated processing process, and achieve the effect of low cost, wide application prospect and simple use

Active Publication Date: 2018-09-04
HUBEI UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The research of traditional glass surface superhydrophilic agents mainly focuses on nano-TiO 2 thin film, but TiO 2 Films generally need to be induced by ultraviolet rays to show superhydrophilicity, and the treatment process is more complicated. However, the method of using surfactants to treat the glass surface is simple but lacks durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-hydrophilicity and high-adhesion glass surface treatment agent and preparation method thereof
  • Super-hydrophilicity and high-adhesion glass surface treatment agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of glass surface superhydrophilic, high adhesion treatment agent of the present embodiment, described treatment agent is made of SiO 2 sol and Si-PEG polymer solution, wherein: the SiO 2 The mass ratio of sol to Si-PEG polymer solution is 1:1.

[0030] The above-mentioned glass surface superhydrophilic and high adhesion treatment agent of the present embodiment is prepared by the following method, including the following steps:

[0031] (1) SiO 2 Sol preparation:

[0032] Mix absolute ethanol, tetraethyl orthosilicate, allyltrimethoxysilane, and deionized water in a molar ratio of 1:10:10:4, then react at 30°C for 6 hours, and the reaction ends Afterwards, stand at room temperature for 12h to prepare the SiO 2 Sol;

[0033] (2) Preparation of Si-PEG polymer solution:

[0034] Under the condition of 50°C and argon, slowly drop phenyltrichlorosilane into polyethylene glycol, react for 3h, and then add isopropanol to prepare a Si-PEG polymer solution with a ma...

Embodiment 2

[0038] A kind of glass surface superhydrophilic, high adhesion treatment agent of the present embodiment, described treatment agent is made of SiO 2 sol and Si-PEG polymer solution, wherein: the SiO 2 The mass ratio of sol to Si-PEG polymer solution is 1:1.

[0039] The above-mentioned glass surface superhydrophilic and high adhesion treatment agent of the present embodiment is prepared by the following method, including the following steps:

[0040] (1) SiO 2 Sol preparation:

[0041] Mix absolute ethanol, tetraethyl orthosilicate, n-propyltrimethoxysilane, and deionized water in a molar ratio of 1:10:10:4, then react at 30°C for 6 hours, and the reaction ends Afterwards, stand at room temperature for 12h to prepare the SiO 2 Sol;

[0042] (2) Preparation of Si-PEG polymer solution:

[0043] Under the condition of 50°C and argon, slowly add methyltrichlorosilane into polyethylene glycol dropwise, react for 3h, and then add isopropanol to prepare a Si-PEG polymer solutio...

Embodiment 3

[0047] A kind of glass surface superhydrophilic, high adhesion treatment agent of the present embodiment, described treatment agent is made of SiO 2 sol and Si-PEG polymer solution, wherein: the SiO 2 The mass ratio of sol to Si-PEG polymer solution is 1:5.

[0048] The above-mentioned glass surface superhydrophilic and high adhesion treatment agent of the present embodiment is prepared by the following method, including the following steps:

[0049] (1) SiO 2 Sol preparation:

[0050] Mix absolute ethanol, tetraethyl orthosilicate, n-propyltrimethoxysilane, and deionized water in a molar ratio of 2:12:9:4, then react at 30°C for 6 hours, and the reaction ends Afterwards, stand at room temperature for 12h to prepare the SiO 2 Sol;

[0051] (2) Preparation of Si-PEG polymer solution:

[0052] Under the condition of 50°C and argon, slowly add methyltrichlorosilane into polyethylene glycol dropwise, react for 3h, and then add isopropanol to prepare a Si-PEG polymer solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
contact angleaaaaaaaaaa
Login to View More

Abstract

The invention relates to a super-hydrophilicity and high-adhesion glass surface treatment agent and a preparation method thereof. The treatment agent is prepared from SiO2 sol and a Si-PEG polymer solution, wherein the mass ratio of the SiO2 sol to the Si-PEG polymer solution is (1:1) to (1:5); the SiO2 sol is prepared by the steps of uniformly mixing absolute ethyl alcohol, ethyl orthosilicate, silane and deionized water, reacting at 20 to 40 DEG C for 5 to 7 hours, and standing at room temperature for 12 to 24 hours after the reaction; the Si-PEG polymer solution is prepared by the steps ofslowly dropwise adding chlorosilane into polyethylene glycol, reacting for 3 to 5 hours, and then adding an organic solvent. The super-hydrophilicity treatment agent has good scrubbing resistance, issimple to use, can be directly applied to the surface of glass to form a transparent super-hydrophilic film, has the advantages of short consumption time, long effect lasting time and low cost, and can be applied to building exterior glass, car windshield, etc.

Description

technical field [0001] The invention relates to the technical field of hydrophilic glass, in particular to a glass surface superhydrophilic and high adhesion treatment agent and a preparation method thereof. Background technique [0002] As two extreme wetting phenomena, superhydrophilic and superhydrophobic have attracted the attention of scholars at home and abroad. In general, a superhydrophobic surface refers to a surface with a solid-liquid contact angle greater than 150°. On the contrary, a superhydrophilic surface refers to a surface on which a liquid can spread completely and the contact angle is close to or equal to 0°. Both superhydrophilic and superhydrophobic can make the surface self-cleaning to some extent, but when the superhydrophobic surface faces water mist, it is difficult for small water droplets to roll off the surface, and the stains will remain after the water droplets evaporate on the surface. This situation makes the super-hydrophilic surface highl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/32C03C17/25
CPCC03C17/009C03C2217/445C03C2217/478C03C2217/70C03C2218/11
Inventor 施德安杨颖涂港张新立
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com