Anti-aging paint and preparation method thereof

An anti-aging and paint technology, applied in the field of anti-aging paint and its preparation, can solve the problems of not easy drying, low viscosity and long service life, and achieve the effects of not easy to fade, high viscosity and long service life

Inactive Publication Date: 2018-10-02
惠州市绿孔雀科技股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the existing ones do not have anti-aging effect, the service life is not long, the viscosity is not high, and it is not easy to dry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-aging paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-aging coating is made of the following materials in parts by weight, including 22 parts of epoxy resin, 16 parts of palm wax, 3-9 parts of polyvinyl butyral, 26 parts of ammonium aluminum sulfate, aluminum powder 4 parts, 7 parts of sugarcane wax, 16 parts of nano-silver, 3 parts of cinnabar, 8 parts of pure acrylic emulsion, 11 parts of cobalt soap, 13 parts of isononanoic acid, 6 parts of aluminum phosphate, 5 parts of acrylic resin, 12 parts of mica, inositol 16 parts of hexaphosphate, 4 parts of dodecyl alcohol ester, 10 parts of alkoxysilane, 12 parts of orthosilicic acid and 8 parts of polyisocyanate.

[0024] A preparation method of an anti-aging coating, comprising the following steps:

[0025] 1) Mix 22 parts of epoxy resin, 16 parts of palm wax, 3-9 parts of polyvinyl butyral, 26 parts of aluminum ammonium sulfate, 4 parts of aluminum powder, 7 parts of sugarcane wax, 16 parts of nano silver, 3 parts of cinnabar, Put 8 parts of pure acrylic emulsion i...

Embodiment 2

[0034] An anti-aging coating is made of the following materials in parts by weight, including 23 parts of epoxy resin, 17 parts of palm wax, 6 parts of polyvinyl butyral, 28 parts of ammonium aluminum sulfate, and 6 parts of aluminum powder , 9 parts of sugarcane wax, 18 parts of nano-silver, 4 parts of cinnabar, 9 parts of pure acrylic emulsion, 12.5 parts of cobalt soap, 15.5 parts of isononanoic acid, 7 parts of aluminum phosphate, 7.5 parts of acrylic resin, 13.5 parts of mica, phytic acid 18 parts of ester, 6 parts of dodecyl alcohol ester, 12.5 parts of alkoxysilane, 13.5 parts of orthosilicic acid and 9 parts of polyisocyanate.

[0035] A preparation method of an anti-aging coating, comprising the following steps:

[0036] 1) Mix 23 parts of epoxy resin, 17 parts of palm wax, 6 parts of polyvinyl butyral, 28 parts of ammonium aluminum sulfate, 6 parts of aluminum powder, 9 parts of sugarcane wax, 18 parts of nano silver, 4 parts of cinnabar, pure acrylic acid 9 parts o...

Embodiment 3

[0045] An anti-aging coating, made of the following materials in parts by weight, including 24 parts of epoxy resin, 18 parts of palm wax, 9 parts of polyvinyl butyral, 30 parts of ammonium aluminum sulfate, and 8 parts of aluminum powder , 11 parts of sugarcane wax, 20 parts of nano-silver, 5 parts of cinnabar, 10 parts of pure acrylic emulsion, 14 parts of cobalt soap, 18 parts of isononanoic acid, 8 parts of aluminum phosphate, 10 parts of acrylic resin, 15 parts of mica, phytic acid 20 parts of ester, 8 parts of dodecyl alcohol ester, 15 parts of alkoxysilane, 15 parts of orthosilicic acid and 10 parts of polyisocyanate.

[0046] A preparation method of an anti-aging coating, comprising the following steps:

[0047] 1) Mix 24 parts of epoxy resin, 18 parts of palm wax, 9 parts of polyvinyl butyral, 30 parts of ammonium aluminum sulfate, 8 parts of aluminum powder, 11 parts of sugarcane wax, 20 parts of nano-silver, 5 parts of cinnabar, pure acrylic acid 10 parts of the em...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-aging paint, prepared from the following materials in parts by weight: 22 to 24 parts of epoxy resin, 16 to 18 parts of palm wax, 3 to 9 parts of polyvinyl butyral, 26to 30 parts of ammonium aluminum sulfate, 4 to 8 parts of aluminum powder, 7 to 11 parts of sugar cane wax, 16 to 20 parts of nano silver, 3 to 5 parts of cinnabar, 8 to 10 parts of pure acrylic emulsion, 11 to 14 parts of cobalt soap, 13 to 18 parts of iso-nonanoic acid, 6 to 8 parts of aluminum phosphate, 5 to 10 parts of acrylic resin, 12 to 15 parts of mica, 16 to 20 parts of phytate, 4 to 8 parts of dodecyl carbon alcohol ester, 10 to 15 parts of alkoxysilane, 12 to 15 parts of orthosilicic acid and 8 to 10 parts of polyisocyanate. The anti-aging paint has an anti-aging effect, is long inservice life, high in viscosity and easy to dry.

Description

technical field [0001] The invention relates to a new material, in particular to an anti-aging coating and a preparation method thereof. Background technique [0002] Paint, traditionally called paint in China. The so-called paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, oil, or emulsion, with or without adding pigments, fillers, adding The corresponding additives are viscous liquids prepared with organic solvents or water. The relatively authoritative book "Painting Technology" in the Chinese coatings industry defines it as follows: "Painting is a material that can be coated on the surface of an object by different construction techniques to form a firm adhesion, a certain strength, and a continuous coating. Solid film. The film formed in this way is commonly called a coating film, also known as a paint film or a coating." [0003] Paint is what ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D133/04C09D133/00C09D129/14C09D7/61C09D7/63
CPCC09D163/00C08K2201/011C08L2205/02C08L2205/035C08L91/06C08L29/14C08L33/04C08L33/00C08K13/02C08K2003/0812C08K2003/0806C08K3/34C08K5/521
Inventor 肖启宝
Owner 惠州市绿孔雀科技股份有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com