Plant fiber foaming material and production method thereof
A plant fiber and foam material technology, applied in the chemical industry, can solve the problem of high production cost, achieve the effects of simple production process, low comprehensive production cost and excellent product performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] 1) Dry the collected wild hay grass and pulverize it with a pulverizer to make 1-2mm plant fiber powder;
[0031] 2) Take 40 parts of plant fiber foam, add 28 parts of sodium alkylbenzene sulfonate, 15 parts of gelatin, 15 parts of phenolic resin, and 2 parts of sodium bicarbonate in sequence, mix, stir, and mechanically foam for 30 minutes to make a foam;
[0032] 3) Add a certain amount of aluminum sulfate to the foam made by step 2), let it stand for 20 minutes to form, and form a blank;
[0033] 4) Put the raw material made in step 3) into a blast drying oven to dry for 60 minutes, and then the finished plant fiber foam is made, and the finished product is tested.
Embodiment 2
[0035] 1) Pulverize the bamboo sawdust with a pulverizer to make 1-2mm plant fiber powder;
[0036] 2) Take 50 parts of plant fiber fragments, add 28 parts of sodium alkane sulfate, 10 parts of silica gel, 10 parts of epoxy resin, and 2 parts of ammonium nitrite in sequence, mix, stir, and mechanically foam for 50 minutes to make a foam ;
[0037] 3) adding an appropriate amount of aluminum sulfate to the foam made in step 3), and standing for 30 minutes to form a blank;
[0038] 4) Put the raw material made in step 4) into a blast drying oven to dry for 60 minutes, and then the finished plant fiber foam is made, and the finished product is tested.
Embodiment 3
[0040] 1) The dried wheat straw is crushed into fiber fragments with a pulverizer to make 1-2mm plant fiber fragments;
[0041] 2) Take 45 parts of plant fiber powder, add 19 parts of alkylphenol polyoxyethylene ether, 20 parts of silica gel, 15 parts of epoxy resin, and 1 part of ammonium carbonate in sequence, mix, stir, and mechanically foam for 30 minutes to make a foam ;
[0042] 3) adding an appropriate amount of aluminum sulfate to the foam made in step 3), and standing for 30 minutes to form a blank;
[0043] 4) Put the blank made in step 4) into a blast drying oven to dry for 60 minutes to make a finished plant fiber foam, and test the finished product.
[0044] In the above examples, the pulverizers, mixers, and blast drying ovens used are small and medium-sized equipment commonly used in industrial experiments, wherein, the pulverizer model is DRB-0.5T, the mixer model is 50 gallons, and the blast drying oven model is: DHG-9076A.
[0045] After testing, the perfo...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More