ABS material and preparation method thereof

A technology of ABS material and ABS resin, which is applied in the field of ABS materials, can solve the problems of limiting the application of ABS materials, difficulty in balancing weather resistance and mechanical properties, etc., to improve light aging resistance, improve processing stability, improve weather resistance and mechanical properties performance effect

Inactive Publication Date: 2018-10-12
ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The weather resistance and mechanical properties of existing ABS materials are difficult to balance, which seriously limits the application of ABS materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The preparation method of the disclosed ABS material comprises the following steps:

[0043] Step (1) Weighing raw materials in proportion.

[0044] Step (2) Put the first ABS resin, the second ABS resin, the AES resin and the dispersant into the mixer in sequence and stir evenly to obtain a premix. The sequential mixing of the first ABS resin, the second ABS resin, the AES resin and the dispersant is beneficial to ensure the mixing uniformity of each raw material. The stirring time in step (2) can be 2min-10min. Further, the stirring time in step (2) may be 5min-7min.

[0045] Step (3) adding the remaining raw materials into the obtained premixed material and stirring evenly to obtain the mixed material. After the preparation of the premix, the preparation of the mixture can effectively avoid the problem of uneven mixing of powdery raw materials and other types of original materials, thereby ensuring the uniform mixing of each raw material, which is conducive to obt...

Embodiment 1

[0050] (1) In parts by weight, weigh 75 parts of the first ABS resin, 12.5 parts of the second ABS resin, 12.5 parts of AES resin, 0.2 part of hindered phenolic antioxidant 1010, 0.2 part of phosphite antioxidant 168 , 0.1 part of UV absorber UV-327, 0.1 part of UV absorber UV-P, 0.1 part of hindered amine light stabilizer UV-770, 0.3 part of lubricant EBS, 0.4 part of dispersant silicone oil;

[0051] (2) Put the first ABS resin, the second ABS resin, the AES resin and the dispersing agent into the mixer in sequence and stir for 5 minutes to obtain the premix;

[0052] (3) Add the rest of the raw materials into the premix and stir for 8 minutes to obtain a homogeneous mixture;

[0053] (4) Feed the obtained mixture into a twin-screw extruder, and obtain ABS material A1 through melting, extrusion, water cooling, air-drying, and cutting into pellets, wherein the temperature zone of the twin-screw extruder is set at 180° C., 190° C. °C, 200 °C, 210 °C, 220 °C, 230 °C, 230 °C, 2...

Embodiment 2

[0055] (1) In parts by weight, weigh 75 parts of the first ABS resin, 12.5 parts of the second ABS resin, 12.5 parts of AES resin, 0.2 part of hindered phenolic antioxidant 1010, 0.2 part of phosphite antioxidant 168 , 0.3 parts of UV absorber UV-327, 0.3 parts of UV absorber UV-P, 0.3 parts of hindered amine light stabilizer UV-770, 0.3 parts of lubricant EBS, 0.4 parts of dispersant silicone oil;

[0056] (2) Put the first ABS resin, the second ABS resin, the AES resin and the dispersing agent into the mixer in sequence and stir for 5 minutes to obtain the premix;

[0057] (3) adding the rest of the raw materials into the obtained premix and stirring for 8 minutes to obtain a homogeneous mixture;

[0058] (4) Feed the obtained mixture into a twin-screw extruder, and obtain weather-resistant ABS material A2 through melting, extrusion, water cooling, air-drying, and pelletizing, wherein the temperature zone of the twin-screw extruder is set at 180°C, 190°C, 200°C, 210°C, 220°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ABS material and a preparation method thereof. The ABS material is prepared from, by weight, 70-85 parts of first ABS resin, 5-15 parts of second ABS resin, 10-20 parts of AES resin, 0.2-0.6 part of hindered phenol antioxidant, 0.2-0.6 part of phosphite antioxidant, 0.1-1.0 part of ultraviolet light absorber, 0.1-0.8 part of hindered amine light stabilizer, 0.2-0.5 partof lubricating agent and 0.3-0.6 part of dispersing agent; the first ABS resin is synthesized ABS resin by using a continuous bulk method, and the second ABS resin is the synthesized ABS resin by using a emulsion polymerization method. By utilizing synergistic effects among all the components, the method improves the weather-proof performance and mechanical performance of the ABS material.

Description

technical field [0001] The invention relates to the field of ABS materials, more specifically, to an ABS material and a preparation method thereof. Background technique [0002] Acrylonitrile-butadiene-styrene copolymer (ABS) is a polymer material with excellent comprehensive properties, which can be used in different fields such as automobiles and home appliances. It is difficult to balance the weather resistance and mechanical properties of existing ABS materials, which severely limits the application of ABS materials. [0003] Therefore, how to improve the weather resistance and mechanical properties of ABS materials has become an urgent technical problem in this field. Contents of the invention [0004] An object of the present invention is to provide a new technical solution of ABS material with excellent weather resistance and good mechanical properties. [0005] According to a first aspect of the present invention, an ABS material is provided. [0006] ABS materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L51/04C08K5/134C08K5/526C08K5/3475C08K5/3435
CPCC08L55/02C08L2201/08C08L2205/025C08L2205/03C08L51/04C08K5/1345C08K5/526C08K5/3475C08K5/3435
Inventor 邓俊杰程健黄家奇
Owner ANHUI JIANGHUAI AUTOMOBILE GRP CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap