Relief brick and preparation method thereof

A technology of embossing and desulfurizing building gypsum, which is applied in the field of building materials, can solve problems such as accidents, and achieve the effects of reduced production costs, simple manufacturing process, good compressive strength and frost resistance

Inactive Publication Date: 2020-11-24
郑州天罡实业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is also the danger of accidents in the tailings pond, and once it happens, the consequences will be very serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Relief brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Relief bricks, including the following raw materials in parts by weight: 30 parts of iron tailings, 48 ​​parts of desulfurized building gypsum, 20 parts of fly ash, 2 parts of reinforcing agent, wherein the reinforcing agent includes water reducing agent, water repellent and Latex powder, wherein, the weight ratio of described water reducer, water-repellent agent and latex powder is 1:1:2.

[0027] The iron tailings are solid wastes discharged by iron ore enterprises after grinding iron ore and extracting fine iron powder.

[0028] The desulfurized building gypsum is solid waste produced by desulfurization in coal-fired enterprises, and it is calcined at low temperature and ground to make it into hemihydrate gypsum to obtain the desulfurized building gypsum.

[0029] The fly ash is fly ash produced by coal-burning enterprises.

[0030] The fly ash is primary ash or high calcium ash.

[0031] The preparation method of described relief brick, comprises the steps:

[00...

Embodiment 2

[0036] Relief bricks, including the following raw materials in parts by weight: 35 parts of iron tailings, 44 parts of desulfurized building gypsum, 20 parts of fly ash, and 1 part of reinforcing agent, wherein the reinforcing agent includes water reducing agent and water repellent and latex powder, wherein the weight ratio of the water reducer, water repellent and latex powder is 1:1:2.

[0037] The iron tailings are solid wastes discharged by iron ore enterprises after grinding iron ore and extracting fine iron powder.

[0038] The desulfurized building gypsum is solid waste produced by desulfurization in coal-fired enterprises, and it is calcined at low temperature and ground to make it into hemihydrate gypsum to obtain the desulfurized building gypsum.

[0039] The fly ash is fly ash produced by coal-burning enterprises.

[0040] The fly ash is primary ash or high calcium ash.

[0041] The preparation method of described relief brick, comprises the steps:

[0042] Step ...

Embodiment 3

[0046] Relief bricks, including the following raw materials in parts by weight: 25 parts of iron tailings, 48 ​​parts of desulfurized building gypsum, 25 parts of fly ash, 2 parts of reinforcing agent, wherein the reinforcing agent includes water reducing agent and water repellent and latex powder, wherein the weight ratio of the water reducer, water repellent and latex powder is 1:1:2.

[0047] The iron tailings are solid wastes discharged by iron ore enterprises after grinding iron ore and extracting fine iron powder.

[0048] The desulfurized building gypsum is solid waste produced by desulfurization in coal-fired enterprises, and it is calcined at low temperature and ground to make it into hemihydrate gypsum to obtain the desulfurized building gypsum.

[0049] The fly ash is fly ash produced by coal-burning enterprises.

[0050] The fly ash is primary ash or high calcium ash.

[0051] The preparation method of described relief brick, comprises the steps:

[0052] Step 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an embossed brick and a preparation method thereof, and belongs to the technical field of building materials. The embossed brick is prepared from the following raw materials in parts by weight: 25 to 35 parts of iron tailings, 45 to 49 parts of desulfurization building gypsum, 20 to 25 parts of fly ash, and 1 to 2 parts of reinforcing agent. The preparation method of the embossed brick comprises the following steps: respectively weighing the iron tailings, the desulfurization building gypsum and the fly ash for subsequent use according to the weight ratios; uniformly mixing the iron tailings, the desulfurization building gypsum and the fly ash and stirring by adding water until solid content is 65 to 75 percent; pouring the iron tailings, the desulfurization building gypsum and the fly ash into a mould to be molded; removing the mould after 1 hour; naturally curing a molded product for 3 days so as to obtain the embossed brick. The embossed brick and the preparation method thereof have the following advantages that the iron tailings are not needed to be graded, so that large-scale utilization of the iron tailings is possibly achieved; the preparation process is simple, burning and steaming are eliminated, so that the production cost is greatly reduced, and the produced embossed brick has the advantages of good compressive strength and freezing resistance.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a relief brick and a preparation method thereof. Background technique [0002] Relief bricks are carved from sintered blue bricks, which is labor-intensive and time-consuming, and the preparation cost is very high. The pouring rapid prototyping method proposed in this patent can greatly reduce the production cost of relief bricks. [0003] Iron tailings, fly ash and desulfurized gypsum are all blue-gray granular materials, which are good materials for making blue-gray relief bricks. After proper treatment, using these industrial wastes to make relief bricks is an effective way to recycle waste resources. . [0004] With the continuous development of the national economy, the scale of mineral resource development is increasing, and the output of tailings is also increasing. In order to manage these tailings well, it is necessary to carry out tailings proj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14
CPCC04B28/144C04B2201/50C04B18/08C04B18/142C04B2103/302C04B2103/65C04B24/26
Inventor 符勇张文博
Owner 郑州天罡实业有限公司