Preparation method of hydrogel material for bionic fishing baits

A technology of bionic fishing bait and hydrogel, applied in the direction of artificial fish bait, fishing, application, etc., can solve the problems of environmental protection, sustainable development, not causing fish, environmental pollution, etc., to improve the fishing rate , dehydration shrinkage, and the effect of improving crosslinking strength and toughness

Inactive Publication Date: 2018-11-13
界首市汇珠渔具有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to improve the success rate of fishing, more and more people are starting to use bionic fishing baits. Bionic fishing baits are generally made of materials such as plastic or rubber, while most of the artificial fishing baits sold on the market are made of a separate plastic shell and Composed of fishhooks, its shape is stiff and unrealistic, it does not emit light and has no food-attracting fragrance, so it cannot attract the attention of fish, and the fishing efficiency is low. Some bionic fishing baits contain phthalates, which pollute the environment. Does not meet the requirements of the era of environmental protection and sustainable development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of hydrogel material for bionic fishing baits
  • Preparation method of hydrogel material for bionic fishing baits

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for preparing a hydrogel material for bionic fishing bait, which is made by the following steps:

[0016] (1) Rinse 10 parts by weight of recovered fish scales with water to remove surface dirt and blood, then place them in 80 parts of dilute hydrochloric acid solution, boil for 10 minutes, take them out, rinse them twice with distilled water, dry them at 40°C, and use The ball mill grinds the fish scales into flakes with a diameter of 100 μm, puts them into the mixer, and sprays the shell powder and hydroxypropyl-β-cyclodextrin solution under the stirring of 300 rpm. The spraying time is 3 minutes. After the spraying is completed, the Stir at 500rpm for 10min and dry at 30°C;

[0017] (2) Mix 3 parts of tangerine peel, 2 parts of seaweed powder, 1 part of clove, and 3 parts of fennel powder in a dry mixer for 5 minutes, then transfer to distilled water 20 times its volume, boil for 30 minutes under magnetic stirring at 100 rpm, and filter to obtain Filtrate, ...

Embodiment 2

[0023] A method for preparing a hydrogel material for bionic fishing bait, which is made by the following steps:

[0024] (1) Rinse 12 parts by weight of recovered fish scales with water to remove surface dirt and blood, then place them in 110 parts of dilute hydrochloric acid solution, boil for 20 minutes, take them out, rinse them with distilled water for 3 times, dry them at 45°C, and use The ball mill grinds the fish scales into flakes with a diameter of 300 μm, puts them into the mixer, and sprays the shell powder and hydroxypropyl-β-cyclodextrin solution under the stirring of 350 rpm. The spraying time is 4 minutes. After the spraying is completed, the Stir at 700rpm for 15min, and dry at 35°C;

[0025] (2) Mix 4 parts of tangerine peel, 6 parts of laver powder, 2 parts of cloves, and 4 parts of fennel powder in a dry mixer for 7 minutes, then transfer to distilled water 25 times its volume, boil for 40 minutes under magnetic stirring at 150 rpm, and filter to obtain Fi...

Embodiment 3

[0031] A method for preparing a hydrogel material for bionic fishing bait, which is made by the following steps:

[0032] (1) Rinse 15 parts by weight of recovered fish scales with water to remove surface dirt and blood, then place them in 150 parts of dilute hydrochloric acid solution, boil for 30 minutes, take them out, rinse them with distilled water for 3 times, dry them at 50°C, and use The ball mill grinds the fish scales into flakes with a diameter of 500 μm, puts them into the mixer, and sprays the shell powder and hydroxypropyl-β-cyclodextrin solution under the stirring of 400 rpm. The spraying time is 5 minutes. After the spraying is completed, the Stir at 800rpm for 20min, and dry at 40°C;

[0033] (2) Mix 5 parts of tangerine peel, 8 parts of laver powder, 2 parts of cloves, and 4 parts of fennel powder in a dry mixer for 10 minutes, then transfer to distilled water 30 times its volume, boil for 60 minutes under magnetic stirring at 200 rpm, and filter to obtain F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a hydrogel material for bionic fishing baits. By interaction of fish scales, shell powder and hydroxypropyl-beta-cyclodextrin, shell powder with a characteristic of light reflection is adhered to scale surfaces to form duplex reflective substances which are applied to the fishing baits, on the one hand, fishes can be attracted by twinkling under sunlight irradiation to increase the fishing rate, and on the other hand, density and mechanical properties of the material can be enhanced by taking the substances as filler, the material can be quicklyimmersed in water and prevented from floating due to low density. The hydrogel material is applied to the field of the bionic fishing baits to make full use of water-absorption swelling characteristics of hydrogel. When the fishing baits are soaked in water during fishing, the bionic fishing baits quickly absorb water to swell due to excellent swelling characteristics of the hydrogel materials, surface smoothness and wet viscosity are realized, and high biofidelity is achieved. Further, due to the self-repair characteristics of hydrogel, recycling is realized, so that cost saving is realized.

Description

technical field [0001] The invention belongs to the technical field of fishing bait preparation, and in particular relates to a method for preparing a hydrogel material used for bionic fishing bait. Background technique [0002] In order to improve the success rate of fishing, more and more people are starting to use bionic fishing baits. Bionic fishing baits are generally made of materials such as plastic or rubber, while most of the artificial fishing baits sold on the market are made of a separate plastic shell and Composed of fishhooks, its shape is stiff and unrealistic, it does not emit light and has no food-attracting fragrance, so it cannot attract the attention of fish, and the fishing efficiency is low. Some bionic fishing baits contain phthalates, which pollute the environment. It does not meet the requirements of the era of environmental protection and sustainable development. Contents of the invention [0003] In view of the above problems, the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/075C08L33/02C08L89/00C08L5/16C08K3/26C08K5/00C08F120/02A01K85/01
CPCA01K85/01C08F120/02C08J3/075C08J2333/02C08J2489/00C08K5/00C08K2003/265
Inventor 朱银忠
Owner 界首市汇珠渔具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com