Vitrification agent and preparation method and application method thereof

A pottery and formula technology, applied in the direction of metal material coating process, etc., can solve problems such as a large number of phosphating slag, and achieve the effects of prolonging corrosion resistance time, low energy consumption, and simple raw materials

Inactive Publication Date: 2018-11-13
深圳市华世纪联合企业管理有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the pretreatment of iron and steel adopts phosphating treatment process. Although the phosphating process can meet the production requirements of pretreatment, phosphating will produce a large amount of phosphating slag, and the carcinogenic sodium nitrite will be used as a carcinogen during the production process. Phosphating Accelerator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A vitrifying agent, containing the following raw materials in weight percentage: 1% ammonium fluozirconate, 0.2% acetic acid, 0.5% citric acid, 0.5% vinyl silane, 0.1% sodium chloride, 0.2% ultrafine active zinc oxide, rare earth Accelerator 0.01%, the balance is water.

[0043] A kind of preparation method of preparing vitrifying agent as above, is characterized in that, comprises the following steps:

[0044] Step 1: Under normal temperature and pressure, add 2 / 3 of the water of the formula into the reaction vessel and stir slowly;

[0045] Step 2: While keeping stirring, slowly add ammonium fluorozirconate, acetic acid, citric acid, vinyl silane, sodium chloride, zinc oxide, ultrafine active zinc oxide, and rare earth accelerators to the reaction vessel in sequence;

[0046] Step 3: After the liquid stirring tool is continuously stirred for 0.5 h, the remaining water is added to adjust the density to 1.01 g / ml.

[0047] A kind of use method that is applied to vitri...

Embodiment 2

[0056] A vitrifying agent, containing the following raw materials in weight percentage: 5% ammonium fluozirconate, 1.5% acetic acid, 0.8% citric acid, 3% vinyl silane, 3% sodium chloride, 1% ultrafine active zinc oxide, rare earth Accelerator 0.1%, the balance is water.

[0057] A kind of preparation method of preparing above-mentioned potting agent, it is characterized in that, comprises the following steps:

[0058] Step 1: Under normal temperature and pressure, add 2 / 3 of the water of the formula into the reaction vessel and stir slowly;

[0059] Step 2: While keeping stirring, slowly add ammonium fluorozirconate, acetic acid, citric acid, vinyl silane, sodium chloride, zinc oxide, ultrafine active zinc oxide, and rare earth accelerators to the reaction vessel in sequence;

[0060] Step 3: After the liquid stirring tool was continuously stirred for 1.5 hours, the remaining water was added to adjust the density to 1.03 g / ml.

[0061] A kind of use method that is applied to...

Embodiment 3

[0070] A vitrification agent, containing the following raw materials in weight percentage: 3% ammonium fluozirconate, 0.8% acetic acid, 0.6% citric acid, 2.5% vinyl silane, 2.1% sodium chloride, 0.7% ultrafine active zinc oxide, rare earth Accelerator 0.08%, the balance is water.

[0071] A kind of preparation method of preparing above-mentioned potting agent, it is characterized in that, comprises the following steps:

[0072] Step 1: Under normal temperature and pressure, add 2 / 3 of the water of the formula into the reaction vessel and stir slowly;

[0073] Step 2: While maintaining stirring, slowly add formula quantities of ammonium fluorozirconate, acetic acid, citric acid, vinyl silane, sodium chloride, zinc oxide, ultrafine active zinc oxide, and rare earth accelerators to the reaction vessel in sequence;

[0074] Step 3: After the liquid stirring tool continues to stir for 1 hour, add the remaining water to adjust the density to 1.02g / ml.

[0075] A kind of use method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a vitrification agent and a preparation method and an application method thereof. The vitrification agent contains the following raw materials of, by weight, 1%-5% of ammonium fluorozirconate, 0.2-1.5% of acetic acid, 0.5-0.8% of citric acid, 0.5-3% of vinyl silane, 0.1-3% of sodium chloride, 0.2-1% of zinc oxide and the balance water. The preparation method of the vitrification agent mainly comprises the following steps of 1, under normal temperature and normal pressure, water which accounts for two thirds of a formula amount is added into a reaction container, and thewater is slowly and non-stopping stirred; 2, the ammonium fluorozirconate, the acetic acid, the citric acid, the vinyl silane, the sodium chloride and the zinc oxide are sequentially and slowly addedinto the reaction container according to the formula amount while the stirring is kept; and 3, after a liquid stirring tool is continuously stirred for a certain time, the residual water is added andthe density is adjusted until 1.01-1.03 g / ml. The application method of the vitrification agent mainly comprises the following steps of degreasing treatment, two water washing, surface treatment on the vitrification agent prepared by the method, washing with pure water, drying, spraying and solidifying.

Description

technical field [0001] The invention relates to the technical field of metal surface treatment, in particular to a ceramic agent and its preparation method and use method. Background technique [0002] Steel usually needs to be pre-treated before painting. The chemical pre-treatment method is usually to form a chemical conversion film on the surface of the steel. The conversion film must have a certain anti-corrosion ability to ensure that the parts do not return to rust before spraying. It can also increase the roughness of the surface of the part and enhance the bonding force between the coating and the substrate. [0003] At present, most of the pretreatment of iron and steel adopts phosphating treatment process. Although the phosphating process can meet the production requirements of pretreatment, phosphating will produce a large amount of phosphating slag, and the carcinogenic sodium nitrite will be used as a carcinogen during the production process. Phosphating accele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/34
CPCC23C22/34
Inventor 黄列霜
Owner 深圳市华世纪联合企业管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com