Method for producing sintered straight-through water-conveying water-permeable bricks by utilizing lithium tailings and steel slag tailings

A technology of lithium tailings and permeable bricks, which is applied in the field of solid waste utilization, can solve the problems of polluting the environment and occupying land, and achieve the effects of good water permeability, reducing occupation, and maintaining surface water circulation

Inactive Publication Date: 2018-11-16
唐山庄信科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These solid wastes not only occupy the land, but also pollute the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing sintered straight-through water-conveying water-permeable bricks by utilizing lithium tailings and steel slag tailings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method of using lithium tailings and steel slag tailings to produce sintered straight-through water delivery type permeable bricks, said method comprising the following steps:

[0029] (1) Homogenization treatment of lithium tailings and steel slag tailings: Firstly, homogenize lithium tailings and steel slag tailings respectively, and crush the steel slag tailings through a 10-mesh sieve after homogenization, and pass through a 20-mesh sieve after homogenizing the lithium tailings ;

[0030] (2) Ingredients: Put 52kg of lithium tailings, 15kg of steel slag tailings, 33kg of clay raw materials, and 42kg of water into a ball mill, mix and grind for 13 hours, and pass through an 80-mesh sieve to remove iron;

[0031] (3) Preparation of sintered straight-through water-transporting permeable bricks: Put the ingredients after iron removal into the mud pool, filter them into mud cakes, and then knead the mud. After kneading the mud, squeeze out the mud section. The mud sec...

Embodiment 2

[0034] A method of using lithium tailings and steel slag tailings to produce sintered straight-through water delivery type permeable bricks, said method comprising the following steps:

[0035] (1) Homogenization treatment of lithium tailings and steel slag tailings: Firstly, homogenize lithium tailings and steel slag tailings respectively, and crush the steel slag tailings through a 10-mesh sieve after homogenization, and pass through a 20-mesh sieve after homogenizing the lithium tailings ;

[0036] (2) Ingredients: Put 55kg of lithium tailings, 20kg of steel slag tailings, 35kg of clay raw materials, and 45kg of water into a ball mill, mix and grind for 12 hours, and pass through an 80-mesh sieve to remove iron;

[0037] (3) Preparation of sintered straight-through water-transporting permeable bricks: Put the ingredients after iron removal into the mud pool, filter them into mud cakes, and then knead the mud. After kneading the mud, squeeze out the mud section. The mud secti...

Embodiment 3

[0040] A method of using lithium tailings and steel slag tailings to produce sintered straight-through water delivery type permeable bricks, said method comprising the following steps:

[0041] (1) Homogenization treatment of lithium tailings and steel slag tailings: Firstly, homogenize lithium tailings and steel slag tailings respectively, and crush the steel slag tailings through a 10-mesh sieve after homogenization, and pass through a 20-mesh sieve after homogenizing the lithium tailings ;

[0042] (2) Ingredients: Put 57kg of lithium tailings, 22kg of steel slag tailings, 38kg of clay raw materials, and 47kg of water into a ball mill, mix and grind for 13 hours, and pass through an 80-mesh sieve to remove iron;

[0043] (3) Preparation of sintered straight-through water-transporting permeable bricks: Put the ingredients after iron removal into the mud pool, filter them into mud cakes, and then knead the mud. After kneading the mud, squeeze out the mud section with a moistu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Splitting tensile strengthaaaaaaaaaa
Water permeability coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing sintered straight-through water-conveying water-permeable bricks by utilizing lithium tailings and steel slag tailings. The method comprises the following steps: performing homogenization treatment on the lithium tailings and the steel slag tailings, putting the processed lithium tailings, the processed steel slag tailings, a clay raw material and water into a ball mill according to a certain ratio, performing mixing fine grinding, performing sieving to remove iron, putting the iron-removed material in a mud pool, performing filter pressing to form a mud cake, performing mud refining to extrude mud sections, performing extrusion molding on the mud sections to obtain wet green sintered water-permeable bricks with uniformly-distributed straight-through water-conveying holes of 5-10 mm, cutting the wet green bricks, putting the cut wet green bricks on supporting plates, sending the supporting plates to a tunnel kiln, and performing drying; and performing high-temperature sintering on dry green bricks according to a certain firing system at temperature of 1100-1200 DEG C in an energy-saving double-layer tunnel kiln to prepare the water-permeable bricks. The water-permeable bricks disclosed by the invention have a plurality of functions such as very good water permeability and hydrophobicity, no pollution, high strength, strong corrosion resistance, good freeze-thaw resistance, long service life, climate adjustment, elimination of an urban heat island effect, and maintaining of surface water circulation, and meet the requirements ofenergy conservation and emission reduction, environmental protection and development of low carbon economy in China.

Description

technical field [0001] The invention belongs to the technical field of solid waste utilization, and in particular relates to a method for producing sintered straight-through water delivery type permeable bricks by utilizing lithium tailings and steel slag tailings. Background technique [0002] With the rapid development of my country's economy, the continuous improvement of people's living standards and the large-scale construction of cities, most of the city's surface is covered by buildings, cement concrete, floor tiles, etc. These solid objects are not conducive to the infiltration of rainwater into the ground in time. Heavy rainstorms are prone to waterlogging, which brings great problems to the travel and traffic safety of urban people. This kind of situation generally occurs in cities all over the country every summer, and the painful lessons are vividly remembered. In addition, the currently used road square bricks are generally unfired cement sand bricks, which basi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/138C04B33/132C04B33/10C04B33/32
CPCC04B33/10C04B33/132C04B33/138C04B33/32C04B2201/50C04B2235/96Y02P40/60Y02A30/60
Inventor 吴冀
Owner 唐山庄信科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com