A method for preparing an anticorrosion antioxidation material

An anti-oxidation and corrosion-resistant technology, which is applied in the field of preparation of corrosion-resistant and anti-oxidation materials, can solve problems such as poor interface compatibility and affect the mechanical properties of composite materials, so as to improve the density, improve the uniformity of components, and improve the mechanical strength Effect

Inactive Publication Date: 2018-11-30
陶玲
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the high polarity of the surface of plant fibers makes the interfacial compatibility poor when mixed with non-polar polymers, which seriously affects the mechanical properties of composite materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for preparing a corrosion-resistant and anti-oxidation material, comprising the following steps:

[0019] 1) Add bamboo powder to 12 times NaOH solution with a concentration of 8.5wt%, soak it under stirring for 4 hours at room temperature, filter the product and wash it with water until neutral, and after drying, it is alkali-treated bamboo powder; 2) Alkali-treated Bamboo powder was added to 6 times of 95wt% ethanol solution containing 0.8wt% vinyltrimethoxysilane, stirred to disperse evenly, and the pH value was adjusted to 4.2 with hydrochloric acid, then stirred and reacted at 60°C for 4h, cooled and washed with distilled water 3) Add 0.5 parts by weight of stearic acid to 200 parts by weight of distilled water, stir and heat up to 66°C, add 48 parts by weight of alkali-treated bamboo powder after complete dissolution, and stir at constant temperature reacted for 30 minutes; the product was repeatedly washed with distilled water to remove unreacted modifie...

Embodiment 2

[0022] A method for preparing a corrosion-resistant and anti-oxidation material, specifically comprising the following steps:

[0023] 1) Add bamboo powder to 16 times the NaOH solution with a concentration of 9.5wt%. The NaOH solution also contains 0.49‰ cytisine. Stir and soak at room temperature for 6 hours. The product is suction filtered and washed with water until neutral. After drying at 100°C for 36 hours, it is ready for use, which is alkali-treated bamboo powder;

[0024] 2) Add the alkali-treated bamboo powder to 8 times the 95wt% ethanol solution containing 1.0wt% vinyltrimethoxysilane, stir to make it evenly dispersed, and adjust the pH value to 4.4 with hydrochloric acid, then stir and react at 80°C for 8h, After cooling, wash with distilled water until neutral, and dry at 100°C for 36 hours to obtain silane-modified bamboo powder;

[0025] 3) Add 0.7 parts by weight of stearic acid into 240 parts by weight of distilled water, stir and heat up to 76°C, add 62 pa...

Embodiment 3

[0030] A method for preparing a corrosion-resistant and anti-oxidation material, specifically comprising the following steps:

[0031] A: Add bamboo powder to 15 times the NaOH solution with a concentration of 9wt%, soak it at room temperature for 4 hours under stirring, filter the product and wash it with water until it is neutral, dry it at 96°C for 24 hours, and then use it as alkali-treated bamboo powder;

[0032] B: Add alkali-treated bamboo powder to 8 times of 95wt% ethanol solution containing 1wt% vinyltrimethoxysilane, stir to disperse evenly, and adjust the pH value to 4.2 with hydrochloric acid, then stir and react at 65°C for 5h, and cool Finally, wash with distilled water to neutrality, and dry to obtain silane-modified bamboo powder;

[0033] C: Add 0.7 parts by weight of stearic acid and 0.014 parts by weight of 3-bromocamphor-8-sulfonate ammonium salt to 220 parts by weight of distilled water, stir and heat up to 70°C, add 50 parts by weight of alkali-treated b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid resistanceaaaaaaaaaa
acid resistanceaaaaaaaaaa
acid resistanceaaaaaaaaaa
Login to View More

Abstract

A method for preparing an anticorrosion antioxidation material is disclosed. The method includes firstly adding bamboo powder into a NaOH solution containing cytosine; soaking and reacting the bamboopowder; then reacting the alkali-treated bamboo powder in an ethanol solution containing vinyltrimethoxysilane to obtain silane-modified bamboo powder; modifying and reacting alkali-treated bamboo powder in distilled water containing stearic acid and ammonium 3-bromocamphor-8-sulfonate to obtain bamboo powder modified with stearic acid; finally fully mixing the silane-modified bamboo powder, the bamboo powder modified with stearic acid, polypropylene powder and an antioxidant; and subjecting the mixture to melting and granulation to obtain the anticorrosion antioxidation material. Beneficial effects are that the method can effectively improve roughness of the surface and inside of bamboo powder, polarity of the bamboo powder is increased, the degree of crystallization of cellulose molecules is increased, mechanical meshing between the bamboo powder and a resin matrix is further improved, the density and uniformity of the composite material are improved, and mechanical strength and an antioxidation function of the material are improved.

Description

technical field [0001] The invention relates to the field of material preparation, in particular to a method for preparing a corrosion-resistant and anti-oxidation material. technical background [0002] Materials are those substances that humans use to make articles, devices, components, machines or other products. Materials are substances, but not all substances can be called materials. Such as fuels and chemical raw materials, industrial chemicals, food and pharmaceuticals are generally not considered materials. But this definition is not so strict. For example, explosives and solid rocket propellants are generally called "energetic materials" because they are part of artillery or rockets. Due to the variety, there is no unified standard for classification methods. From the perspective of physical and chemical properties, it can be divided into metal materials, inorganic non-metallic materials, organic polymer materials and composite materials composed of different typ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L97/02
CPCC08L23/12C08L2201/08C08L2205/025C08L2205/03C08L97/02
Inventor 陶玲
Owner 陶玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com