Nanometer composite-layer garment material

A nano-composite and clothing technology, applied in the field of clothing materials, can solve problems such as poor antibacterial ability and poor anti-ultraviolet ability, and achieve the effects of improving additional performance, increasing economic and social benefits, and enhancing self-cleaning performance.

Inactive Publication Date: 2018-12-07
揭阳市腾晟科技咨询有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to overcome the deficiencies in the prior art, the purpose of the present invention is to provide a nano-composite layer clothing material, which effectively makes up for the defects of the existing nano-composite layer clothing materials, such as poor antibacterial ability and poor anti-ultraviolet ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A nano-composite layer clothing material, the clothing material is composed of a garment outer layer front sheet, a nano-finishing layer and a garment inner layer:

[0027] Among them, the front panel of the outer layer of the garment is composed of a self-cleaning layer, an antibacterial layer, and an anti-ultraviolet layer;

[0028] Among them, the self-cleaning layer is made of nano-titanium dioxide, penetrating agent and softener;

[0029] The antibacterial layer is made of nano titanium dioxide, nano zinc oxide and hot melt adhesive;

[0030] The main components of the anti-ultraviolet layer are nano-iron oxide and nano-alumina;

[0031] Wherein, softening agent is polyether;

[0032] Among them, the finishing process of the nano-finishing layer is: adding nano-titanium dioxide to toluene solvent, using ultrasonic waves to disperse nano-titanium dioxide, drying the water to 11%, and evenly coating the surface of the fabric;

[0033] The inner layer of the garmen...

Embodiment 2

[0036] A nano-composite layer clothing material, the clothing material is composed of a garment outer layer front sheet, a nano-finishing layer and a garment inner layer:

[0037] Among them, the front panel of the outer layer of the garment is composed of a self-cleaning layer, an antibacterial layer, and an anti-ultraviolet layer;

[0038] Among them, the self-cleaning layer is made of nano-titanium dioxide, penetrating agent and softener;

[0039] The antibacterial layer is made of nano titanium dioxide, nano zinc oxide and hot melt adhesive;

[0040] The main components of the anti-ultraviolet layer are nano-iron oxide and nano-alumina;

[0041] Wherein, the softening agent is silicone;

[0042] Among them, the finishing process of the nano-finishing layer is: adding nano-titanium dioxide to toluene solvent, using ultrasonic waves to disperse nano-titanium dioxide, drying the water to 10%, and evenly coating the surface of the fabric;

[0043] The inner layer of the gar...

Embodiment 3

[0046] A nano-composite layer clothing material, the clothing material is composed of a garment outer layer front sheet, a nano-finishing layer and a garment inner layer:

[0047] Among them, the front panel of the outer layer of the garment is composed of a self-cleaning layer, an antibacterial layer, and an anti-ultraviolet layer;

[0048] Among them, the self-cleaning layer is made of nano-titanium dioxide, penetrating agent and softener;

[0049] The antibacterial layer is made of nano titanium dioxide, nano zinc oxide and hot melt adhesive;

[0050] The main components of the anti-ultraviolet layer are nano-iron oxide and nano-alumina;

[0051] Wherein, softening agent is polyamine;

[0052] Among them, the finishing process of the nano-finishing layer is: adding nano-titanium dioxide to toluene solvent, using ultrasonic waves to disperse nano-titanium dioxide, drying the water to 12%, and evenly coating the surface of the fabric;

[0053] The inner layer of the garmen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of garment materials, in particular to a nanometer composite-layer garment material. The garment material is composed of a garment outer-layer front piece,a nanometer after-finishing layer and a garment inner layer, wherein the garment outer-layer front piece is composed of a self-cleaning layer, an anti-bacterial layer and an anti-ultraviolet layer; the main components of the anti-ultraviolet layer include nanometer iron oxide and nanometer aluminum oxide. A finishing process of the nanometer after-finishing layer includes the steps of adding nanometer titanium dioxide into a methylbenzene solvent, adopting ultrasonic waves for dispersing the nanometer titanium dioxide, roasting the mixture to a certain degree, and uniformly coating the surface of a fabric with the mixture. The provided technical scheme effectively overcomes the defects that existing nanometer composite-layer garment materials are poor in antibacterial capability and anti-ultraviolet capability.

Description

technical field [0001] The invention relates to the technical field of clothing materials, in particular to a nanocomposite layer clothing material. Background technique [0002] Clothing material is the material used to make the surface layer of clothing. Mostly for textiles, fur, leather, artificial leather and so on. Among them, textile is the main material, which can be divided into weaving and knitting. Woven fabrics are interwoven with yarns as warp and weft, also known as woven fabrics. [0003] Composite fabric is a new type of material formed by bonding one or more layers of textile materials, non-woven materials and other functional materials. Suitable for making sofas, clothing and other textiles, it is an indispensable fabric for people's home life. [0004] Nano finishing clothing is a new type of functional clothing, which increases the added value of clothing and improves the profit margin of products. The market has more and more demands for a variety of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A41D31/02
CPCA41D2400/26A41D2400/36
Inventor 苏映惜陈晓如徐立志许文文
Owner 揭阳市腾晟科技咨询有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com