Ceramic filter element, preparation method and application thereof

A technology of ceramic filter elements and filter elements, which is applied in its preparation and in the field of ceramic filter elements, can solve the problems of ineffective removal of chromium heavy metal pollution, mixing of composite base materials, long standing time, and uneven strength of filter elements, etc., to eliminate tissue defects and perfect Pore ​​structure, the effect of high yield rate

Active Publication Date: 2018-12-07
BEYCLEAN ENVIRONMENTAL PROTECTION TECH
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantages of the above traditional preparation methods: (1) the addition of pore-forming agents affects the precision of ceramics; (2) the use of ball mills for grinding increases the process flow; The sintering time of the billet is long...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic filter element, preparation method and application thereof
  • Ceramic filter element, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] In this embodiment, a method for preparing a ceramic filter element is provided, and the method for preparing a ceramic filter element includes the following steps:

[0056] (1) 80 parts by weight of 200 mesh diatomite, 5 parts by weight of silver-loaded titanium dioxide, 5 parts by weight of titanium dioxide and 10 parts by weight of Na 2 O 3SiO 2 Mix under stirring for 10 minutes, and then carry out carbon dioxide air-curing molding under the conditions of carbon dioxide purity of 99% and blowing pressure of 0.5 MPa to obtain a green filter element;

[0057] (2) Divide the filter element green body obtained in step (1) into six sections for sintering according to the sintering temperature. In the first section, the sintering temperature is raised from 25°C to 110°C at a heating rate of 1°C / min, and kept for 2 hours. In the first stage, the sintering temperature is raised from 110°C to 350°C at a rate of 1°C / min, and held for 1 hour; in the third stage, the sinter...

Embodiment 2

[0059] (1) 70 parts by weight of 100 mesh diatomite, 10 parts by weight of silver-loaded titanium dioxide, 5 parts by weight of titanium dioxide and 15 parts by weight of Na 2 O SiO 2 Mix under stirring for 10 minutes, and then carry out carbon dioxide air-hardening method under the conditions of carbon dioxide purity of 90% and blowing pressure of 1 MPa to obtain a green filter element;

[0060] (2) Divide the filter element green body obtained in step (1) into six sections for sintering according to the sintering temperature. In the first section, the sintering temperature is raised from 25°C to 110°C at a heating rate of 5°C / min, and kept for 2 hours. In the first stage, the sintering temperature was raised from 110°C to 350°C at a rate of 5°C / min, and held for 2 hours; in the third stage, the sintering temperature was raised from 350°C to 780°C at a rate of 5°C / min, and held for 2 hours The first stage raises the sintering temperature from 780°C to 1100°C at a heati...

Embodiment 3

[0062] (1) 70 parts by weight of 200 mesh diatomite, 10 parts by weight of silver-loaded titanium dioxide, 5 parts by weight of titanium dioxide and 15 parts by weight of 3Na 2 O SiO 2 Mix under stirring for 10 minutes, and then carry out carbon dioxide air-curing molding under the conditions of carbon dioxide purity of 60% and blowing pressure of 0.1 MPa to obtain a green filter element;

[0063] (2) Divide the filter element green body obtained in step (1) into six sections for sintering according to the sintering temperature. In the first section, the sintering temperature is raised from 25°C to 110°C at a heating rate of 15°C / min, and kept for 2 hours. The first stage raises the sintering temperature from 110°C to 350°C at a heating rate of 15°C / min, and keeps it for 1 hour. The first stage raises the sintering temperature from 780°C to 1100°C at a heating rate of 15°C / min, and keeps it for 5 hours. The sintering temperature was lowered from 500°C to 80°C at a heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Meshaaaaaaaaaa
Login to view more

Abstract

The invention discloses a ceramic filter element, a preparation method and an application thereof. The preparation method comprises the following step: sintering a filter element blank, wherein in thesintering process, the sintering temperature is divided into 3-6 sections. The ceramic filter element has the advantages of high mechanical strength, good filter effect, free of heavy metal pollution, high yield, low cost and short process consumed time, 20-30% of time is shortened compared with that of a conventional process, and the ceramic filter element is suitable for water quality treatment.

Description

technical field [0001] The invention belongs to the field of water purification and relates to a ceramic filter element, its preparation method and application. Background technique [0002] Ceramic filter elements have unique functions such as acid and alkali resistance, high temperature resistance, and corrosion resistance, and are widely used in the field of water treatment. It has the following characteristics: light weight, high porosity, long service life, easy to clean and regenerate; with good condition and high filtration accuracy, it is an environmentally friendly water quality filter material. [0003] CN107158805A discloses a multifunctional composite ceramic filter element and a preparation method thereof. The ceramic powder, adhesive, organic pore-forming agent, etc. are evenly stirred, and the slurry is left to age for 24 hours, then grouted, demoulded, and dried. Carry out sintering at last, cool, obtain ceramic filter element; CN107089836A discloses a kind ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/14C04B35/622C04B35/626B01D39/20
CPCB01D39/2068C04B35/14C04B35/622C04B35/62605C04B2235/3232C04B2235/408C04B2235/6562C04B2235/6565C04B2235/6567C04B2235/661
Inventor 苏发兴李延涛苏志波陈柔羲苏清龙叶锦华
Owner BEYCLEAN ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap