Automobile polyurethane combination material and preparation method thereof

A technology of combining materials and polyurethane, applied in the field of polyurethane materials, can solve the problems of insufficient product elongation, irritating odor, easy shrinkage, etc., and achieve the effects of low volatility, improved product elongation, and increased open porosity.

Inactive Publication Date: 2018-12-07
长春峰泰汽车胶业有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polyurethane materials for automobiles generally have a pungent odor, and there are also defects such as easy shrinkage after demoulding, insufficient elongation of the product, and easy crystallization below 10 °C.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The preparation of embodiment 1 automobile polyurethane composite material

[0042] Add 32.5 parts by weight of the polyether polyol of 330N produced by Shanghai Gaoqiao Petrochemical Co., Ltd. into the reactor, and then add 10 parts by weight of the polymer polyol of 36 / 28 from Tianjin No. 3 Petrochemical Plant, 3 The ethylene glycol of weight part, the model that 0.5 weight part U.S. GE Toshiba Organic Silicon Company produces is the inspiration catalyst of A-1, the model that 0.1 weight part U.S. GE Toshiba Organic Silicon Company produces is the gel catalyst of A33, 0.08 part of Nanjing clock The model produced by Shan Chemical Co., Ltd. is KF-28 cell opener, 3 parts by weight of silicone oil, 1.6 parts by weight of triethanol and 3.5 parts by weight of water into the reactor, and finally add 32.5 parts by weight of Shanghai Gaoqiao Petrochemical Company The produced polyether polyol of model 330N and 22.09 parts by weight of modified MDI were stirred at room temper...

Embodiment 2

[0043] Embodiment 2 Preparation of Polyurethane Composite Materials for Automobiles

[0044] Add 35 parts by weight of the polyether polyol of 330G produced by Shanghai Gaoqiao Petrochemical Company to the reactor, and then add 15 parts by weight of Tianjin No. Parts of 1,4-butanediol, 1 part by weight of U.S. Air Products company brand name is BL-11 inspired catalyst, 0.2 parts by weight of stannous octoate, 0.12 parts of CO-108 developed by Shanghai Lanjing Polyurethane Special Materials Co., Ltd. Pore ​​agent, the silicone oil of 5 weight parts, the diethanol of 2.5 weight parts and the water of 5 weight parts are in the reactor, finally add the polyether polyol of 330G and 62.29 weight parts of the model that Shanghai Gaoqiao Petrochemical Company produces 35 weight parts The modified MDI was stirred at room temperature with a rotation speed of 65r / min, and glue was produced to obtain a polyurethane composite material for automobiles.

Embodiment 3

[0046] Add 40 parts by weight of the polyether polyol of 330G produced by Shanghai Gaoqiao Petrochemical Co., Ltd. into the reactor, and then add 25 parts by weight of polymer polyol of 36 / 28 from Tianjin No. 3 Petrochemical Plant, 8 The Diethylene Glycol of parts by weight, 1.5 parts by weight of U.S. Huntsmen company trade mark are the inspired catalyst of ZF-22, the dibutyltin dilaurate of 0.3 parts by weight, the model produced by Shanghai Heda Polymer Technology Co., Ltd. of 0.16 parts is CO - 1006-2 cell opening agent, 6 weight parts of silicone oil, 3.3 weight parts of diethyl alcohol and 8.6 weight parts of water into the reactor, and finally add 40 parts by weight of 330G polymer produced by Shanghai Gaoqiao Petrochemical Co. Ether polyol and 66.43 parts by weight of modified MDI were stirred at room temperature at a speed of 80 r / min, and glue was produced to obtain a polyurethane composite material for automobiles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an automobile polyurethane combination material and a preparation method thereof. The technical problems of an automobile polyurethane material, such as pungent smell and die shrinkage after demoulding are solved. The invention belongs to the technical field of polyurethane materials. The polyurethane combination material is prepared by the steps of mixing and stirring a component A and a component B according to the mass ratio of 100-110: 28-50, wherein the component A comprises polyether polyol, polypolyols, a chain extender, a heuristic catalyst, a gel catalyst, a cell opener, silicone oil, a cross-linking agent and water; and the component B is modified MDI. According to the automobile polyurethane combination material, elongation of the product is enhanced, cell opening rate is increased, and the product is basically odor-free. The preparation method of the automobile polyurethane combination material is simple to operate and is more energy-saving and environmentally-friendly because there is no need to heat the raw materials during the production process.

Description

technical field [0001] The invention relates to the technical field of polyurethane materials, in particular to a polyurethane composite material for automobiles and a preparation method thereof. Background technique [0002] Polyurethane material is the abbreviation of polyurethane, and its English name is polyurethane, which is a kind of polymer material. Polyurethane is an emerging organic polymer material, known as the "fifth largest plastic", and is widely used in many fields of the national economy because of its excellent performance. The product application fields involve light industry, chemical industry, electronics, textile, medical treatment, construction, building materials, automobile, national defense, aerospace, aviation, etc. In the automotive field, such as car roof, bumper, interior trim (steering wheel, instrument panel), etc. are widely used. However, the existing polyurethane materials for automobiles generally have a pungent odor, and also have defec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/48C08G18/40C08G18/32C08J9/08C08G101/00
CPCC08G18/3206C08G18/40C08G18/48C08G18/6674C08G18/7671C08G2110/0083
Inventor 刘冬梅冯俊山
Owner 长春峰泰汽车胶业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap