Preparation method of PVC pipe with high weather resistance

A PVC pipe material and weather-resistant technology, which is applied in the direction of tubular objects, applications, household appliances, etc., can solve the problems of poor weather resistance, achieve the effects of improving production efficiency and product qualification rate, prolonging oxidation induction time, and reducing manufacturing costs

Inactive Publication Date: 2018-12-07
胡建芳
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for preparing high weather-resistant PVC pipes. Through the improvement of the pipe formula, the inner and outer walls of the pipes produced by using SG-3 PVC raw materials are very smooth, and the original mechanical strength is maintained. It not only solves the problem of poor weather resistance in the process of pipeline use, but also significantly improves production efficiency and product qualification rate, and greatly reduces the manufacturing cost of products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of high weather resistance PVC pipe, comprising the following steps:

[0017] (1) High weather resistance PVC pipes include the following components: 100 parts of SG-3 type PVC, 20 parts of toluene isocyanate, 1 part of iron oxide powder with a particle size of 13nm, 2 parts of heat transfer agent, 3 parts of heat absorbing agent, and 2 parts of paraffin wax 1 part, 1 part of low-lead composite stabilizer, 2 parts of erucamide; weigh each component, and put each component into the mixer in turn, and mix them evenly at 80°C to obtain the mixture. The speed of the mixer is 300rpm;

[0018] (2) The mixture is extruded with a screw extruder. During the extrusion process, the screw temperature is 90°C, the barrel temperature is 190°C, and the mold temperature is 210°C; the screw speed is 20r / min;

[0019] (3) After the pipe is extruded, the pipe is cooled and shaped by the vacuum cooling and sizing method. The vacuum degree during cooling is -0.02MPaMPa...

Embodiment 2

[0021] A preparation method of high weather resistance PVC pipe, comprising the following steps:

[0022] (1) High weather resistance PVC pipes include the following components: 100 parts of SG-3 type PVC, 20-30 parts of toluene isocyanate, 1-5 parts of iron oxide powder with a particle size of 13-18nm, 2-3 parts of heat transfer agent, 3-6 parts of endothermic agent, 2-7 parts of paraffin wax, 1-3 parts of low-lead composite stabilizer, 2-6 parts of erucamide; weigh each component, and put each component into the mixer in turn, Mix evenly at 80-100°C to obtain a mixture, and the speed of the mixer is 300-400rpm;

[0023] (2) The mixture is extruded with a screw extruder. During the extrusion process, the screw temperature is 90-110°C, the barrel temperature is 190-210°C, the mold temperature is 210-240°C; the screw speed is 20~25r / min;

[0024] (3) After the pipe is extruded, use the vacuum cooling and sizing method to cool and shape the pipe. The vacuum degree during cool...

Embodiment 3

[0026] A preparation method of high weather resistance PVC pipe, comprising the following steps:

[0027] (1) High weather resistance PVC pipes include the following components: 100 parts of SG-3 type PVC, 30 parts of toluene isocyanate, 5 parts of iron oxide powder with a particle size of 118nm, 3 parts of heat transfer agent, 6 parts of heat absorbing agent, and 7 parts of paraffin wax 3 parts, 3 parts of low-lead composite stabilizer, 2-6 parts of erucamide; weigh each component, put each component into the mixer in turn, and mix them evenly at 100°C to obtain the mixture. The speed is 400rpm;

[0028] (2) The mixture is extruded with a screw extruder. During the extrusion process, the screw temperature is 110°C, the barrel temperature is 210°C, and the mold temperature is 240°C; the screw speed is 25r / min;

[0029] (3) After the pipe is extruded, the pipe is cooled and shaped by the vacuum cooling and sizing method. The vacuum degree during cooling is -0.04MPa, and the co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A preparation method of a PVC pipe with high weather resistance comprises the following steps: (1) the PVC pipe with the high weather resistance comprises the following components: 100 parts of SG-3 type PVC, 20-30 parts of toluene isocyanate, 1-5 parts of iron oxide powder, 2-3 parts of a heat transfer agent, 3-6 parts of a heat absorbent, 2-7 parts of paraffin, 1-3 parts of a low-lead compound stabilizer and 2-6 parts of erucyl amide; weighing the components, sequentially feeding all the components into a material mixing machine, uniformly mixing at 80-100 DEG C to obtain a mixture; (2) extruding and forming the mixture by using a screw extruder; (3) cooling and shaping the pipe through a vacuum cooling sizing method after the pipe is extruded. According to the method disclosed by the invention, by improving the formula of the pipe, the inner wall and the outer wall of the pipe produced by the SG-3 type PVC raw material are smooth and smooth, and on the premise that the original mechanical strength is kept, so that the problem that the weather resistance is poor in the using process of the pipeline is solved, the production efficiency and the product percent of pass are obviouslyimproved, and the manufacturing cost of products is greatly reduced.

Description

technical field [0001] The invention relates to a pipe extrusion molding method, in particular to a preparation method of a high weather-resistant PVC pipe. Background technique [0002] The Chinese invention patent with publication date of January 14, 2015 and publication number CN 104277353 A discloses a production method for PVC pipes: using ingredients and recycled materials to co-extrude PVC pipes, the ingredients include sequentially mixing components and The mass percentage of each component is: PVC resin 48-53%, light calcium carbonate 39-44%, stabilizer 1-3%, paraffin 0.5-2%, stearic acid 1-3%, CPE 3-5% and Titanium dioxide 0.5-2%; The recycled material is obtained by the following steps: chopping, using a shredder to chop the recycled PVC waste pipe to obtain recycled materials; PVC material removal; Grinding, using a grinder to grind the screened PVC material to obtain granular recycled material with a diameter of 2.7-3.3mm. The production method of PVC pipe mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/29C08K3/22C08K5/20B29D23/00
CPCC08L27/06B29D23/001C08K2003/2272C08K2201/011C08L2201/08C08L2203/18C08L91/06C08K13/02C08K5/29C08K3/22C08K5/20
Inventor 胡建芳
Owner 胡建芳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com