Caulking material for decoration

A joint filling material, quartz sand technology, applied in the direction of adhesive type, adhesive additives, non-polymer adhesive additives, etc., can solve problems such as joint problems that cannot be completely solved, and achieve strong adhesion, Easy construction and good compatibility

Inactive Publication Date: 2018-12-21
苏州铭晟通物资有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For a long time, people in the domestic decoration and decoration industry have adopted a variety of construction schemes to continuously manufacture various materials, such as adhesive mounting with bandages, nailing with copper tape or bonding with flexible flat bottom ash, and construction with epoxy resin synthetic materials. , all kinds of methods and means cannot completely solve the joint problem of various materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A sealing material for decoration, comprising diatomaceous earth, urea-formaldehyde resin, quartz sand, titanium dioxide, activated clay, additives and water, the components of which are in parts by weight:

[0024] 20 parts of diatomaceous earth;

[0025] 40 parts of urea-formaldehyde resin;

[0026] 20 parts of quartz sand;

[0027] 3 parts of titanium dioxide;

[0028] 10 parts of activated clay;

[0029] 8 parts of auxiliary agent;

[0030] 15 parts of water;

[0031] The auxiliary agent is defoamer and water retaining agent, and the weight ratio of defoamer and water retaining agent is 1:1;

[0032] The quartz sand is crushed into quartz powder and passed through a 4000-mesh sieve, and titanium dioxide is passed through a 5000-mesh sieve.

Embodiment 2

[0034] A sealing material for decoration, comprising diatomaceous earth, urea-formaldehyde resin, quartz sand, titanium dioxide, activated clay, additives and water, the components of which are in parts by weight:

[0035] 25 parts of diatomaceous earth;

[0036] 45 parts of urea-formaldehyde resin;

[0037] 23 parts of quartz sand;

[0038] 4 parts of titanium dioxide;

[0039] 15 parts of activated clay;

[0040] 12 parts of auxiliary agent;

[0041] 17 parts of water;

[0042] The auxiliary agent is defoamer and water retaining agent, and the weight ratio of defoamer and water retaining agent is 1:1;

[0043] The quartz sand is crushed into quartz powder and passed through a 4000-mesh sieve, and titanium dioxide is passed through a 5000-mesh sieve.

Embodiment 3

[0045] A sealing material for decoration, comprising diatomaceous earth, urea-formaldehyde resin, quartz sand, titanium dioxide, activated clay, additives and water, the components of which are in parts by weight:

[0046] 30 parts of diatomaceous earth;

[0047] 50 parts of urea-formaldehyde resin;

[0048] 25 parts of quartz sand;

[0049] 6 parts of titanium dioxide;

[0050] 20 parts of activated clay;

[0051] 16 parts of auxiliary agent;

[0052] 20 parts of water;

[0053] The auxiliary agent is defoamer and water retaining agent, and the weight ratio of defoamer and water retaining agent is 1:1;

[0054] The quartz sand is crushed into quartz powder and passed through a 4000-mesh sieve, and titanium dioxide is passed through a 5000-mesh sieve.

[0055] The beneficial effects of the invention are: simple construction, can be used after mixing with water, easy to fill and fill, no shrinkage, good compatibility with various materials, easy to dry, no yellowing, stro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a caulking material for decoration. The caulking material is prepared from diatomaceous earth, urea-formaldehyde resin, quartz sand, titanium dioxide, activated clay, additivesand water. The caulking material for decoration has the beneficial effects that the caulking material is simple and convenient in construction, can be used after being mixed with water and evenly stirred, is easy in full filling, does not shrink, and is good in solubility with various materials, easy to dry, non-yellowing, strong in adhesive property, explosion-proof, good in durability, healthyand environmentally-friendly.

Description

technical field [0001] The invention relates to a decoration material, in particular to a decoration sealing material. Background technique [0002] Building materials are a general term for materials used in civil engineering and construction engineering. It can be divided into structural materials, decorative materials and some special materials. Structural materials include wood, bamboo, stone, cement, concrete, metal, bricks, ceramics, glass, engineering plastics, composite materials, etc.; decorative materials include various coatings, paints, coatings, veneers, tiles of various colors, and special effects Glass, etc.; special materials refer to waterproof, moisture-proof, anti-corrosion, fire-proof, flame-retardant, sound insulation, heat insulation, heat preservation, sealing, etc. [0003] For a long time, people in the domestic decoration and decoration industry have adopted a variety of construction schemes to continuously manufacture various materials, such as a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/24C09J11/04
CPCC09J161/24C08K2003/2241C09J11/04C08K7/26C08K3/36C08K3/22C08K3/346
Inventor 周卫东
Owner 苏州铭晟通物资有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap