Surface pretreatment method for improving abrasion resistance of automobile brake pad

A technology for surface pretreatment and automobile brakes, applied in heat treatment furnaces, heat treatment equipment, furnaces, etc., can solve the problems of low mechanical properties of brake pads, increase the preparation process, affect the use effect, etc., and achieve good safety and chemical stability Strong resistance and prolonging the service life

Inactive Publication Date: 2019-01-11
NINGGUO FEIYING AUTO SPARE PARTS
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Brake pads are the most critical safety parts in the braking system of a car. The brake pads play a decisive role in the quality of all braking effects. Therefore, good brake pads are the protectors of people and cars. The heat insulation layer is made of Composed of heat transfer materials, the purpose is heat insulation. The friction block is composed of friction material and adhesive. When braking, it is squeezed on the brake disc or brake drum to generate friction, so as to achieve the purpose of vehicle deceleration and braking, but the mechanics of the brake pad Low performance will not only lead to poor braking effect, but also lead to serious wear and tear, greatly affecting its use effect; The cost of preparation will increase the preparation process, and there are few researches on the surface treatment of brake pads, which has led to the lack of breakthrough development in the field of brake pads.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The surface pretreatment method that present embodiment improves the wear resistance of automobile brake pads comprises the following steps:

[0025] S1. Heat-treat the brake pad blank obtained by molding, put the brake pad blank into an electric furnace to heat, the heating temperature is 450°C, and the heating time is 9h, cool the brake pad blank after heat treatment, and firstly heat it on a drilling machine Drilling and chamfering, and then moving to the grinding machine to remove flash and burrs, and get pre-treated brake pads;

[0026] S2. The brake pads pretreated in step S1 are subjected to frosting treatment and cleaning treatment. After cleaning, the brake pads are placed in an electric furnace, and the temperature is raised to 750°C once, and the holding time is 65min. After 41 minutes, cool down to room temperature at a rate of 40°C / min, then raise the temperature to 550°C three times, keep warm for 20 minutes, and air-cool to room temperature with the furna...

Embodiment 2

[0032] The surface pretreatment method that present embodiment improves the wear resistance of automobile brake pads comprises the following steps:

[0033] S1. Heat-treat the brake pad blank obtained by molding, put the brake pad blank into an electric furnace to heat, the heating temperature is 490°C, and the heating time is 10h, cool the brake pad blank after heat treatment, and firstly heat it on a drilling machine Drilling and chamfering, and then moving to the grinding machine to remove flash and burrs, and get pre-treated brake pads;

[0034] S2. The brake pads pretreated in step S1 are subjected to frosting treatment and cleaning treatment. After the cleaning treatment, the brake pads are placed in an electric furnace, and the temperature is raised to 850° C. for 70 minutes, and then the temperature is raised to 1010° C. for the second time. After 45 minutes, cool down to room temperature at a rate of 40°C / min, then raise the temperature to 570°C three times, keep warm...

Embodiment 3

[0040] The surface pretreatment method that present embodiment improves the wear resistance of automobile brake pads comprises the following steps:

[0041] S1. Heat-treat the brake pad blank obtained by molding, put the brake pad blank into an electric furnace to heat, the heating temperature is 470°C, and the heating time is 9.5h. Cool the brake pad blank after heat treatment, and first place it on a drilling machine. Carry out drilling and chamfering treatment, and then move to the grinding machine to remove flash and burrs, and obtain pre-treated brake pads;

[0042] S2. The brake pads pretreated in step S1 are subjected to frosting treatment and cleaning treatment. After the cleaning treatment, the brake pads are placed in an electric furnace, and the temperature is raised to 800° C. for 68 minutes, and then the temperature is raised to 995° C. for the second time. After 43 minutes, cool down to room temperature at a rate of 40°C / min, then raise the temperature to 560°C t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a surface pretreatment method for improving the abrasion resistance of an automobile brake pad and relates to the technical field of processing and treatment of brake pads. Thesurface pretreatment method for improving the abrasion resistance of the automobile brake pad comprises the processes that a brake pad blank is subjected to heat treatment and cutting machining and then subjected to sanding treatment, cleaning treatment, carbon and nitrogen infiltration treatment, sand blasting treatment, secondary cleaning treatment and the like; and finally, a layer of treatmentliquid is smeared, and gluing is conducted after drying. After a series of treatment, the internal stress of the brake pad can be effectively lowered, the surface hardness of the brake pad can be improved, the brake pad has the quite high abrasion resistance, corrosion resistance, thermal fatigue resistance and adhesion prevention, and the service life of the brake pad is greatly prolonged.

Description

technical field [0001] The invention relates to the technical field of brake pad processing, in particular to a surface pretreatment method for improving the wear resistance of automobile brake pads. Background technique [0002] With the rapid development of the automobile industry, automobile users have higher and higher requirements for braking safety performance. The common brake pads on the market are mostly asbestos products. In the case of emergency braking, the friction coefficient will drop sharply, resulting in a decline in power torque Seriously, it affects the safety of driving, and asbestos material will produce a lot of dust under the action of high temperature wear, which has carcinogenic effect. Excellent friction plate materials should have good friction coefficient and wear resistance, high elastic modulus, sufficient mechanical strength, high heat resistance, high thermal conductivity and heat capacity, in order to ensure that the service life meets the de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C8/30C21D9/00
CPCC21D9/0068C23C8/30
Inventor 孙奇春
Owner NINGGUO FEIYING AUTO SPARE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products