Water-based coating using shell powder and preparation method thereof

A technology of water-based paint and shell powder, applied in the direction of fireproof paint, coating, etc., can solve the problems of short service life, breeding bacteria, mildew on the wall, etc., and achieve the effect of high wear resistance, good adhesion, and strong hardness

Inactive Publication Date: 2019-02-12
高卓彤
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the water-based paints or latex paints on the market are not breathable. Spraying or smearing on the wall surface will cause mildew on the wall surface and breed bacteria; although the content of harmful substances is below the national standard, there are still a lot of harmful substances in it. substances; and there are many problems such as short service life, easy wear and tear, not environmental protection, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The technical solution adopted in the present invention is: a water-based coating made of shell powder, which is prepared from the following raw materials: 8% diatomite; 50% shell powder; 6% calcium powder; 5% kaolin; %; Thickener 1.2%; Emulsion 12%; Humidity Conditioning Agent 1.3%; Leveling Agent 1.8% and Deionized Water 36%.

[0029] The preparation method comprises the following steps:

[0030] (1) First mix diatomite, shell powder, calcium powder and kaolin evenly, pour 30% of the total amount of deionized water, and mix evenly to form a base material to be mixed;

[0031] (2) Add defoamer, thickener, humidity conditioner and leveling agent to the base material to be mixed obtained in step (1), and other raw materials except deionized water, stir for 20 minutes, and then add the remaining deionized Ionized water, mixed evenly to form a mixture;

[0032] (3) Grind and filter the mixture obtained in step (2), and stir again until the mixture is evenly mixed to obta...

Embodiment 2

[0034] The technical solution adopted in the present invention is: a water-based coating made of shell powder, which is prepared from the following raw materials: 5% diatomite; 55% shell powder; 8% nano-scale calcium powder; 8% kaolin; defoaming Thickener 0.5%; thickener 1.5%; styrene-acrylic emulsion 10%; humidity conditioner 1.5%; leveling agent 1.5%; %.

[0035] The preparation method comprises the following steps:

[0036] (1) First mix diatomite, shell powder, calcium powder and kaolin evenly, pour into a high-speed disperser, then pour 30% of the total deionized water, first stir at 800 rpm for 10 minutes at a low speed, and then Stir at 1000 rpm at high speed for 10 minutes, mix evenly, and form the base material to be mixed;

[0037] (2) Add defoamer, thickener, humidity conditioner and leveling agent to the base material to be mixed obtained in step (1), and other raw materials except deionized water, first stir at a low speed of 500 rpm for 12 Minutes, then stirre...

Embodiment 3

[0040] The technical solution adopted in the present invention is: a water-based coating made of shell powder, which is prepared from the following raw materials: 10% diatomite; 40% shell powder; 5% nano-scale calcium powder; 3% kaolin; defoaming Thickener 1%; Thickener 1%; Styrene Acrylic Emulsion 15%; Humidity Conditioning Agent 1%; Leveling Agent 2%; %.

[0041] The preparation method comprises the following steps:

[0042] (1) First mix diatomite, shell powder, calcium powder and kaolin evenly, pour into a high-speed disperser, then pour 30% of the total amount of deionized water, first stir at a low speed of 500 rpm for 10 minutes, and then accelerate Stir at a high speed of 1500 rpm for 10 minutes, mix evenly, and form the base material to be mixed;

[0043] (2) Add defoamer, thickener, humidity conditioner and leveling agent to the base material to be mixed obtained in step (1), and other raw materials except deionized water, first stir at 800 rpm at a low speed for 8...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based coating using shell powder and a preparation method thereof. The water-based coating is prepared by the following steps of using the shell powder as the main rawmaterial, adding diatomite, calcium powder, kaolin and other additives, and mixing, so as to form the water-based coating using the shell powder. The water-based coating using the shell powder has the beneficial effects that the air ventilating property is good, the mildew-proof effect is realized, the poisonous substances are decomposed and adsorbed, and the air humidity is regulated; the environment-friendly effect is better, all adopted raw materials are substances containing no grease or benzene ring, and the finished product is free from toxicity or odor; the abrasion-resistant propertyis high, and the flame-retardant function is realized; the construction property is good, the construction method is flexible, and the water-based coating can be sprayed or coated.

Description

technical field [0001] The invention belongs to paint preparation technology, in particular to a water-based paint made from shell powder and a preparation method thereof. Background technique [0002] Any paint that uses water as a solvent or as a dispersion medium can be called a water-based paint. Water-based coatings are divided into two categories: natural water-based coatings of natural substances or minerals and synthetic resin water-based coatings. Water-based coatings of artificial synthetic resins include water-soluble coatings, water-dilutable coatings and water-dispersible coatings. Water-soluble coatings use water-soluble resins as film-forming materials, represented by polyvinyl alcohol and its various modified products, in addition to water-soluble alkyd resins, water-soluble epoxy resins, and inorganic polymer water-based resins. [0003] At present, most of the water-based paints or latex paints on the market are not breathable. Spraying or smearing on the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/18C09D7/61
CPCC08K2003/265C08K2201/014C09D5/18C09D7/61C09D125/14C08K3/34C08K3/26C08K3/346
Inventor 高卓彤
Owner 高卓彤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com