A kind of graphene coated aluminum composite coating and its preparation method and application

A graphene-coated, aluminum-composite technology, applied in transportation and packaging, metal processing equipment, pressure inorganic powder coating, etc., can solve problems such as accelerated corrosion of magnesium alloy substrates, achieve high structural compactness, avoid pipe plugging, good compactness

Active Publication Date: 2021-02-12
GUANGDONG UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cold-sprayed aluminum-based coatings on magnesium alloys have attracted the most attention because of their low cost and good protective effect. However, due to the strong activity of magnesium alloys, it is necessary to have a high density of the coating structure, otherwise the slight coating Defects are also likely to cause accelerated corrosion of the magnesium alloy matrix

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene coated aluminum composite coating and its preparation method and application
  • A kind of graphene coated aluminum composite coating and its preparation method and application
  • A kind of graphene coated aluminum composite coating and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Coating of aluminum powder: weigh 0.02g graphene oxide, put into 100mL deionized water and disperse to a clear and transparent solution, and obtain a graphene oxide aqueous solution with a concentration of 0.2g / L; weigh 20g aluminum powder (10 ~40μm) into the dispersed graphene oxide aqueous solution with a concentration of 0.2g / L and magnetically stirred. After reacting for 300s, filter off the excess water and wash the above-mentioned graphene-coated powder with alcohol and filter again. Bake it down for 18 hours to obtain a graphene-coated aluminum powder with a graphene mass fraction of 0.1 wt%.

[0033] 2. Surface roughening of the substrate: use YT-9060 sandblasting machine to sandblast the surface of the magnesium alloy. After sanding and sanding, the surface roughness is 5-10Ra.

[0034] 3. Surface cleaning: Put the substrate treated in step 2 into alcohol and ultrasonically clean it for 20 minutes to remove oil and impurities, and dry it for later use.

[...

Embodiment 2

[0044] The aluminum powder coating process and the coating preparation steps are the same as in Example 1, the difference being that the graphene oxide weighed is 0.03g, the concentration of the graphene oxide aqueous solution is 0.3g / L, and the graphene mass fraction obtained is 0.15 Wt% graphene-coated aluminum powder; the reaction time of aluminum powder in the solution is 400s; the blasting gas pressure is 0.6MPa, the blasting angle is 85°, or polished with 200 mesh sandpaper; cold spraying process parameters: working pressure is 0.8Mpa, the gas temperature is 400°C, the moving speed of the nozzle relative to the sample is 100mm / min, the distance between the bottom of the nozzle and the surface of the sample is 20mm, and the powder feeding rate is 0.2g / s.

Embodiment 3

[0046] The aluminum powder coating process and the coating preparation steps are the same as in Example 1, the difference is that the weighed graphene oxide amount is 0.04g, the concentration of the graphene oxide aqueous solution is 0.4g / L, and the obtained graphene mass fraction is 0.2 Wt% graphene-coated aluminum powder; the reaction time of aluminum powder in the solution is 450s; the blasting gas pressure is 0.65MPa, the blasting angle is 80°, or polished with 400 mesh sandpaper; cold spraying process parameters: working pressure is 0.65Mpa, the gas temperature is 450°C, the moving speed of the nozzle relative to the sample is 200mm / min, the distance between the bottom of the nozzle and the surface of the sample is 10mm, and the powder feeding rate is 0.4g / s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of metal surface treatment, and discloses a graphene-coated aluminum composite coating, a preparation method and application thereof. The method is to put the aluminum powder into the graphene oxide aqueous solution, stir and react, and dry to obtain the graphene-coated aluminum powder; use mechanical treatment to make roughness on the metal surface, and dry it after cleaning to obtain a rough metal surface; Cold spraying equipment, put graphene-coated aluminum powder into the designated powder supply cylinder; install the metal surface with roughness on a specific fixture, set the cold spraying process parameters, start the spraying device to deposit the synthesized graphene-coated aluminum powder On a metal surface with roughness, a graphene-coated aluminum powder coating is prepared. After the method is coated, the surface hardness of the aluminum powder is improved and the fluidity is better, the phenomenon of pipe blocking during spraying is avoided, and the spraying efficiency is improved. The graphene-coated aluminum composite coating has a high structure density, can efficiently isolate corrosive ions, exhibits stronger corrosion resistance, and can be applied in the field of anti-corrosion.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and more specifically relates to a graphene-coated aluminum composite coating, a preparation method and application thereof. Background technique [0002] Magnesium alloys have broad application prospects in the fields of automobiles, electronic communications, aerospace, and biomedicine due to their high specific strength, excellent cutting processing, casting properties, and biocompatibility. The resulting poor corrosion resistance severely limits its application. Surface coating protection is the most commonly used and efficient protection method for magnesium alloys, mainly including: electroplating, vapor deposition, thermal spraying, plasma spraying and organic coating, etc. These methods have pollution, complicated process, many coating defects or insufficient protection effect And other issues. Low-pressure cold spraying is a new method of preparing protective coatings d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C24/04B22F1/02
CPCC23C24/04B22F1/16
Inventor 张留艳王秀金揭晓华麦永津
Owner GUANGDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap