Anti-seepage recycled concrete and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of recycled concrete and recycled coarse aggregate, which is applied in the field of building materials, can solve the problems of high porosity and poor impermeability, and achieve the effects of reducing porosity, enhancing strength and reducing porosity
Active Publication Date: 2019-03-12
曙光装配式建筑科技(浙江)有限公司
View PDF7 Cites 18 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Compared with the natural aggregate, the recycled coarse aggregate in the above-mentioned patent is covered with hardened cement slurry on the surface of the recycled coarse aggregate, so the total content of new and old cement mortar in recycled concrete is higher than that of ordinary concrete, so its porosity is higher than that of natural concrete , poor impermeability
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0046] Embodiment 1: a kind of impermeable recycled concrete, its raw material comprises the component of following parts by weight:
[0047] 75 parts of ordinary Portland cement;
[0048] 60 parts of natural fine aggregate;
[0049] 90 parts of modified recycled coarse aggregate;
[0050] 8 parts of fly ash;
[0051] 1 part of polycarboxylate superplasticizer;
[0052] 8 parts of sodium gluconate;
[0053] 5 parts of carbon nanofiber;
[0054] 35 parts of water;
[0055] The preparation method of modified recycled coarse aggregate is as follows:
[0056] (1) breaking the discarded concrete into aggregates of 5-40 mm, then washing the broken aggregates with water, and drying naturally to obtain dry aggregates, the moisture content of which is 2.5%;
[0057] (2) Mix penetrant, nano-titanium dioxide and water uniformly to form a modified liquid. The parts by weight of penetrant, nano-titanium dioxide and water are 10 parts, 1 part and 90 parts respectively, and the penetr...
Embodiment 2
[0064] Embodiment 2: An anti-permeability recycled concrete, the difference from Embodiment 1 is that the moisture content of the dry aggregate is 2%.
Embodiment 3
[0065] Embodiment 3: An anti-permeability recycled concrete, the difference from Embodiment 1 is that the moisture content of the dry aggregate is 1.5%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an anti-seepage recycled concrete and a preparation method thereof, and relates to the technical field of building materials. The anti-seepage recycled concrete is prepared from the following raw materials in parts by weight: 75 to 85 parts of ordinary Portland cement, 50 to 60 parts of natural fine aggregate, 90 to 100 parts of modified recycled coarse aggregate, 8 to 10 parts of fly ash, 1 to 2 parts of polycarboxylate water reduction agent, 8 to 12 parts of sodium gluconate, 5 to 6 parts of nanometer carbon fiber, and 35 to 45 parts of water. The preparation method of the modified recycled coarse aggregate comprises the following steps of (1) crushing the waste concrete into the aggregate with size of 5 to 40 mm, cleaning the crushed aggregate by water, and naturally airing, so as to obtain the dried aggregate; (2) uniformly mixing a penetrant, nanometer titanium dioxide and water to form a modifying liquid, feeding the dried aggregate into the modifying liquid, and uniformly stirring and mixing, so as to obtain a suspension liquid; (3) putting the suspension liquid into a sealed container, leading carbon dioxide gas into the suspension liquid, filtering,and airing the aggregate, so as to obtain the modified recycled coarse aggregate. The anti-seepage recycled concrete has the advantage of good anti-seepage property.
Description
technical field [0001] The invention relates to the technical field of building materials, more specifically, it relates to an impermeable recycled concrete and a preparation method thereof. Background technique [0002] With the rapid development of the construction industry, the pace of urbanization is getting faster and faster, and at the same time, there are more and more old city renovation projects, which have resulted in a large amount of abandoned construction waste. Most of the construction waste in our country has not been recycled in a scientific way. The vast majority of construction waste is disposed of as garbage, randomly piled in the open air, or disposed of in a simple landfill. [0003] A Chinese invention patent with publication number CN107010896A discloses a recycled concrete mixed with chopped basalt fiber and recycled coarse aggregate, which is characterized in that: it is made of the following raw materials by weight: 100-300 parts of water, ordinary...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more