Waterborne fireproof coating material and preparation method and device thereof

A fire retardant coating and water-based technology, applied in the field of coatings, can solve the problems of insufficient convective tumbling, insufficient dispersion effect, and insufficient shearing effect, and achieve the effect of good shearing effect, excellent dispersion effect, and improving excellent characteristics.

Inactive Publication Date: 2019-03-12
FUJIAN MINHUA WATERPROOF MATERIAL ENG
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the dispersing process of this disperser, the shearing effect is not good enough and the efficiency of material tumbling up and down is not good enough, which leads to the dispersing effect is not good enough, and the convective tumbling is not uniform enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne fireproof coating material and preparation method and device thereof
  • Waterborne fireproof coating material and preparation method and device thereof
  • Waterborne fireproof coating material and preparation method and device thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]A new water-based fireproof coating, comprising the following components in parts by weight: 65 parts of acrylic water-based emulsion, 12 parts of organic solvent, 7 parts of wax emulsion, 10 parts of auxiliary agent, 0.5 part of graphene oxide, 3 parts of dispersant, 8 parts of filler, 3 parts of silicone resin, 160 parts of water, 20 parts of titanium dioxide.

[0035] The organic solvent is one or more of ethanol monobutyl ether, cyclohexanone, and isophorone. The solvent described in this example is formed by mixing ethanol monobutyl ether and isophorone, and the ethanol monobutyl ether and isophorone are mixed at a volume ratio of 5:2.

[0036] The filler includes nano-montmorillonite, glass powder and barium sulfate. The weight mixing ratio of montmorillonite, glass powder and barium sulfate described in this embodiment is 5:2:2.

[0037] The auxiliary agent includes a leveling agent, a water-based defoamer, and a matting agent. Among them, 2 parts of leveling a...

Embodiment 2

[0050] A new water-based fireproof coating, comprising the following components by weight: 75 parts of acrylic water-based emulsion, 8 parts of organic solvent, 5 parts of wax emulsion, 12 parts of auxiliary agent, 1 part of graphene oxide, 5 parts of dispersant, 11 parts of filler, 2 parts of silicone resin, 120 parts of water, 16 parts of titanium dioxide.

[0051] The organic solvent is one or more of ethanol monobutyl ether, cyclohexanone, and isophorone. The solvent described in the present invention is formed by mixing ethanol monobutyl ether and isophorone, and the alcohol monobutyl ether and isophorone are mixed according to a volume ratio of 8:1.

[0052] The filler includes nano-montmorillonite, glass powder and barium sulfate. The weight mixing ratio of montmorillonite, glass powder and barium sulfate in the present invention is 2:3:1.

[0053] The montmorillonite is nanoscale montmorillonite.

[0054] The additives include leveling agent, water-based defoamer, m...

Embodiment 3

[0060] A new water-based fireproof coating, comprising the following components by weight: 70 parts of acrylic water-based emulsion, 15 parts of organic solvent, 3 parts of wax emulsion, 8 parts of additives, 0.8 parts of graphene oxide, 13 parts of filler, 4 parts of silicone resin , 200 parts of water, 5 parts of dispersant, 25 parts of titanium dioxide.

[0061] The organic solvent is one or more of ethanol monobutyl ether, cyclohexanone, and isophorone. The solvent described in this example is formed by mixing ethanol monobutyl ether and isophorone, and the ethanol monobutyl ether and isophorone are mixed according to a volume ratio of 13:5.

[0062] The filler includes nano-montmorillonite, glass powder and barium sulfate. In this embodiment, the weight mixing ratio of the montmorillonite, glass powder and barium sulfate is 7:5:3.

[0063] The montmorillonite is nanoscale montmorillonite.

[0064] The glass powder is spherical fine powder.

[0065] The additives inclu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne fireproof coating material and a preparation method and a device thereof. The waterborne fireproof coating material comprises the following components in parts byweight: 65-75 parts of acrylic waterborne emulsions, 8-15 parts of organic solvents, 3-7 parts of wax emulsions, 8-12 parts of auxiliaries, 0.5-1 part of graphene oxide, 8-13 parts of fillers, 2-4 parts of organic silicon resins, 3-5 parts of dispersants, 120-200 parts of water and 16-25 parts of titanium dioxide. According to the waterborne fireproof coating material, additives with adverse effects on human body and environment such as a feeling agent, a flatting agent, an anti-scratch agent and a dispersant can be greatly reduced or saved, the excellent quality of the produced coating material is improved, and stable existence of other components in a filler mesh combining montmorillonite, glass powder and barium sulfate is guaranteed; the graphene oxide strengthens uniformity and stability of the filler mesh, so that the produced waterborne fireproof coating material can be more stable, more excellent in performance and more stable in overall performance; and meanwhile, the preparation method of the waterborne fireproof coating material is simple, a dispersing plate of a dispersion machine can efficiently and uniformly blend the slurry material, the shearing effect is good, andthe dispersing effect is excellent.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based fireproof coating and a preparation method and equipment thereof. Background technique [0002] Fire retardant coating is to brush the paint on the surface of those flammable materials, which can improve the fire resistance of the material, slow down the speed of flame spread, or prevent burning within a certain period of time. This type of coating is called fire retardant coating, or flame retardant coating. [0003] Fireproof coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. Applied on the surface of flammable substrates to change the combustion characteristics of the material surface and retard the rapid spread of fire; or applied to building components to improve the fire...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/18C09D5/08C09D7/61B01F7/26B01F15/00B01F27/93
CPCC09D133/00C09D5/08C09D5/18C09D7/61C08L2201/02C08K2201/011C08K2003/3045B01F27/93B01F35/42B01F2101/30
Inventor 余学晖周骏宇
Owner FUJIAN MINHUA WATERPROOF MATERIAL ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com