Preparation method of heat-resistant plastic product

A plastic product and heat-resistant technology, applied in the field of plastics, can solve problems such as unsatisfactory use requirements, heat resistance, poor mechanical properties and aging resistance, and achieve performance improvement, good compatibility, impact strength and thermal stability Improved effect

Inactive Publication Date: 2019-03-19
安庆市航海印务有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current plastic materials have poor heat resistance, mechanical properties, and aging resistance, which cannot meet the requirements of people's life and industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing a heat-resistant plastic product, comprising the steps of:

[0018] S1. Weigh each raw material according to parts by weight: 70 parts of perchlorethylene resin, 40 parts of polystyrene, 6 parts of nano-zinc oxide, 8 parts of modified magnesium aluminum hydrotalcite, 3 parts of lubricant, 1 part of dispersant, 2 parts Antioxidant, 3 parts vinyl silane;

[0019] S2. Mix perchlorethylene resin, polystyrene, nano-zinc oxide, modified magnesium aluminum hydrotalcite, lubricant, dispersant, antioxidant, and vinyl silane, stir at 100r / min for 10min, and heat to 160°C. Continue to stir for 50min to obtain the mixture;

[0020] S3. Put the mixture into a mold with a preheating temperature of 200° C., and cool it to obtain a product;

[0021] Wherein, the raw material of described modified magnesium aluminum hydrotalcite comprises magnesium aluminum hydrotalcite, citrate, β-sodium taurine, titanate coupling agent, ethanol solution, distilled water;

[0...

Embodiment 2

[0025] A method for preparing a heat-resistant plastic product, comprising the steps of:

[0026] S1. Weigh each raw material according to parts by weight: 50 parts of perchlorethylene resin, 50 parts of polystyrene, 2 parts of nano zinc oxide, 15 parts of modified magnesium aluminum hydrotalcite, 1 part of lubricant, 3 parts of dispersant, 1 part of Antioxidant, 7 parts vinyl silane;

[0027] S2. Mix perchlorethylene resin, polystyrene, nano-zinc oxide, modified magnesium aluminum hydrotalcite, lubricant, dispersant, antioxidant, and vinyl silane, stir at 50r / min for 30min, and heat to 140°C. Continue to stir for 70min to obtain the mixture;

[0028] S3. Put the mixture into a mold with a preheating temperature of 180° C., and cool it to obtain a product;

[0029] Wherein, the raw material of described modified magnesium aluminum hydrotalcite comprises magnesium aluminum hydrotalcite, citrate, β-sodium taurine, titanate coupling agent, ethanol solution, distilled water;

...

Embodiment 3

[0033] A method for preparing a heat-resistant plastic product, comprising the steps of:

[0034] S1. Weigh each raw material according to parts by weight: 60 parts of perchlorethylene resin, 45 parts of polystyrene, 4 parts of nano-zinc oxide, 12 parts of modified magnesium aluminum hydrotalcite, 2 parts of lubricant, 2 parts of dispersant, 1.5 parts Antioxidant, 5 parts vinyl silane;

[0035] S2. Mix perchlorethylene resin, polystyrene, nano-zinc oxide, modified magnesium aluminum hydrotalcite, lubricant, dispersant, antioxidant, and vinyl silane, stir at 80r / min for 20min, and heat to 150°C. Continue to stir for 60min to obtain the mixture;

[0036] S3. Put the mixture into a mold with a preheating temperature of 190° C., and cool it to obtain a product;

[0037] Wherein, the raw material of described modified magnesium aluminum hydrotalcite comprises magnesium aluminum hydrotalcite, citrate, β-sodium taurine, titanate coupling agent, ethanol solution, distilled water;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a heat-resistant plastic product. The preparation method of the heat-resistant plastic product comprises the following steps: S1, weighing the followingraw materials in parts by weight: perchloroethylene resin, polystyrene, nano zinc oxide, modified magnalium hydrotalcite, a lubricant, a dispersing agent, an antioxidant and vinyl silanes; S2, mixingthe perchloroethylene resin, the polystyrene, the nano zinc oxide, the modified magnalium hydrotalcite, the lubricant, the dispersing agent, the antioxidant and the vinyl silanes, stirring, heating,and keeping stirring to obtain a mixture; and S3, placing the mixture in a preheated mold, and cooling to obtain the product. The modified magnalium hydrotalcite comprises the following raw materials:magnalium hydrotalcite, citric acid, beta-tarine sodium, a titanate coupling agent, an ethanol solution and distilled water. The prepared plastic product is excellent in mechanical property and heatresistance, the stretching, bending and impact strength and the thermal stability are remarkably improved, and the service life is prolonged effectively.

Description

technical field [0001] The invention relates to the technical field of plastics, in particular to a method for preparing heat-resistant plastic products. Background technique [0002] Plastic products are a general term for daily necessities and industrial products processed with plastic as the main raw material, including products of all processes such as injection molding and blistering with plastic as raw material. Plastic is a kind of synthetic polymer material with plasticity. It, synthetic rubber and synthetic fiber form the three major synthetic materials that are indispensable in today's daily life. Compared with metal, stone, and wood, plastic products have the advantages of low cost and strong plasticity, and are widely used in the national economy. The plastics industry occupies an extremely important position in the world today. Over the years, the production of plastic products has developed at a high speed all over the world. . However, the current plastic ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/24C08L25/06C08K13/06C08K9/04C08K3/26C08K3/22C08K5/5425
CPCC08K2003/2296C08K2201/011C08L27/24C08L2201/08C08L25/06C08K13/06C08K9/04C08K3/26C08K3/22C08K5/5425
Inventor 汪余海
Owner 安庆市航海印务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com