A kind of integral type diesel vehicle exhaust gas oxidation catalyst and preparation method thereof

An oxidation catalyst, diesel vehicle technology, applied in the direction of physical/chemical process catalysts, molecular sieve catalysts, chemical instruments and methods, etc., can solve the problems of pore structure collapse, active site reduction, catalytic activity reduction, etc., to achieve good catalytic oxidation activity and thermal stability effects

Active Publication Date: 2020-03-17
SICHUAN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the DPF fuel injection regeneration process, the exhaust gas temperature will rise sharply, the DOC outlet temperature will be as high as 650 ° C, and the Pt catalytic active component or carrier will be sintered, which will lead to a decrease in catalyst activity.
Pt particles with good initial dispersion, aggregate or grain growth at high temperature, resulting in reduced surface active sites and reduced catalytic activity
At the same time, the sintering of the carrier will cause the collapse of the pore structure and the reduction of active sites, and the existing DOC catalysts cannot meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of integral type diesel vehicle exhaust gas oxidation catalyst and preparation method thereof
  • A kind of integral type diesel vehicle exhaust gas oxidation catalyst and preparation method thereof
  • A kind of integral type diesel vehicle exhaust gas oxidation catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment provides Pt / Y 2 o 3 / SiO 2 -Al 2 o 3 The preparation method of catalyst comprises the following steps:

[0023] (1) the calculated amount of yttrium nitrate (15wt% Y 2 o 3 ) was dissolved in deionized water and impregnated in SiO by the isoporous volume impregnation method 2 -Al 2 o 3 On the carrier, let stand for 2h;

[0024] (2) Place the sample obtained in (1) in a drying oven to dry at 60°C for 12 hours, and then bake it in a roasting furnace at 550°C for 3 hours to obtain Y 2 o 3 / SiO 2 -Al 2 o 3 Modified carrier powder;

[0025] (3) Appropriately dilute the platinum nitrate solution (1wt% Pt), and impregnate the Y obtained in (2) by the isoporous volume impregnation method 2 o 3 / SiO 2 -Al 2 o 3 Powder, dry, roast the same as (2) to get Pt / Y 2 o 3 / SiO 2 -Al 2 o 3 Catalyst powder materials;

[0026] (4) Grinding the catalyst powder material obtained in (3) with 2-5wt% aluminum sol and 2-5wt% acetic acid to make a catalyst s...

Embodiment 2

[0030] (1) The calculated amount of Ca(NO 3 ) 2 (10wt% CaO) was dissolved in deionized water and impregnated in SiO 2 -Al 2 o 3 On the support, drying, roasting (same as the step (2) of embodiment 1), make CaO / SiO 2 -Al 2 o 3 carrier material;

[0031] (2) According to the same method of embodiment 1 step (3), impregnate the platinum nitrate solution in the CaO / SiO prepared by (1) 2 -Al 2 o 3 On the carrier material, dry and calcined to obtain Pt / CaO / SiO 2 -Al 2 o 3 catalyst powder;

[0032] (3) According to the same method of steps (4) in Example 1, (5) and (6), the monolithic Pt / CaO / SiO is prepared 2 -Al 2 o 3 catalyst.

Embodiment 3

[0034] (1) Mn(NO 3 ) 2 Solution (15wt%MnO 2 ) isoporous volume method impregnated in SiO 2 -Al 2 o 3 On the carrier, drying, roasting and (the same method as step (2) of Example 1), obtain MnO x / SiO 2 -Al 2 o 3 carrier material;

[0035] (2) According to the same method of embodiment 1 step (3), impregnate the platinum nitrate solution in the CaO / SiO prepared by (1) 2 -Al 2 o 3 On the carrier material, dry and calcined to obtain Pt / MnO x / SiO 2 -Al 2 o 3 catalyst powder;

[0036] (3) According to the same method of steps (4) in Example 1, (5) and (6), the monolithic Pt / MnO is prepared x / SiO 2 -Al 2 o 3 catalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses an integral diesel vehicle tail gas oxidation catalyst and a preparation method thereof. Including: loading precious metals on additive-modified SiO 2 ‑Al 2 o 3 The catalyst powder material is obtained on the carrier, and then the catalyst powder material is coated on the cordierite substrate; wherein SiO 2 The mass percent content in the carrier is 10-30wt%; the noble metal is Pt or / and Pd, and the total load is 1-3wt%. The present invention prepares SiO by modifying additives such as rare earth metals and alkaline earth metals 2 ‑Al 2 o 3 The carrier, the DOC catalyst prepared by the carrier can improve the activity of CO, HC, SOF and NO and the anti-aging performance at high temperature, especially the oxidation activity of NO.

Description

technical field [0001] The invention belongs to the technical field of catalyst research and preparation. In particular, it belongs to the technical field of research and preparation of motor vehicle tail gas treatment catalysts, and in particular relates to an integral diesel vehicle tail gas oxidation catalyst and a preparation method thereof. Background technique [0002] Motor vehicle exhaust is one of the main sources of air pollutants, the main pollutants include: carbon monoxide (CO), hydrocarbons (HC), nitrogen oxides (NO x ) and particulate matter (PM). It not only causes serious environmental pollution, but also seriously endangers human health. Diesel vehicles have been widely used because of their fuel economy and high thermal efficiency. Diesel vehicle oxidation catalyst (DOC) mainly purifies carbon monoxide (CO), hydrocarbons (HC), nitrogen oxides (NOx) and soluble organic components (SOF) on the surface of particulate matter (PM) in the exhaust gas of diese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/076B01D53/94B01D53/72B01D53/62B01D53/56
CPCB01D53/944B01D2257/502B01J29/076Y02A50/20
Inventor 王健礼梁艳丽陈耀强赵明
Owner SICHUAN UNIV