Method for preparing monolithic catalyst using waste-based material

An integrated catalyst and base material technology, applied in physical/chemical process catalysts, chemical instruments and methods, catalyst activation/preparation, etc., can solve problems such as poor economy, secondary pollution of catalysts, industrial needs, etc., and increase service life. , good catalytic activity, good mechanical strength effect

Active Publication Date: 2019-04-16
SHANGHAI UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 3. The amplification effect is not obvious;
[0009] 1. When the impregnation method is used to prepare monolithic catalysts, the active components are easy to fall off and the loading rate is not high;
[0010] 2. When using the blending extrusion molding method to prepare monolithic catalysts, the consumption of catalyst core components is large and the economy is poor;
[0011] 3. In the catalyst molding process, it is necessary to calcine at a high temperature above 1100°C to improve the mechanical properties of the catalyst, which will lead to the deactivation of the active components in the catalyst and reduce the performance of the catalyst
[0012] Therefore, there is an urgent need to find a new technology to solve many problems in the production and use of transition metal catalysts, including the high cost of catalyst production and use, the secondary pollution of waste-based catalysts, and various aspects of catalyst molding. Whether the indicators can meet the needs of industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing monolithic catalyst using waste-based material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In this example, see figure 1 , a method for preparing monolithic catalysts using waste-based materials, using manganese slag, fly ash and plasma glass slag as raw materials for preparing monolithic catalysts, the steps are as follows:

[0040] Step 1: Activate the waste-based material, the specific activation method steps are as follows:

[0041] a. Prepare HNO with a concentration of 1mol / L 3 solution and a NaOH solution with a concentration of 1mol / L, for subsequent use; and take manganese slag, and pass through a 50-mesh sieve through crushing to obtain manganese slag waste-based powder, for subsequent use;

[0042] b. Get 3g of the manganese slag waste base powder prepared in the step a, add 25ml of HNO prepared in the step a 3 The solutions were mixed, and after stirring for 30 minutes, a certain amount of NaOH solution prepared in the step a was added, so that the pH of the solution was controlled at 8 to 8.5, and after stirring for 30 minutes, the solid was ce...

Embodiment 2

[0053] This embodiment is basically the same as Embodiment 1, especially in that:

[0054] In this embodiment, a method for preparing monolithic catalysts using waste-based materials, using manganese slag, fly ash and plasma glass slag as raw materials for preparing monolithic catalysts, the steps are as follows:

[0055] Step 1: Activate the waste-based material, the specific activation method steps are as follows:

[0056] a. This step is the same as in Embodiment 1;

[0057] b. Get 1g of the manganese slag waste base powder prepared in the step a, add 25ml of HNO prepared in the step a 3 The solutions were mixed, and after stirring for 30 minutes, a certain amount of NaOH solution prepared in the step a was added, so that the pH of the solution was controlled at 8.5 to 9, and after stirring for 30 minutes, the solid was collected by centrifugation and set aside;

[0058] c. Put the solid obtained in the step b into an oven at 100°C for 5 hours of drying treatment. After t...

Embodiment 3

[0068] This embodiment is basically the same as the previous embodiment, and the special features are:

[0069] In this embodiment, a method for preparing monolithic catalysts using waste-based materials, using waste-based materials as raw materials for preparing monolithic catalysts, the steps are as follows:

[0070] Step 1: Activate the waste-based material, the specific activation method steps are as follows:

[0071] a. This step is the same as in Embodiment 1;

[0072] b. get 3g of the blast furnace slag waste base powder prepared in said step a, the mass content of the blast furnace slag waste base material components used in the activation process is: the content of transition metal is 10%, SiO 2 35%, Al 2 o 3 12%, K 2 O is 0.8%, MgO is 0.5%; add 25ml of HNO prepared in step a 3 The solutions were mixed, and after stirring for 30 minutes, a certain amount of NaOH solution prepared in the step a was added, so that the pH of the solution was controlled at 8 to 8.5, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing a monolithic catalyst by using a waste-based material. According to the method, a waste-based material is used as a raw material for preparing the monolithic catalyst, the preparation process mainly comprises an excitation part and a forming part, the forming of the catalyst can be finished within 200 DEG C, the connection between the substances in theformed catalyst mainly includes ionic bonds and covalent bonds, and hydrogen bonds and Van der Waals force are auxiliary, the catalyst has good mechanical strength. The catalyst not only has good catalytic effect on the surface, but also has good catalytic activity after the active components on the surface fall off and the internal components are exposed, thereby not only is the service life ofthe catalyst prolonged, but also, compared with a prior catalyst, the use of the catalyst reduces the cost of catalyst replacement. The preparation method of the catalyst is novel, simple, efficient,low in cost, long in service life, high in strength, good in activity and high in quality, can achieve recycling of wastes, is environment-friendly, and has obvious popularization value.

Description

technical field [0001] The invention relates to a method for preparing an integral catalyst, and also relates to a method for recycling waste, which is applied in the technical field of catalyst preparation and application. Background technique [0002] A catalyst is a chemical reaction that can change the chemical reaction rate of the reactants without changing the chemical balance. The catalyst can both increase or decrease the chemical reaction rate of the reactants, and its quality and chemical properties have not changed before and after the chemical reaction. substance. According to statistics, more than 90% of industrial processes use catalysts, such as chemical, petrochemical, biochemical, and environmental protection. Catalysts play an extremely important role in the modern chemical industry. The activity, selectivity and stability of catalysts are important indicators to measure the performance of catalysts. Noble metal catalysts and transition metal catalysts are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/34B01J27/185B01J27/187B01J37/08
CPCB01J23/34B01J27/1853B01J27/187B01J37/08
Inventor 张佳王晶晶殷瑞夏青玲崔耀文周吉峙钱光人
Owner SHANGHAI UNIV