Chitin polyester fiber

A polyester fiber and chitin technology, applied in the fiber field, can solve the problems of many rabbits, affecting the unwinding performance of the winding drum, and the loss of chitin on the fiber surface, achieving long-lasting antibacterial and bacteriostatic properties, preventing broken heads and wool, the effect of improving the winding performance

Pending Publication Date: 2019-05-10
ZHONGKE TEXTILE RES INST QINGDAO CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] From the current existing technology, most chitin polyester fibers are attached to textile fibers through post-treatment, but with daily use, washing, etc., the chitin on the fiber surface will gradually lose
At the same time, when chitin is added to polyester melt chips for spinning, due to the change of polyester fiber process and shape, the phenomenon of tripping is serious in the process of preparing polyester fibers, and there are many cases of rabbit heads, which are serious. It affects the unwinding performance of the winding drum, resulting in broken ends and hairs in the subsequent processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chitin polyester fiber
  • Chitin polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 A kind of chitin polyester fiber, its raw material comprises polyester chip, chitosan, modifier, regulator; The mass ratio of described polyester chip, chitosan, modifier, regulator is 75 :3:5.5:1.5;

[0035] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said chitosan: deacetylation degree ≥ 95%, moisture content ≤ 80.5%, viscosity ≤ 50mpa.s;

[0036] Described modifying agent is made up of triethyl citrate, talcum powder, potassium methyl silicate, guar gum; Preferably, in described modifying agent, triethyl citrate, talcum powder, methyl silicate The preferred ratio of potassium to guar gum is 17:1:4:2.

[0037] Described conditioning agent is made up of sodium acetate, sodium alginate, isopropanol;

[0038] The preferred mass ratio of sodium acetate, sodium a...

Embodiment 2

[0049] Embodiment 2 A kind of chitin polyester fiber, its raw material comprises polyester chip, chitosan, modifier, regulator; The mass ratio of described polyester chip, chitosan, modifier, regulator is 75 :3:5.5:1.5;

[0050] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said chitosan: deacetylation degree ≥ 95%, moisture content ≤ 80.5%, viscosity ≤ 50mpa.s;

[0051] Described modifying agent is made up of triethyl citrate, talcum powder, potassium methyl silicate, guar gum; In described modifying agent, triethyl citrate, talcum powder, potassium methyl silicate, guar gum The preferred ratio of Er gum is 18:2:3:3.

[0052] Described conditioning agent is made up of sodium acetate, sodium alginate, isopropanol;

[0053] The preferred mass ratio of sodium acetate, sodium alginate...

Embodiment 3

[0064] Embodiment 3 A kind of chitin polyester fiber, its raw material comprises polyester chip, chitosan, modifier, regulator; The mass ratio of described polyester chip, chitosan, modifier, regulator is 85 :5:4:2.3;

[0065] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said chitosan: deacetylation degree ≥ 95%, moisture content ≤ 80.5%, viscosity ≤ 50mpa.s;

[0066] Described modifying agent is made up of triethyl citrate, talcum powder, potassium methyl silicate, guar gum; In described modifying agent, triethyl citrate, talcum powder, potassium methyl silicate, guar gum The preferred ratio of Er gum is 20:1:4:3.

[0067] Described conditioning agent is made up of sodium acetate, sodium alginate, isopropanol;

[0068] The preferred mass ratio of sodium acetate, sodium alginate a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
antibacterial rateaaaaaaaaaa
water contentaaaaaaaaaa
Login to view more

Abstract

The invention provides a chitin polyester fiber. Raw materials for preparing the fiber include polyester chips, chitosan, a modifier and a regulator; and the mass ratio of the polyester chips to chitosan to the modifier to the regulator is (75-85):(3-5):(4-5.5):(1.5-2.3). The polyester chips has the water content of less than or equal to 0.2%, the acetaldehyde content of less than or equal to 1%,the acid value of max.35 Meq/kg and the inherent viscosity of 0.865+/-0.015 dl/g; the chitin polyester fiber provided by the invention has the water retention rate of 18-20% and the dyeing degree of 92-95%; and the chitin polyester fiber has functions of permanent skin affinity, antibacterial property and mildew prevention. No spinder webs are generated in a process of preparing the chitin polyester fiber, so that the winding performance of a bobbin is improved, the web breaking and filament breaking caused in subsequent processing due to the addition of chitin fiber are avoided, and the quality of the fiber is improved.

Description

technical field [0001] The invention relates to a chitin polyester fiber and belongs to the field of fiber technology. Background technique [0002] As one of the three main fibers in synthetic fibers, polyester is widely used in clothing fabrics and other non-clothing fields because of its excellent physical and chemical properties. Since its inception, polyester products have also been used by downstream users as the main textile raw material for weaving various textiles due to their good drapability, high strength and crispness. With the globalization of the economy and the internationalization of the market, people's requirements for clothing are getting higher and higher. Not only must they be comfortable, but they must also be functional. It is necessary to continuously improve performance to meet weaving requirements. The polyester industry in my country has developed rapidly. The output of polyester fiber has grown from 5.165 million tons in early 2000 to 27 million ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01F8/18D01F1/10
Inventor 黄效华甄丽刘洁
Owner ZHONGKE TEXTILE RES INST QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap