A kind of heat-resistant steel for key hot-end parts of ultra-high parameter steam turbine

A hot-end component and heat-resistant steel technology, which is applied in the field of heat-resistant steel, can solve the problems of limited improvement of high-temperature durability and oxidation resistance of heat-resistant steel, so as to improve high-temperature performance and oxidation resistance, prevent powder agglomeration, The effect of increasing the temperature parameter

Active Publication Date: 2020-08-04
DONGFANG TURBINE CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, adjusting W, Co, B, Nb, N and other elements is also limited to improve the high-temperature durability and oxidation resistance of heat-resistant steel. Oxidation properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of heat-resistant steel for key hot-end parts of ultra-high parameter steam turbine
  • A kind of heat-resistant steel for key hot-end parts of ultra-high parameter steam turbine
  • A kind of heat-resistant steel for key hot-end parts of ultra-high parameter steam turbine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] According to the required chemical elements, weigh each component to obtain raw materials, put the raw materials in a vacuum smelting furnace for smelting, add block additives during the vacuum smelting process, and then carry out electroslag remelting smelting to ensure uniform melting, then casting Form a steel ingot, the size of the steel ingot is ψ50, forge the steel ingot, the forging temperature range is 1100-1200°C; then carry out the following treatment on the steel ingot: quenching treatment temperature is 1050°C, holding time 1h, oil cooling or air cooling to room temperature, Then perform a tempering treatment, the tempering temperature is 700°C, the holding time is 4h, air-cooled or air-cooled to room temperature, and then a second tempering treatment is performed, the tempering temperature is 680°C, the holding time is 4h, air-cooled or air-cooled to room temperature room temperature. The weight percentage (%) of each component of the heat-resistant steel: ...

Embodiment 2

[0058] According to the required chemical elements, weigh each component to obtain raw materials, put the raw materials in a vacuum smelting furnace for smelting, add block additives during the vacuum smelting process, and then carry out electroslag remelting smelting to ensure uniform melting, then casting Form a steel ingot, the size of the steel ingot is ψ50, the forging temperature range is 1100-1200°C; then the steel ingot is treated as follows: the quenching temperature is 1050°C, the holding time is 1h, oil cooling or air cooling to room temperature, and then a tempering For processing, the tempering temperature is 680°C, the holding time is 6h, and air-cooled or air-cooled to room temperature. The weight percentage (%) of each component of the heat-resistant steel: C: 0.05, Cr: 9.25, Co: 2.92, W: 2.96, Mo: 0.38, V: 0.15, Ni: 0.43, Nb: 0.08, N: 0.034, B: 0.023, Si: 0.0013, Mn: 0.21, S: 0.0018, P: 0.0010, Y: 0.60.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a heat-resistant steel for the key hot end parts of an ultra-high parameter steam turbine, which contains: C: 0.02-0.08, Cr: 8.00-10.00, Co: 2.0-4.0, W: 2.0 in weight percentage ~4.0, Mo: 0.10~0.80, V: 0.10~0.30, Ni: 0.30~0.70, Nb: 0.05~0.15, N: 0.010~0.050, B: 0.010~0.030, rare earth elements: 0.1~1.0, Si: ≤0.10 , Mn: 0.10 ~ 1.00, the balance consists of Fe and unavoidable impurities. The heat-resistant steel belongs to martensitic heat-resistant steel and has good high-temperature performance and oxidation resistance, thereby improving the temperature parameter of the steam turbine and helping to improve the power generation efficiency of the steam turbine.

Description

technical field [0001] The heat-resistant steel for key hot-end parts of ultra-high parameter steam turbines involved in the present invention is mainly used in the field of steam turbines, especially the key hot-end parts of steam turbines that have special requirements for creep strength and high-temperature oxidation resistance, such as high-temperature turbine blades, Heat-resistant steel for small and medium forgings such as spool parts. Background technique [0002] The current global energy revolution and transformation has put forward new requirements for power generation equipment, and the development of power generation equipment is facing new tasks of promoting green and low-carbon development and upgrading of energy structure. my country's energy structure is "more coal, less oil, and less gas". Coal will exist as the main energy source for a long time. Efficient and clean use of coal is the most effective means to reduce air pollution and carbon dioxide emission...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/46C22C38/48C22C38/52C22C38/54C21D8/00C22C33/04
Inventor 裴玉冰王天剑巩秀芳江雷郭汉杰郭靖杨文晟张邦强王芬玲王海洋
Owner DONGFANG TURBINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap