Environment-friendly sand-p0lastic composite material and preparation method thereof
A composite material and sand plastic technology, applied in the field of composite materials, can solve the problem of less research on purifying gas, and achieve the effects of improving smoothness, reducing static electricity, and expanding the scope of use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] This embodiment provides a method for preparing an environmentally friendly sand-plastic composite material, including:
[0038] (1) Weigh 25Kg of quartz sand, 3Kg of anion powder, 15Kg of polypropylene resin, 25Kg of polyethylene resin and 5Kg of silane coupling agent KH550;
[0039] (2) Mix quartz sand, polypropylene resin, polyethylene resin and silane coupling agent KH550, and heat to 270°C under the protection of nitrogen to obtain the first slurry;
[0040] (3) Mix water and negative ion powder at a mass ratio of 10:1, and ultrasonicate the water bath for 20 minutes at a temperature of 40°C to obtain a negative ion excitation material slurry;
[0041] Under stirring, adding the negative ion excitation material slurry to the first slurry to obtain the second slurry;
[0042] (4) Put the second slurry in a mold, cool to room temperature (25° C.), demold, and obtain a sand-plastic composite material A.
Example Embodiment
[0043] Example 2
[0044] This embodiment provides a method for preparing an environmentally friendly sand-plastic composite material, including:
[0045] (1) Weigh 35Kg of quartz sand, 1Kg of anion powder, 20Kg of polypropylene resin, 17Kg of polyethylene resin, 2Kg of silane coupling agent KH550 and 0.5Kg of pore former;
[0046] Wherein, the pore former is a mixture of absolute ethanol and ethylene glycol, and the mass ratio of absolute ethanol to ethylene glycol is 5:1;
[0047] (2) Mix quartz sand, polypropylene resin, polyethylene resin and silane coupling agent KH550, and heat to 350°C under the protection of nitrogen to obtain the first slurry;
[0048] (3) Mix anhydrous ethanol, ethylene glycol, anion powder and water, and ultrasonicate the water bath for 20 minutes at a water bath temperature of 50°C to obtain anion excitation material slurry; the amount of water added is 1 time the mass of the anion powder;
[0049] Under stirring, adding the negative ion excitation material s...
Example Embodiment
[0051] Example 3
[0052] This embodiment provides a method for preparing an environmentally friendly sand-plastic composite material, including:
[0053] (1) Weigh 30Kg of quartz sand, 2Kg of nano tourmaline, 19Kg of polypropylene resin, 20Kg of polyethylene resin, 3Kg of silane coupling agent KH550, 2Kg of pore former and 3Kg of antifouling agent;
[0054] Wherein, the pore former is a mixture of absolute ethanol and ethylene glycol, and the mass ratio of absolute ethanol to ethylene glycol is 7:3;
[0055] The antifouling agent is a mixture of acetic acid and an antifouling adjuvant, the antifouling adjuvant is molybdenum disulfide and sorbitan fatty acid ester; the mass ratio of acetic acid to the antifouling adjuvant is 7:1; molybdenum disulfide The mass ratio to sorbitan fatty acid ester is 2:9;
[0056] (2) Mix quartz sand, polypropylene resin, polyethylene resin and silane coupling agent KH550, and heat to 300°C under the protection of nitrogen to obtain the first slurry;
[005...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap